冲击载荷下纤维复合材料裂纹起裂的实验研究
Experimental Studies on the Initiation of Crack in Fiber-reinforced Composites under Impact Loading
查看参考文献10篇
|
文摘
|
采用SHTB技术对纤维增强复合材料裂纹动态起裂行为进行了实验研究。使用应变片方法确定了裂纹的起裂时间，结合有限元数值模拟得到了裂纹的起裂韧性；同时观察了裂纹在冲击载荷作用下的裂纹起裂和扩展方式，分析了纤维的铺层角度对裂纹起裂和扩增的影响。 |
|
其他语种文摘
|
It is investigated that the initiation of crack in fiber-reinforced composites under impact loading by SHTB experimental technology in this paper. The initiation time of crack is measured by strain gauge on the sample. The fracture toughness of the composite material is determined by FEM numerical simulation. The patterns of fracture of the crack under impact are observed and the influence of plies angle on the growth of the crack is analyzed. |
|
来源
|
爆炸与冲击
,2002,22(2):111-118 【核心库】
|
|
关键词
|
纤维复合材料
;
裂纹的动态起裂
;
冲击
;
SHTB实验
|
|
地址
|
1.
中国科学院力学研究所, 北京, 100080
2.
中国运载火箭技术研究院材料与工艺研究所, 北京, 100076
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-1455 |
|
学科
|
力学 |
|
文献收藏号
|
CSCD:955397
|
参考文献 共
10
共1页
|
|
1.
Aliyu A A.
Effects of Strain Rate on Delamination Fracture Toughness of Graphite/Epoxy,1985:336-348
|
CSCD被引
2
次
|
|
|
|
|
2.
Mall S. Loading Rate Effect on Interlaminar Fracture Toughness of a Themo-plastic Composite.
J Compos Mater,1987,21:569-579
|
CSCD被引
2
次
|
|
|
|
|
3.
Smiley A J. Rate Effects on Mode I Interlaminar Fracture Toughness in Composite Materials.
J Compos Matter,1987,21:670-687
|
CSCD被引
1
次
|
|
|
|
|
4.
绕世国.
材料动态断裂的理论和实验研究,1992:19-55
|
CSCD被引
1
次
|
|
|
|
|
5.
王从约.
杆-杆型冲击拉伸试验系统的动力学数值分析,1996:26-137
|
CSCD被引
1
次
|
|
|
|
|
6.
Harding J. A Tensile Testing Technique for Fiber-reinforced Composites at Impact Rates of Strain.
J Mater Sci,1983,18:1810
|
CSCD被引
18
次
|
|
|
|
|
7.
Dally J W. Strain Gage Methods for Measuring the Opening Mode Stress Intensity Factor K_1.
Proc 1985 SEM Spring Conf On Exp Mech,1985:851-860
|
CSCD被引
1
次
|
|
|
|
|
8.
Dally J W. Dynamic Measurements of Initiation Toughness at High Loading Rates.
Experimental Mechanics,1988,28(9):298-303
|
CSCD被引
6
次
|
|
|
|
|
9.
林君山. Charpy裂纹试样的起裂点确定与动态断裂韧性.
金属学报（A）,1992,28(4):170-175
|
CSCD被引
1
次
|
|
|
|
|
10.
Shih C F. Crack Extension Modeling with Singular Quadratic Isoparametric Elements.
Inter J Fracturere,1976,12:647-651
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问