Evaluation of the Interfacial Adhesion between Brittle Coating and Ductile Substrate by Cross-Secitional Indention
查看参考文献6篇
文摘
|
The cross-sectional indentation method is extended to evaluate the interfacial adhesion between brittle coating and ductile substrate. The experimental results on electroplated chromium coating/steel substrate show that the interfacial separation occurs due to the edge chipping of brittle coating. The corresponding models are established to elucidate interfacial separation processes. This work further highlights the advantages and potential of this novel indentation method. |
来源
|
材料热处理学报
,2004,25(5II):1187-1190 【核心库】
|
关键词
|
coating
;
interface adhesion
;
indentation
|
地址
|
Institute of Mechanics, Chinese Academy of Sciences, 北京
|
语种
|
英文 |
文献类型
|
研究性论文 |
ISSN
|
1009-6264 |
学科
|
金属学与金属工艺 |
文献收藏号
|
CSCD:1847759
|
参考文献 共
6
共1页
|
1.
HUANG Li-ye. Nano-scratch Behaviors of Diamond Like Carbon Films during LoadingUnloading Processes.
Acta Metallurgical Sinica (in Chinese),2001,37(12):1247-1250
|
被引
1
次
|
|
|
|
2.
A A Volinsky. Interfacial Toughness Measurements for Thin Films on Substrates.
Acta Mater,2002,50(3):441-466
|
被引
26
次
|
|
|
|
3.
Sanchez J M. A New Technique for Thin Film Interfacial Adhesion Characterization.
Acta Mater,1999,47(17):4405-4413
|
被引
7
次
|
|
|
|
4.
M R Elizalde. Interfacial Fracture Induced by Cross-Sectional Nanoindentation in MetalCeramic Thin Film Structures.
Acta Mater,2003,51(14):4295-4305
|
被引
12
次
|
|
|
|
5.
N J McCormick. Edge Flaking of Brittle Materials.
J. Hard Mater,1990,1(1):25-51
|
被引
2
次
|
|
|
|
6.
R Morrel. Edge Chipping of Hard Materials.
Int. J. Refract. Met. Hard Mater,2001,19(4/6):293-301
|
被引
1
次
|
|
|
|
|
|