USSP表面纳米化Fe-20Cr合金的腐蚀性能及机制研究
Corrosion Behavior of Fe-20Cr Alloy Treated by Ultrasonic Shot Peening Technique

查看参考文献3篇

李雪莉 1   李瑛 1   王福会 1   雍兴平 2  
文摘 利用电化学方法，结合XRD、EDX、SEM和EPMA等表面分析技术，研究了经超声喷丸表面纳米化的Fe-20Cr合金在0．05mol/L H2SO4+0.5mol/L NaCl溶液中的腐蚀性能。结果表明，纳米化后合金的耐蚀性能降低。相对于粗晶合金，纳米材料晶粒的细化、钝化金属中Cr元素分析的均匀性降低以及超声喷丸技术在制备纳米晶过程中所带来的残余应力是纳米材料耐蚀性能降低的原因。
其他语种文摘 Electrochemical methods and XRD,EDX,SEM, EPMA technique were used to investigate the corro-sion performance of nanocrystallized Fe - 20Cr surface which was fabricated by using an ultrasonic shot .peening (USSP)technique, and the corrosion solution was 0.05 mol/L F_2SO_4 + 0.5 mol/L NaCl.The results show that the capability of corrosion resistance of the SNC Fe - 20Cr alloy was lower than that of the cast alloy. Contrast to the cast alloy, the reduction of the grain size, the less uniform passive element of Cr, and the remnant strain caused by USSP technique are thought to be the main reasons which result in the poorer corrosion resistance of nanocrystal alloy.
来源 中国腐蚀与防护学报 ,2002,22(6):326-329,334 【核心库】
关键词 超声喷丸 ; 表面纳米化 ; Fe-20Cr ; 钝化 ; 残余应力
地址

1. 中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016  

2. 中国科学院金属研究所, 快速凝固非平衡国家重点实验室, 沈阳, 110016

语种 中文
文献类型 研究性论文
ISSN 1005-4537
学科 金属学与金属工艺
基金 国家自然科学基金
文献收藏号 CSCD:1121710

参考文献 共 3 共1页

1.  Tao N R. Nanostructured Materials,1999,11(4):433 被引 74 次    
2.  Lu K. J. Mater. Sci. Technol.,1999,15(3):193 被引 205 次    
3.  Lug H P K. X-Ray Diffraction Procedures for Polycrystalline and Amorphous Materials,1974 被引 1 次    
引证文献 12 篇

1 李瑛 磁控溅射IN738涂层耐盐水腐蚀性能研究 中国腐蚀与防护学报,2002,22(6):349-354
被引 0 次

2 吕爱强 表面纳米化对316L不锈钢性能的影响 材料研究学报,2005,19(2):118-124
被引 19 次

显示所有12篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护：中国科学院文献情报中心
地址：北京中关村北四环西路33号 邮政编码：100190 联系电话：(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号