两种盐沉积对LY12铝合金大气腐蚀行为的影响
Effect of deposition of ammonium chloride and ammonium sulfate on atmospheric corrosion of LY12 alloy
查看参考文献17篇
|
文摘
|
在温度为298 K,相对湿度为(85士5)%的条件下,对硫酸铵和氯化铵两种盐沉积后的LY12铝合金大气腐蚀行为进行了研究.腐蚀动力学曲线表明:沉积硫酸铵和氯化铵的LY12样品比空白样品的腐蚀更为严重,而且经氯化铵沉积的样品比经硫酸铵沉积的样品腐蚀严重得多.采用傅里叶变换红外光谱、扫描电镜以及光电子能谱等微观方法研究了不同腐蚀周期样品表面的结构和形貌,结果表明腐蚀主要沿着盐沉积的区域进行,随着时间的延长,腐蚀产物的生成减缓了LY12合金的腐蚀质量损失.对两种盐沉积条件下LY12合金的腐蚀机理进行了讨论. |
|
其他语种文摘
|
The atmospheric corrosion of LY12 alloy deposited with (NH_4)_2SO_4 and NH_4Cl particles was investiga-ted at 298 K with relative humidity of (85±5)%. The results show thatj the samples deposited with NH_4C1 parti-cles corrode more seriously than the samples with (NH_4)_2SO_4 particles. FTIR, SEM and XPS were utilized to study the development of corrosion process and characterization of corrosion products. The results also indicate that LY12 alloy contaminated by salts is corroded much faster than the clean samples, and corrosion of LY12 alloy initiates a-long the deposition area of (NH_4)_2SO_4 and NH_4C1 particles. A corrosion mechanism was proposed to explain the observation. |
|
来源
|
中国有色金属学报
,2004,14(7):1149-1155 【核心库】
|
|
关键词
|
LY12铝合金
;
盐沉积
;
大气腐蚀
|
|
地址
|
中国科学院,金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1004-0609 |
|
学科
|
冶金工业 |
|
基金
|
国家自然科学基金资助项目
|
|
文献收藏号
|
CSCD:1586870
|
参考文献 共
17
共1页
|
|
1.
王光雍. 自然环境的腐蚀与防护(大气?海水?土壤)[M].
自然环境的腐蚀与防护(大气·海水·土壤),1997:26-27
|
被引
1
次
|
|
|
|
|
2.
梁成浩. 金属腐蚀学导论[M].
金属腐蚀学导论,1998:132
|
被引
1
次
|
|
|
|
|
3.
Graedel T E. Corrosion mechanisms for aluminum exposed to the atmosphere[J].
Journal of the Electrochemical Society,1989,136(4):204-212
|
被引
40
次
|
|
|
|
|
4.
Vashi R T. Atmospheric corrosion study of baroda industrial area[J].
Bulletin of Electrochemical,1997,13:343-348
|
被引
1
次
|
|
|
|
|
5.
Elola A S. Evolution of the pitting of aluminum exposed to the atmosphere[J].
Corrosion,1992,48(10):854-863
|
被引
24
次
|
|
|
|
|
6.
Blucher Bengtsson D. The effect of CO2 on the NaCl-induced atmospheric corrosion of aluminum[J].
Journal of the Electrochemical Society,2001,148(4):B127-B131
|
被引
6
次
|
|
|
|
|
7.
万晔. 硫酸铵颗粒沉积作用下A3钢的大气腐蚀行为.
物理化学学报,2002,18(2):156-159
|
被引
6
次
|
|
|
|
|
8.
Godard H P. The Corrosion of Light Metals[M].
The Corrosion of Light Metals,1967:3
|
被引
4
次
|
|
|
|
|
9.
吴瑾光. 近代傅立叶变换红外光谱技术及应用(下卷)[M].
近代傅立叶变换红外光谱技术及应用(下卷),1994:272
|
被引
1
次
|
|
|
|
|
10.
Nyquist R A. Infrared Spectra of Inorganic Compounds[M].
Infrared Spectra of Inorganic Compounds,1971:16
|
被引
1
次
|
|
|
|
|
11.
吴瑾光. 近代傅立叶变换红外光谱技术及应用(上卷)[M].
近代傅立叶变换红外光谱技术及应用(上卷),1994:606
|
被引
1
次
|
|
|
|
|
12.
Lobnig R E. Atmospheric corrosion of zinc in the presence of ammonium sulfate particle[J].
Journal of the Electrochemical Society,1996,143(5):1539-1546
|
被引
8
次
|
|
|
|
|
13.
刘世宏. X射线光电子能谱分析[M].
X射线光电子能谱分析,1988:305
|
被引
3
次
|
|
|
|
|
14.
Kaeshe H. Passivity of Metals[M].
Passivity of Metals,1978:935
|
被引
1
次
|
|
|
|
|
15.
Foroulis Z A. A study of the pitting corrosion of Al by scanning electron microscopy[J].
Werkstoffe und Korrosion,1975,5:350-355
|
被引
1
次
|
|
|
|
|
16.
Richardson J A. A study of the pitting corrosion of Al by scanning electron microscopy[J].
Corrosion Science,1970,10:313-323
|
被引
3
次
|
|
|
|
|
17.
Stumm W. Aquatic Surface Chemistry.
Chemical Processes at the Particle-Water Interface,1987:197
|
被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问