Ti_3SiC_2在900 ℃与1000 ℃下的热腐蚀行为
Hot corrosion of Ti_3SiC_2-based ceramic in molten Na_2SO_4 at 900 ℃ and 1000 ℃
查看参考文献8篇
文摘
|
研究了Ti_3SiC_2三元层状陶瓷材料在900 ℃和1000 ℃下由Na_2SO_4盐膜引起的热腐蚀行为。用XRD及SEM分析了腐蚀产物膜的成分、结构和形貌等。实验表明,腐蚀膜由TiO_2和SiO_2混合组成:在结构上明显地分成两层,外层晶粒粗大且多孔,内层晶粒细小且致密。Ti_3SiC_2与熔融盐接触遭受严重的腐蚀。 |
其他语种文摘
|
The hot corrosion behaviors of polycrystalline bulk samples of Ti_3SiC_2 coated with Na_2SO_4 film were studied at 900 ℃ and 1000 ℃ in air. The surface morphology, structure and composition of scales were investigated by SEM/EDS and XRD. It was shown that Ti_3SiC_2 suffered from serious hot corrosion at 900 ℃ and 1000 ℃. The oxide scales have a duplex structure. The outer layer consists of coarse grains with many pores, while the inner layer consists of fine grain and is compact. The mixtures of TiO_2 an SiO_2 formed during the hot corrosion are different from those of Ti_3SiC_2 oxidized in air. |
来源
|
金属学报
,2002,38(4):417-420 【核心库】
|
关键词
|
Ti_3SiC_2
;
热腐蚀
;
氧化膜
|
地址
|
中国科学院金属研究所, 沈阳材料科学国家(联合)实验室, 沈阳, 110016
|
语种
|
中文 |
文献类型
|
研究性论文 |
ISSN
|
0412-1961 |
学科
|
金属学与金属工艺 |
基金
|
国家自然科学基金国家杰出青年科学基金
|
文献收藏号
|
CSCD:1027757
|
参考文献 共
8
共1页
|
1.
Elraghy T.
J Am Ceram Soc,1997,80:513
|
被引
2
次
|
|
|
|
2.
Racault C.
J Mater Sci,1994,29:3384
|
被引
27
次
|
|
|
|
3.
Gao N F.
J Mater Sci,1999,34:4385
|
被引
26
次
|
|
|
|
4.
Barsoum M W.
J Am Ceram Soc,1996,79:1953
|
被引
142
次
|
|
|
|
5.
Broum M W.
J Electrochem Soc,1997,144:2508
|
被引
27
次
|
|
|
|
6.
Feng A.
J Mater Res,1999,14:925
|
被引
11
次
|
|
|
|
7.
Turkdogan E T.
Physical Chemistry of High Temperature Technology,1980
|
被引
28
次
|
|
|
|
8.
张允书.
中国腐蚀与防护学报,1992,12
|
被引
1
次
|
|
|
|
|
|