喷丸对DD412单晶高温合金表面完整性和疲劳性能的影响
Effects of shot peening on surface integrity and fatigue properties of DD412 single crystal superalloy
查看参考文献24篇
|
文摘
|
为提高涡轮叶片榫头的疲劳性能,研究了喷丸对DD412单晶合金表面完整性和高温疲劳性能的影响规律。采用白光干涉仪、粗糙度仪、显微硬度计、扫描电镜、透射电镜等分别对喷丸前后的表面形貌、粗糙度、硬度梯度、微观组织进行表征,并采用旋弯疲劳试验机测试高温疲劳寿命和极限。结果表明:喷丸后,表面磨削刀痕被消除,显著降低表面微观应力集中系数;试样表层组织发生剧烈塑性变形,并形成深度约0.10~0.32 mm的硬化层。相比未喷丸试样,优化工艺喷丸试样在600 ℃/500 MPa条件下的旋弯中值疲劳寿命提高21.7倍以上,在600 ℃下的中值疲劳极限提高了17.3%。经分析认为,喷丸对表面完整性的优化是DD412合金高温疲劳性能提升的主要原因。 |
|
其他语种文摘
|
To improve the fatigue performance of turbine blade tenon, the effect of shot peening on the surface integrity and high temperature fatigue performance of DD412 single crystal alloy was investigated. The surface morphology, roughness, hardness gradient and microstructure after shot peening were characterized by white light interferometer, roughness tester,microhardness tester, scanning electron microscope and transmission electron microscope respectively. The results show that after shot peening,the surface grinding tool marks are eliminated, and the surface micro stress concentration factor is significantly reduced. Severe plastic deformation occurr in the surface layer of the specimen, and a hardened layer with a depth of about 0.10-0.32 mm is formed. The mean fatigue life of the optimal shot peening specimens at 600 ℃/500 MPa is increased by more than 21.7 times, and the median fatigue limit at 600 ℃ is increased by 17.3%. The favorable change of surface integrity is the main reason for the improvement of high temperature fatigue properties of DD412 alloy after shot peening. |
|
来源
|
材料工程
,2024,52(7):152-161 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2023.000680
|
|
关键词
|
喷丸
;
单晶合金
;
表面完整性
;
疲劳寿命
;
微观组织
;
硬度
|
|
地址
|
1.
中国航发北京航空材料研究院表面工程研究所, 北京, 100095
2.
中国航发北京航空材料研究院, 航空材料先进腐蚀与防护航空科技重点实验室, 北京, 100095
3.
中国航发北京航空材料研究院, 先进高温结构材料国家重点实验室, 北京, 100095
4.
北京航空航天大学材料科学与工程学院, 北京, 100191
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
一般工业技术;金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
国家重大科技专项
|
|
文献收藏号
|
CSCD:7782221
|
参考文献 共
24
共2页
|
|
1.
陈荣章. 航空铸造涡轮叶片合金和工艺发展的回顾与展望.
航空制造技术,2002(2):19-23
|
CSCD被引
20
次
|
|
|
|
|
2.
Gell M L. The development of single crystal superalloy turbine blades.
Superalloys,1980:205-214
|
CSCD被引
1
次
|
|
|
|
|
3.
李嘉荣. 第二代单晶高温合金DD6在980℃长期时效后的显微组织与持久性能.
稀有金属材料与工程,2007(10):1784-1787
|
CSCD被引
7
次
|
|
|
|
|
4.
Cetel A D. Second-generation nickel-base single crystal superalloy.
Superalloys,1988:235-244
|
CSCD被引
3
次
|
|
|
|
|
5.
Fleury R M N. The influence of contacting Ni-based single-crystal superalloys on fretting fatigue of Ni-based polycrystalline superalloys at high temperature.
Tribology International,2014,76:63-72
|
CSCD被引
3
次
|
|
|
|
|
6.
Murthy H. Fretting fatigue of single crystal nickel at 600℃.
Tribology International,2006,39(10):1227-1240
|
CSCD被引
4
次
|
|
|
|
|
7.
Zhang J. Low-Cycle Fatigue and Creep-Fatigue Behaviors of a Second-Generation Nickel-Based Single-Crystal Superalloy at 760 °C.
Acta Metallurgica Sinica (English Letters),2020,33(10):1423-1432
|
CSCD被引
4
次
|
|
|
|
|
8.
陈艳华.
镍基单晶高温合金喷丸层塑性变形行为及其表征研究,2016
|
CSCD被引
1
次
|
|
|
|
|
9.
王东林. 利用喷丸再结晶方法提高K417合金的疲劳寿命.
稀有金属材料与工程,2006(8):1294-1298
|
CSCD被引
9
次
|
|
|
|
|
10.
Foss B J. Analysis of shotpeening and residual stress relaxation in the nickel-based superalloy RR1000.
Acta Materialia,2013,61(7):2548-2559
|
CSCD被引
15
次
|
|
|
|
|
11.
Bogachev I. Electron backscattered diffraction analysis of cold work in a shot peened single crystal nickel superalloy.
Acta Materialia,2020,14:100860
|
CSCD被引
4
次
|
|
|
|
|
12.
姜涛. 喷丸对DZ4合金旋转弯曲疲劳断裂特征的影响.
宇航材料工艺,2013,43(3):120-125
|
CSCD被引
3
次
|
|
|
|
|
13.
王欣. 陶瓷弹丸喷丸强化对DD6单晶高温合金表面完整性的影响.
材料工程,2014(4):53-57
|
CSCD被引
10
次
|
|
|
|
|
14.
王欣. 喷丸对第三代单晶合金DD10组织和高温缺口疲劳性能的影响.
第十一次全国热处理大会论文集,2015:768-771
|
CSCD被引
1
次
|
|
|
|
|
15.
王欣. 喷丸对单晶合金中温疲劳性能的强化机制.
航空制造技术,2020,63(12):46-52
|
CSCD被引
4
次
|
|
|
|
|
16.
王仁智. 金属材料的喷丸强化原理及其强化机理综述.
中国表面工程,2012,25(6):1-9
|
CSCD被引
54
次
|
|
|
|
|
17.
Li J. An analysis of stress concentrations caused by shot peening and its application in predicting fatigue strength.
Fatigue & Fracture of Engineering Materials & Structures,1992,15:1271-1279
|
CSCD被引
12
次
|
|
|
|
|
18.
吴庆辉. 喷丸处理对DD6合金表面状态和中温疲劳性能的影响.
热加工工艺,2017,46(12):158-161
|
CSCD被引
4
次
|
|
|
|
|
19.
王欣. 镍基单晶合金中温疲劳性能应力集中敏感性.
材料科学与工艺,2017,25(3):58-62
|
CSCD被引
1
次
|
|
|
|
|
20.
李国禄. 表面强化后梯度结构与残余应力对疲劳寿命的影响.
表面技术,2019(9):1-10
|
CSCD被引
9
次
|
|
|
|
|
了解气象卫星更多信息，请访问