Ti3Al基合金在700～850℃空气中的循环氧化行为
Cyclic oxidation behaviors of Ti3Al-based alloys at 700 -850 ℃ in air
查看参考文献17篇
|
文摘
|
研究了2种成分相近的Ti3Al基合金(Ti-24Al-14Nb-3V-0.5Mo-0.3Si(摩尔分数)及Ti-24Al-14Nb-3V-0.5Mo-0.6Si在700～850℃空气中的循环氧化行为;重点考察了合金的循环氧化动力学行为;结合SEM/EDX及EPMA分析了循环氧化后样品的表面、断面微观形貌及断面成膜元素面分布.结果表明:2种合金在各氧化温度下表面生成了Al2O3和TiO2混合氧化物,Al2O3主要分布在最外层;在700℃下2种合金具有较好的抗循环氧化性能,而在800℃及以上的温度条件下,表面氧化膜易于开裂和剥落;合金在较高温度下表面氧化膜失效方式为膜层中微裂纹的复合及由于这一过程的反复进行而导致的氧化膜间物理分层开裂. |
|
其他语种文摘
|
The cyclic oxidation behaviors of two Ti_3Al-based alloys with similar content of Ti-24Al-14Nb-3V-0. 5Mo-0. 3Si(molar fraction, %)and Ti-24Al-14Nb-3V-0. 5Mo-0. 6Si at 700 - 850 ℃ in air were investigated. The emphasis was placed on the characteristics of cyclic oxidation kinetics, the microstructure of surface and cross-section of oxide scales and the depth profiles of alloying elements by means of XRD/EDX and EPMA. The results show that during the oxidation process, the mixture of Al_2O_3 and TiQ; is formed and the outside layer is enriched with Al. Cyclic oxidation resistance of these two Ti_3 Al-based alloys is good at 700 ℃. But at 800 ℃ or above that, the surface oxide is prone to cracking and spallatioa The failure mode of the oxide scale at higher temperatures is contributed to the physical delamination in the scales due to the initiation and propagation of micro-cracks and during the cyclic oxidation process. |
|
来源
|
中国有色金属学报
,2004,14(9):1609-1614 【核心库】
|
|
关键词
|
Ti3Al基合金
;
循环氧化
;
氧化动力学
|
|
地址
|
1.
宝山钢铁股份有限公司技术中心, 上海, 201900
2.
中国科学院金属研究所, 沈阳材料科学国家联合实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1004-0609 |
|
学科
|
金属学与金属工艺;化学工业 |
|
基金
|
国家自然科学基金资助项目
;
辽宁省沈阳市科技项目
|
|
文献收藏号
|
CSCD:1698453
|
参考文献 共
17
共1页
|
|
1.
仲增墉. 金属间化合物高温结构材料[J].
材料科学进展,1990,4(2):132-142
|
被引
10
次
|
|
|
|
|
2.
Subrahmanyam J. Cyclic oxidation aluminized [J].
Journal of Material Science,1988,23:1906-1910
|
被引
3
次
|
|
|
|
|
3.
Holwach J. Ti/Al design/cost trade-off analysis [R].
Ti/Al design/cost trade-off analysis. AFAPL-TR-78-74,1978
|
被引
1
次
|
|
|
|
|
4.
唐兆麟. 高温钛合金及钛铝金属间化合物的腐蚀与防护[J].
稀有金属,1996,20(4):291-296
|
被引
6
次
|
|
|
|
|
5.
Lipsitt H A. Titanium aluminides-an overview[A].
High Temperature Ordered Intermetallic Alloys,1985:351-364
|
被引
2
次
|
|
|
|
|
6.
Perkins R A. Formation of alumina on Ti-Al alloys[J].
Scripta Metall,1987,21:1505-1510
|
被引
8
次
|
|
|
|
|
7.
Sankaran S N. Oxidation characteristics of Ti-14Al-21Nb (%) ingot alloy[R].
Oxidation characteristics of Ti-14Al-21Nb (%) ingot alloy.NASA-TP-3012,,1990
|
被引
1
次
|
|
|
|
|
8.
Meier G H. Oxidation of titanium-base alloys [A].
Oxidation of High Temperature Intermetallics,1989:185-193
|
被引
2
次
|
|
|
|
|
9.
Welsch G. Oxidation behavior of titanium aluminide alloys [A].
Oxidation of High Temperature Intermetallics,1989:207-218
|
被引
2
次
|
|
|
|
|
10.
Perkins R A. Formation of alumina on niobium and titanium alloys [A].
Oxidation of High Temperature Intermetallics,1989:157-169
|
被引
2
次
|
|
|
|
|
11.
Khobaib M. High temperature oxidation behavior of Ti3 Al alloys[A].
Space Age Metals Technology,1988:262-270
|
被引
2
次
|
|
|
|
|
12.
Choudhury N S. Oxidation behavior of titanium aluminides [A].
Properties of High Temperature Alloys with Emphasis on Environmental Effects,1976:668-680
|
被引
1
次
|
|
|
|
|
13.
Mendiratta M G. Properties and microstructure of high temperature materials [R].
Properties and microstructure of high temperature materials.AFML-TR-78-112,1978
|
被引
1
次
|
|
|
|
|
14.
Tien J K. Oxide spallation mechanisms[A].
Stress Effects and the Oxidation of Metals,1975:200-219
|
被引
1
次
|
|
|
|
|
15.
Evans H E. Stress effects in high temperature oxidation of metals [J].
International Materials Review,1995,40(1):1-40
|
被引
24
次
|
|
|
|
|
16.
Evans H E. Conditions for the initiation of oxide scale cracking and spallation[J].
Corrosion Science,1984,24:209-222
|
被引
30
次
|
|
|
|
|
17.
Bertrand G. Morphology of oxide scales formed on titanium[J].
Oxid Met,1983,21:1-19
|
被引
2
次
|
|
|
|
|
了解气象卫星更多信息，请访问