机械合金化Zr-Al-Ni-Cu-Ag非晶合金的晶化行为
Crystallization of mechanically alloyed amorphous Zr-Al-Ni-Cu-Ag alloy
查看参考文献16篇
|
文摘
|
研究了机械合金化非晶态Zr_(65)Al_(7.5)Ni_(10)Cu_(7.5)Ag_(10)合金的晶化过程。由于存在扩散不均匀区，机械合金化非晶合金在深过冷液相区的退火组织不同于快淬合金。在深过冷液相区退火，析出二十面体准晶相及一些未知相；在靠近第一个放热峰的温度退火，析出Zr_2Cu相；第二个放热峰对应残余非晶相及准晶相向Zr_2Ni、Zr_2Al_3的转变。 |
|
其他语种文摘
|
The multicomponent Zr-Al-Ni-Cu-Ag amorphous alloy powders were obtained by mechanical alloying from the elemental constituents. The crystallization of mechanical alloyed amorphous Zr-based alloy was studied by DSC, X-ray diffraction. After isothermally annealed at a temperature in the supercooled liquid region, the icosahedral quasicrystal and some unknown phases precipitated in the Zr_(65)Al_(7.5)Ni_(10)Cu_(7.5)Ag_(10) amorphous alloys. After annealing at 712K, Zr_2Cu phase precipitated. After the samples were annealed at 758K, the Zr_2Cu phase were found as a single precipitation phase. The transformation of the amorphous alloy upon heating can be represented as follows: amorphous phase→icosahedral phase+amorphase→+amorphous phase→ZrCu + Zr_2Cu + Zr_2Ni + Zr_2Al_3. |
|
来源
|
材料研究学报
,2002,16(1):9-12 【核心库】
|
|
关键词
|
机械合金化
|
|
地址
|
中国科学院金属研究所, 沈阳材料国家（联合）实验室
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-3093 |
|
学科
|
一般工业技术 |
|
基金
|
国家973计划
|
|
文献收藏号
|
CSCD:959175
|
参考文献 共
16
共1页
|
|
1.
Zhang T.
Mater.Trans., JIM,1991,32:1005
|
CSCD被引
76
次
|
|
|
|
|
2.
A. Peter.
Appl.Phys.Lett.,1993,63:2342
|
CSCD被引
290
次
|
|
|
|
|
3.
Inoue A..
Mater.Trans., JIM,1991,31:425
|
CSCD被引
5
次
|
|
|
|
|
4.
A. Inoue.
Mater.Sci.Engng.A,1993,173:1
|
CSCD被引
31
次
|
|
|
|
|
5.
A. Inoue.
Bulk amorphous alloys,1998:27
|
CSCD被引
1
次
|
|
|
|
|
6.
U. Koster.
Mater.Sci.Engng.A,1997,226:995
|
CSCD被引
7
次
|
|
|
|
|
7.
J. Eckert.
Mater.Trans., JIM,1998,36:623
|
CSCD被引
18
次
|
|
|
|
|
8.
Xing L Q.
Appl.Phys.Lett.,1998,74:664
|
CSCD被引
1
次
|
|
|
|
|
9.
Chen M W.
Appl.Phys.Lett.,1999,75:1697
|
CSCD被引
11
次
|
|
|
|
|
10.
Murty B. S..
Scripta Mater,2000,43:103
|
CSCD被引
4
次
|
|
|
|
|
11.
Inoue A..
Appl.Phys.Lett.,2000,76:967
|
CSCD被引
1
次
|
|
|
|
|
12.
Inoue A..
Mater.Trans., JIM,1999,40:1382
|
CSCD被引
9
次
|
|
|
|
|
13.
Saida J..
Appl.Phys.Lett.,1999,75:3497
|
CSCD被引
7
次
|
|
|
|
|
14.
J. Eckert.
Mater.Sci.Engng.A,1997,226:364
|
CSCD被引
5
次
|
|
|
|
|
15.
M. Seidel.
Acta Mater,2000,48:3657
|
CSCD被引
5
次
|
|
|
|
|
16.
Lin X H.
Mater.Trans., JIM,1997,38:473
|
CSCD被引
29
次
|
|
|
|
|
了解气象卫星更多信息，请访问