TA15钛合金表面原位合成TiC增强钛基激光熔覆层的组织与耐磨性
Microstructure and wear resistance of in-situ TiC reinforced Ti-based coating by laser cladding on TA15titanium alloy surface

查看参考文献26篇

安强 1   祁文军 1 *   左小刚 2  
文摘 采用激光熔覆技术在TA15钛合金表面原位合成TiC增强钛基涂层。利用光学显微镜、扫描电镜、X射线衍射仪、能谱分析仪、显微硬度计、摩擦磨损试验机等研究涂层的成形质量、微观组织、物相组成、硬度和摩擦学性能。结果表明:涂层主要由β-Ti,Co_3Ti,CrTi_4和TiC等物相组成,涂层与基体形成了良好的冶金结合。涂层结合区组织是平面晶和柱状晶,中部组织是树枝晶,顶部组织是等轴晶。涂层各微区的碳化钛形貌有显著差别,其中顶部和中部区域碳化钛为粗大的树枝状和花瓣状,而结合区为针状和近球状。涂层显微硬度最大值为715HV,约是TA15显微硬度(330HV)的2.1倍;同等条件下涂层磨损量为30.14mg,约为TA15磨损量98.11mg的30.7%。涂层与基体的磨损机制均为磨粒磨损和黏着磨损的复合磨损模式,但涂层的磨损程度较轻。
其他语种文摘 The TiC-reinforced Ti-based coating was prepared in-situ on the surface of the titanium alloy TA15 by laser cladding technology.The forming quality,microstructure,phase composition, hardness,and tribological properties were investigated by optical microscope,X-ray diffractometer, scanning electron microscope,energy spectrum analyzer,microhardness tester and friction and wear apparatus.The results show that the coating mainly composes ofβ-Ti,Co_3Ti,CrTi_4 and TiC,and the good metallurgical bond is formed between coating and the substrate.The microstructure of the coating bond zone is planar crystal and columnar crystal,the middle is dendritic,and the top is equiaxed.Significant differences in the morphology of TiC are observed in each micro-area of the coating.TiC of the top and middle areas is thick dendritic and petal-like,while TiC of the bonding area is needle-like and spherical.The maximum microhardness of the coating is 715HV,which is about 2.1times than that of TA15(330HV).Under the same conditions,the wear loss of coating is 30.14mg,which is about 30.7%of TA15(98.11mg).The wear mechanism of the cladding coating and substrate is a composite wear mode of adhesive wear and abrasive wear,but the wear degree of the coating is lighter.
来源 材料工程 ,2022,50(4):139-146 【核心库】
DOI 10.11868/j.issn.1001-4381.2020.000996
关键词 TA15 ; 激光熔覆 ; 钛基涂层 ; 微观组织 ; 耐磨性
地址

1. 新疆大学机械工程学院, 乌鲁木齐, 830047  

2. 新疆众合股份有限公司, 乌鲁木齐, 830013

语种 中文
文献类型 研究性论文
ISSN 1001-4381
学科 金属学与金属工艺
基金 新疆维吾尔自治区高校科研计划自然科学重点项目 ;  新疆维吾尔自治区自然科学基金
文献收藏号 CSCD:7208414

参考文献 共 26 共2页

1.  于新年. 钛合金表面缺陷的激光熔覆修复研究. 航空制造技术,2011(16):116-118 CSCD被引 4 次    
2.  Weng F. Microstructures and wear properties of laser cladding Co-based composite coatings on Ti-6Al-4V. Materials & Design,2015,80:174-181 CSCD被引 41 次    
3.  贺星. 激光熔覆Al-Ni-TiC-CeO_2复合涂层的组织与耐腐蚀磨损性能. 材料工程,2019,47(10):68-75 CSCD被引 4 次    
4.  杨胶溪. TiC含量对激光熔覆制备TiC/Ti基复合涂层组织与性能的影响. 航空材料学报,2018,38(3):65-71 CSCD被引 4 次    
5.  李嘉宁. TA15钛合金激光非晶-纳米晶增强镍基涂层的组织结构及耐磨性. 焊接学报,2014,35(10):57-60 CSCD被引 6 次    
6.  Liu S S. Microstructure and wear resistance of laser clad cobalt-based composite coating on TA15surface. Rare Metal Materials & Engineering,2014,43(5):1041-1046 CSCD被引 11 次    
7.  张天刚. 钛基稀土激光熔覆层组织细化机制及性能. 航空学报,2020,41(9):334-347 CSCD被引 5 次    
8.  Zhang K M. Surface modification of TC4 Ti alloy by laser cladding with TiC+Ti powders. Transactions of Nonferrous Metals Society of China,2010,20(11):2192-2197 CSCD被引 26 次    
9.  Shakti K. Parametric study and characterization of AlN-Ni-Ti_6Al_4Vcomposite cladding on titanium alloy. Surface and Coatings Technology,2018,349:37-49 CSCD被引 7 次    
10.  刘亚楠. Ti811表面激光熔覆复合涂层的微观组织及摩擦磨损性能. 中国激光,2019,46(1):157-165 CSCD被引 5 次    
11.  Liu Y B. Fabrication and mechanical properties of in situ TiC/Ti metal matrix composites. Journal of Alloys &Compounds,2011,509(8):3592-3601 CSCD被引 4 次    
12.  杨玉玲. 激光熔覆Ti／C混合粉末原位生成TiC的研究. 应用激光,2008,28(1):6-8 CSCD被引 6 次    
13.  谢亚东. 基于激光熔覆的高铁钢轨强化研究,2017 CSCD被引 4 次    
14.  林熙. TC4表面激光熔覆耐磨涂层组织结构及性能的研究,2018 CSCD被引 3 次    
15.  王红颖. 工具钢表面激光熔覆Co基合金涂层的组织及性能. 吉林大学学报(工学版),2010,40(4):1000-1004 CSCD被引 10 次    
16.  任超. 17-4PH不锈钢表面激光熔覆Stellite6涂层组织及耐水蚀性能. 中国激光,2017,44(4):107-114 CSCD被引 7 次    
17.  Yu S. Effects of combined plasma chromizing and shot peening on the fatigue properties of a Ti_6Al_4Valloy. Applied Surface Science,2015,353:995-1002 CSCD被引 8 次    
18.  Wei D B. Oxidation of double-glow plasma chromising coating on TC4titanium alloys. Corrosion Science,2013,66:43-50 CSCD被引 15 次    
19.  王浩. Ti811表面TC4激光熔覆层的β相变行为. 金属热处理,2019,44(1):167-171 CSCD被引 2 次    
20.  张志强. 激光熔覆碳化钛增强钛基复合涂层研究进展. 表面技术,2020,49(10):138-151 CSCD被引 15 次    
引证文献 3 篇

1 寇斐凡 TiB_2含量对TiB_x/Ti合金涂层组织及摩擦学性能的影响 表面技术,2024,53(11):140-149
CSCD被引 1 次

2 刘雨薇 钛合金摩擦磨损性能及减磨方法研究进展 表面技术,2024,53(12):1-21
CSCD被引 2 次

显示所有3篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护：中国科学院文献情报中心
地址：北京中关村北四环西路33号 邮政编码：100190 联系电话：(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号