不锈钢在含SO_4~(2-)稀HCl中的电化学腐蚀行为
Electrochemical corrosion behavior of stainless steel in dilute hydrochloric acid media containing SO_4~(2-) ions
查看参考文献11篇
|
文摘
|
应用电化学测量技术研究了1Cr18Ti9Ti和316L在含硫酸盐SO_4~(2-)的稀HCl介质中的腐蚀行为。极化曲线测量结果表明，SO_4~(2-)能显著抑制1Cr18Ni9Ti的点蚀，而对316L的腐蚀有加速作用并降低其钝化性能。电化学阻抗谱测量结果表明，不锈钢表面钝化膜的保护性随着温度升高而降低。 |
|
其他语种文摘
|
The corrosion behavior of 1Cr18Ti9Ti and 316L stainless steels had been investigated in dilute hydrochloric acid media containing sulfate by using electrochemical techniques. The polarization curves showed that the pitting behavior of 1Cr18Ni9Ti was inhibited markedly by SO_4~(2-) ions, while the corrosion rate of 316L was accelerated by SO_4~(2-) ions. The potentiostatic polarization at 600 mV vs. SCE for 316L in 0.01 mol/L Na_2SO_4 + 0.01 mol/L HCl solution at 80 ℃ didn't verify that the passive state had perfect stability. The electrochemical impedance spectroscopy (EIS) measurements indicated that the protective performance of passive film on stainless steel surface decreased with increasing the temperature of the test solutions. |
|
来源
|
腐蚀科学与防护技术
,2002,14(3):132-135 【核心库】
|
|
关键词
|
硫酸盐
;
电化学腐蚀
;
不锈钢
;
质子交换膜燃料电池
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-6495 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家973计划
|
|
文献收藏号
|
CSCD:983784
|
参考文献 共
11
共1页
|
|
1.
衣宝廉.
燃料电池,2000:56
|
CSCD被引
5
次
|
|
|
|
|
2.
Hornung R.
J. Power Sources,1998,72:20
|
CSCD被引
18
次
|
|
|
|
|
3.
Davies D P.
J. Power Sources,2000,86:237
|
CSCD被引
38
次
|
|
|
|
|
4.
Makkus R C.
J. Power Sources,2000,86:274
|
CSCD被引
22
次
|
|
|
|
|
5.
Macdonald D D.
J. Electrochem. Soc.,1973,120(3):317
|
CSCD被引
2
次
|
|
|
|
|
6.
Strehblow H H.
Werkst. Korros.,1984,35:437
|
CSCD被引
4
次
|
|
|
|
|
7.
Leckie H P.
J. Electrochem. Soc.,1966,113:1262
|
CSCD被引
10
次
|
|
|
|
|
8.
Pistorius P C.
Corros. Sci.,1992,33:1885
|
CSCD被引
25
次
|
|
|
|
|
9.
Marcus P.
Corrosion Mechanisms in Theory and Practice,1995:201
|
CSCD被引
2
次
|
|
|
|
|
10.
Carranza R M.
Corros. Sci.,1996,38:909
|
CSCD被引
7
次
|
|
|
|
|
11.
Juttner K.
Corros. Sci.,1989,29:279
|
CSCD被引
3
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问