高强度铸造Al-Si-Cu-Mg合金时效特性的研究
Age Hardening Characteristics of High Strength Cast Al-Si-Cu-Mg Alloy

查看参考文献11篇

李润霞 1   李荣德 1   杨秀英 1   李晨曦 1   胡壮麒 2  
文摘 研究了354合金的时效强化行为.试验结果表明,随着时效温度的升高,时效硬化速率增加而时效硬化能力降低.同时发现,在一定温度以上时效,其硬化曲线上出现了两个硬化峰,并且第一个峰值大于第二个峰值.透射电镜试验分析证实,时效硬化的"双峰"现象与时效析出相的析出序列有关,第一个硬化峰主要是由GP区(主要为GPⅡ区)的强化引起的,而第二个时效硬化峰则主要是由亚稳相θ(Al2Cu)和β(Mg2Si)的强化效果造成的,同时孕育期较长的S(Al2Cu Mg)相的析出也可能是引起第二个峰值的一个重要原因.
其他语种文摘 The age hardening characteristics of 354 alloy have been investigated in this paper. The amount and density of GP zone is the key to age hardening, while the density and size of GP zone are mainly decided by the aging temperature. It is shown that the rate of age hardening is raised, but the capability of age hardening reduced with the increase of aging temperature. Two peaks in aging hardening curves have been found also as the aging temperature was raised to a fixed temperature. The result of TEM Observation proved that this phenomenon is related to the precipitation sequence; the first peak is mainly caused by GP zone, and the second one mainly caused by metastable phase θ(Al_2Cu) and p (Mg_2Si), as well as S (AI_2Cu Mg).
来源 铸造 ,2003,52(6):390-394 【核心库】
关键词 铸造铝合金 ; 时效强化 ; 显微组织 ; 双峰时效
地址

1. 沈阳工业大学, 辽宁, 沈阳, 110023  

2. 中国科学院金属研究所, 辽宁, 沈阳, 110016

语种 中文
文献类型 研究性论文
ISSN 1001-4977
学科 金属学与金属工艺
文献收藏号 CSCD:1485078

参考文献 共 11 共1页

1.  百冈山治. Al-Si系合金[J]. 轻金属加工技术,1991,19:43-46 被引 1    
2.  李荣德. 铸造铝合金热处理技术现状及展望[A]. 第十届全国铸造会议论文集,1998 被引 1    
3.  崔忠析. 崔忠析金属热处理原理[M]. 属热处理原理,1995 被引 1    
4.  杨守杰. Zr对超高强铝合金时效过程的影响[J]. 中国有色金属学报,2002(12):226-230 被引 1    
5.  顾景诚. 顾景诚铝合金时效过程[J]. 轻合金加工技术,1985(3/4):25-28 被引 6    
6.  金头男. 尹志民LD10合金的时效特性[J]. 轻合金加工技术,1996,24:27-30 被引 4    
7.  Allen T. Preageing effects in Al-7 % Si-Mg foundry alloys aluminium [J]. Jahragang,1990,11:1083-1097 被引 1    
8.  Kang H K. Age-hardening characteristics of Al-Si-Cu base cast alloy[J]. AFS,1999,27:507-514 被引 2    
9.  何立子. 东北大学. Al-Mg-Si系合金组织性能,2001 被引 11    
10.  Tensi H M. Influence of heat treatment on the microstructure and mechanical behavior of high strength Al-Si cast alloys [A]. Proceedings of the 16th ASM Heat Treating Society Conference & Exposition,1996:243-247 被引 1    
11.  Garcia Celis A L. Aging in heat treatable cast aluminum alloy [J]. Heat Treatment,1999:372-375 被引 2    
引证文献 6

1 肖代红 Si对铸态Al-5.3Cu-0.8Mg-0.6Ag合金显微组织与时效析出的影响 铸造,2007,56(11):1200-1202
被引 0 次

2 李荣德 稀土对Al-Si-Cu-Mg合金组织和性能的影响 铸造,2008,57(8):818-822
被引 4

显示所有6篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号