在多工位炉上CeO_2:Bi_12SiO_20单晶生长的研究(II)——空间生长实验部分
Growth of CeO_2:Bi_12SiO_20 Crystals in Multi-Position Furnace(II)-Space Growth Experiment
查看参考文献17篇
文摘
|
掺Ce:Bi_(12)SiO_(20)单晶在神舟3号(SZ-3)飞船上成功地进行了空间生长,得到晶体尺寸为φ10mmx40mm.将空间生长的晶体和地面生长晶体对比发现:空间生长晶体的外观同地面生长晶体有明显差异.分析测试空间和地面晶体的x射线摇摆曲线、吸收曲线和喇曼光谱,结果表明:空间生长掺Ce:BSO晶体的结构完整性优于地面生长的晶体,掺Ce对BSO晶体光学性能的影响空间制备晶体要大于地面制备的晶体 |
其他语种文摘
|
Ce-doped Bi_(12)Si0_(20) single crystal with size of φ10mm×40mm was successfully grown in space on board of the spacecraft Shenzhou No.3. The surface morphology of space-grown crystal is different from that of ground-grown crystal .The space- and ground-grown crystals were measured by X-ray rocking curves, absorption spectra and micro-Raman spectra. The results show that the quality of Ce-Hoped crystal grown in space is better than that of the ground-grown one. The effect of doping on optical properties of BSO grown in space is evident in comparison with the ground-grown crystal. |
来源
|
无机材料学报
,2004,19(2):283-288 【核心库】
|
关键词
|
掺铈硅酸铋(Ce:BSO)
|
地址
|
1.
中国科学院上海硅酸盐研究所, 上海, 200050
2.
中国科学院半导体研究所, 北京, 100083
3.
中国科学院物理研究所, 北京, 100080
|
语种
|
中文 |
文献类型
|
研究性论文 |
ISSN
|
1000-324X |
学科
|
一般工业技术 |
文献收藏号
|
CSCD:1636661
|
参考文献 共
17
共1页
|
1.
Peltier M.
J.Appl.Phys,1977,48:3683-3687
|
被引
3
次
|
|
|
|
2.
Horwitsz B A.
J.Opt.Engin,1978,17:353-359
|
被引
1
次
|
|
|
|
3.
Wooder M J.
Opt.Commun,1981,63:816-820
|
被引
1
次
|
|
|
|
4.
Foote P D.
Optics and Laser Technol,1986,18:39-43
|
被引
1
次
|
|
|
|
5.
Yeh P.
Appl.Optics,1988,27:2093-2098
|
被引
5
次
|
|
|
|
6.
Abrahams S C.
Chem.Phys,1979,71:788-793
|
被引
1
次
|
|
|
|
7.
Grabmaier B C.
Phys.Stat.Sol,1986,96(a):199-210
|
被引
1
次
|
|
|
|
8.
Xu Xuewu.
Cryst.Res.Technol,1994,29(2):207-213
|
被引
1
次
|
|
|
|
9.
Gospodiov M.
Cryst.Res.Technol,1994,29(5):603-611
|
被引
1
次
|
|
|
|
10.
Katsumata T.
Mater.Res.Bull,1995,30(1):19-26
|
被引
1
次
|
|
|
|
11.
Qiang Liangsheng.
压电与声光,1997,19(3):184-186
|
被引
1
次
|
|
|
|
12.
Mihailova B.
Soild State Commun,1997,102(6):441-444
|
被引
1
次
|
|
|
|
13.
Panda R N.
Mater.Chem.Phys,2002,78:313-317
|
被引
1
次
|
|
|
|
14.
Zhou Yanfei.
无机材料学报,2003,18(1):211-214
|
被引
2
次
|
|
|
|
15.
Zheng Yu.
11th Interational Symposium on Experimental Methods for Micorgravity Materials Research,1999
|
被引
1
次
|
|
|
|
16.
Baonas G A.
Sov.Phys.Solid State,1982,24:921-926
|
被引
1
次
|
|
|
|
17.
Kailinkin A N.
Inorg.Mater,1992,28:422-426
|
被引
1
次
|
|
|
|
|