文摘
|
对3种铜合金-镍复合材料进行了不同温度的退火处理,通过力学拉伸试验和电子探针(EPMA)观察与分析,研究了退火温度对3种复合材料的金相组织、元素扩散以及力学性能的影响.结果表明,经300℃以上温度退火处理后,3种复合材料的抗拉强度、屈服强度和硬度均随退火温度的升高而降低,而伸长率则随退火温度的升高而增大,铜合金与镍之间的Cu/Ni元素均发生了扩散,但主要是铜元素向镍层的扩散.合适的退火温度有利于提高复合材料的综合性能. |
|
其他语种文摘
|
Three kinds of copper alloys-nickel composites were annealed at different temperature. The effect of anneal-ing temperature on the microstructure and mechanical properties of the composites was studied by means of mechani-cal tensile test and EPMA. The result shows that the tensile strength(R_m, R_(p0.2)) and hardness(HV10)of the compos-ites decrease as annealing temperature increasing, the elongation(A)of them increases as annealing temperature in-creasing above 300 ℃ . The diffusion of Cu-Ni elements between copper alloys-nickel observed by EPMA is existent, and the main diffusion is Cu element to Ni layer. The overall properties can be improved by annealing under proper temperature. |
|
来源
|
金属热处理
,2004,29(4):17-20 【核心库】
|
|
关键词
|
退火
;
铜合金-镍复合材料
;
微观组织
;
力学性能
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0254-6051 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家科技部社会公益研究专项
|
|
文献收藏号
|
CSCD:1594441
|
了解气象卫星更多信息，请访问