K38G合金及其纳米晶涂层在900 ℃溶融硫酸盐中的热腐蚀行为
Corrosion behavior of K38G alloy and its nanocrystalline coating in molten sulfate at 900℃
查看参考文献9篇
|
文摘
|
用磁控溅射法在K38G合金上溅射了一层与其成分丰同的纳米晶涂层，研究了铸态合金及其溅射纳米晶涂层在900 ℃的75%Na_2SO_4 + 25%K_2SO_4中的热腐蚀行为，结果表明，K38G合金经溅射形成纳米晶涂层后，腐蚀过程中能生成一层连续的Al_2O_3外氧化膜，延长了失稳氧化的孕育期，提高了合金的抗热腐蚀能力，并讨论了铸态合金及纳米晶涂层的热腐蚀机理。 |
|
其他语种文摘
|
A nanocrystalline coating with the same composition as K38G alloy was sputtered on the substrate alloy K38G by means of magnetron sputtering method. The corrosion behavior of cast alloy and its sputtered nanocrystalline coating in molten 75%Na_2SO_4 + 25%K_2SO_4 at 900 ℃ were studied. The results indicate that the coating prolonged the incubation of the breakaway corrosion and improved the hog corrosion resistance of K38G alloy due to the formation of a continuous and compact Al_2O_3 scale on it. The hot corrosion mechanisms of the cast alloy and the coating were discussed. |
|
来源
|
金属学报
,2002,38(8):871-876 【核心库】
|
|
关键词
|
K38G合金
;
溅射
;
纳米晶涂层
;
熔盐
;
热腐蚀
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金国家杰出青年科学基金
;
国家自然科学基金
;
中国科学院“百人计划”项目
|
|
文献收藏号
|
CSCD:1027915
|
参考文献 共
9
共1页
|
|
1.
Wang F.
Chin J Met Sci Technol,1990,6:61
|
被引
3
次
|
|
|
|
|
2.
Lou H.
Oxid Met,1992,38:299
|
被引
9
次
|
|
|
|
|
3.
Lou H.
Surf Coat Technol,1994,63:105
|
被引
11
次
|
|
|
|
|
4.
Wang F.
Oxid met,1997,48:215
|
被引
18
次
|
|
|
|
|
5.
王福会. 微晶化对高温合金K38G在CO气氛中腐蚀的影响.
金属学报,1997,33:1035
|
被引
4
次
|
|
|
|
|
6.
Goebel J A.
Metall Trans,1970,1:1943
|
被引
24
次
|
|
|
|
|
7.
Goebel J A.
Metall Trans,1973,4:261
|
被引
20
次
|
|
|
|
|
8.
王茂才.
中国腐蚀与防护学报,1986,6:65
|
被引
1
次
|
|
|
|
|
9.
张允书. 金属氧化物在熔融Na↓2SO↓4中的溶解行为.
中国腐蚀与防护学报,1989,9:121
|
被引
5
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问