碳钢与低合金耐大气腐蚀规律研究
Study on atmospheric corrosion of low alloy steels

查看参考文献5篇

文摘 采用干湿复合循环实验、电化学交流阻抗和扫描电镜等方法研究了7种碳钢与低合金钢在试验环境中的腐蚀规律及腐蚀试验后带锈试样的电化学特征结果表明,7种材料的腐蚀失重率随时间均遵从负指数规律:Y=Y_o+Ae~(t/B)、电化学测试结果表明带锈试样进一步腐蚀的速度受阴极扩散过程所控制;7种材料带锈试样的阻抗值与材料的年腐蚀速率呈线性关系
其他语种文摘 The corrosion of 7 kinds of mild steel and low alloy steel in immersion— wet- dry cycle test environ ment and the electrochemical feature of rusted metals after test were studied by using EIS and SEM et al. The solution containing HSO_3~- and C~-l , was used for wetting and immersion specimens at circumstance temperature 40℃ for 4 min respectively.The drying cycle was maintained for 12 min at temperature 12℃ .The results indi cated that, the weight loss all followed exponential decay function: Y= Y_O + A_e ~(t/B). The corrosion rate of mild steel was 2.49 times than that of the most corrosion resistant low alloy after 120 h test. The results of electro chemical measurement showed that, the further corrosion rate would be controlled by cathodic diffusion process. The impedance of 7 kinds of steels after corrosion test was linear with the annual corrosion rate.
来源 中国腐蚀与防护学报 ,2004,24(3):147-150,154 【核心库】
关键词
地址

中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016

语种 中文
文献类型 研究性论文
ISSN 1005-4537
学科 金属学与金属工艺
基金 国家自然科学基金资助项目 ;  国家自然科学基金资助项目
文献收藏号 CSCD:1645126

参考文献 共 5 共1页

1.  Townsend H E. Corrosion,,2001,57(6):497-501 被引 49    
2.  Asami K. J the Japan Institute of Metals,,2002,66(6):649-656 被引 4    
3.  Ishikawa T. corrosion,,2001,57(4):346-352 被引 8    
4.  Kmaimura T. Mater Trans,,2002,43(4):694-703 被引 1    
5.  Yamamoto M. Testsuto Hagane,,2000,86:9 被引 1    
引证文献 10

1 张晓云 40CrNi2Si2MoVA钢的大气应力腐蚀行为 中国腐蚀与防护学报,2006,26(5):275-281
被引 1

2 汪兵 晶粒尺寸对普碳钢耐工业环境下大气腐蚀性能的影响 中国腐蚀与防护学报,2007,27(4):193-196
被引 13

显示所有10篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号