Co-Mn-Ni-O热敏纳米粉体的制备及其特性
Preparation and properties of nanometer powder for Co-Mn-Ni-O thermistors
查看参考文献10篇
|
文摘
|
采用液相共沉淀法用草酸作为沉淀剂制备了Co-Mn-Ni-O陶瓷热敏电阻纳米粉体，并采用综合热分析（TG、DTA）、X射线衍射（XRD）和扫描电子显微技术（SEM）对该法制备的粉体和对照粉体进行了综合表征，结果显示用该方法可以制力求晶粒平均粒径在9nm左右、粉体颗粒形貌呈球形、颗粒粒径在50～100 nm范围内、粒度分布范围较窄的Co-Mn-Ni-O三元系NTC热敏纳米粉体粉体，能够满足Co-Mn-Ni-O陶瓷热敏电阻对粉体的要求。 |
|
其他语种文摘
|
Nanometer powder of Mn - Co - Ni oxides was prepared by using co - precipitation method with oxalic acid as precipitator, and it was tested and analyzed using TG^DTA^XRD^SEM technology. The result shows that the powder of Mn - Co -Ni oxide can be obtained with following properties: grain size about 9nm, near - spherical shape particle with diameter about 50 ~ lOOnm , narrow range of the particle distribution. And these properties meet the requirement for making Co - Mn - Ni - O NTC thermistors. |
|
来源
|
功能材料与器件学报
,2003,9(4):377-380 【扩展库】
|
|
关键词
|
NTC热敏电阻
;
超微细粉体
;
纳米粉体
;
共沉淀法
;
尖晶石
|
|
地址
|
中国科学院新疆理化技术研究所, 新疆, 乌鲁木齐, 830011
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1007-4252 |
|
学科
|
化学 |
|
文献收藏号
|
CSCD:1197802
|
参考文献 共
10
共1页
|
|
1.
王恩信. NTC热敏电阻器的现状与发展趋势 [J].
电子元件与材料,1997,16(4):1-9
|
被引
24
次
|
|
|
|
|
2.
贡长生.
新型功能材料,2001,1:132-136
|
被引
4
次
|
|
|
|
|
3.
Gopal Reddy C V. Preparation and characterization of iron oxide- zirconia nano Powder for itsuse as an ethanol sensor material[A].
103rd Annual Meeting of the American Ceramic Society,2002:67-78
|
被引
1
次
|
|
|
|
|
4.
梁桂勇. 超微粉末的液相制备技术及其比较 [J].
河北师范大学学报 (自然科学版),1999,23(1):97-101,111
|
被引
3
次
|
|
|
|
|
5.
Sunuk Kim. Preparation of Undoped Lead Titanate Ceramics via Sol Gel Processing[J].
J Am Ceram Soc,1999,82(2):289-296
|
被引
1
次
|
|
|
|
|
6.
. Manuel Gaudon Christel Laberty- Robert Florence Ansart Philippe Stevens AbelRousset.
Solid State Sciences,2002,4(1):125-133
|
被引
1
次
|
|
|
|
|
7.
王世敏. 纳米材料制备技术 [M].
纳米材料制备技术,2002,2:113
|
被引
1
次
|
|
|
|
|
8.
Schmidt R. Prepara- tion and Performance of Thick Film NTC Thermistors[A].
7th Conference ＆ Exhibition of the European Ceramic Society Pt.2,2002:1417-1420
|
被引
1
次
|
|
|
|
|
9.
邬建辉. 草酸盐沉淀法在制备粉体材料中的应用 [J].
四川有色金属,2001,3:13-16
|
被引
8
次
|
|
|
|
|
10.
LI Xiaobin. Preparation of zirconia-alumina powder by co-precipitation.
Transactions of Nonferrous Metals Society of China,2000,10(2):257-260
|
被引
1
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问