Cl~- 对S450AW在酸性环境中腐蚀行为的影响
Effect of Cl~- Ions on the Corrosion Behaviors of S450AW in Acidic Medium
查看参考文献18篇
|
文摘
|
为探索S450AW在Cl~-中的腐蚀行为,采用全浸试验、电化学试验和XPS分析技术研究了Cl~-浓度对含Sb耐蚀钢S450AW在0.1 mol/L H_2SO_4水溶液中腐蚀行为以及S450AW腐蚀产物层中合金元素分布规律的影响。结果表明: Cl~-对S450AW在酸性环境下具有缓蚀作用,并且随着Cl~- 浓度的增加,缓蚀效果越显著。XPS结果表明,不同Cl~-浓度下的腐蚀产物均为Fe_3O_4、FeOOH及少量合金元素的稳态氧化物,Cl~-能够促进合金元素在锈层中沉积形成富集合金元素的致密锈层,从而提高S450AW在酸性环境下的抗蚀性。 |
|
其他语种文摘
|
In order to explore the corrosion behaviors of S450AW in the medium with Cl~- ions,the effects of Cl~- on the corrosion behavior of Sb -contained weathering steel S450AW in 0.1 mol/L sulfuric acid solution and the element distributions of S450AW corrosion products were studied by immersion test,electrochemical measurement and X-ray photoelectron spectroscopy(XPS)analysis.Results showed that Cl~- ions could inhibit the corrosion of S450AW in acidic environment,and the corrosion inhibition effect increased with the increase of Clconcentrations.Moreover,XPS results showed that the corrosion products formed with different Cl~- concentrations were composed of Fe_3O_4,FeOOH and a small amount of stable oxides of alloy elements.Owing to promoting the deposition of alloy elements in the rust layer,Cl~- ions could improve the corrosion resistance of S450AW in acidic medium. |
|
来源
|
材料保护
,2020,53(2):21-25,36 【扩展库】
|
|
关键词
|
含Sb耐蚀钢
;
Cl~-
;
酸性环境
;
全浸试验
;
电化学试验
;
XPS分析
;
缓蚀作用
|
|
地址
|
1.
鞍钢集团钢铁研究院, 辽宁, 鞍山, 114021
2.
中国科学院金属研究所石油化工材料腐蚀安全评价实验室, 辽宁, 沈阳, 110016
3.
北京科技大学国家材料服役安全科学中心, 北京, 100083
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-1560 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家重点研发计划
;
国家自然科学基金
|
|
文献收藏号
|
CSCD:6724290
|
参考文献 共
18
共1页
|
|
1.
郭晓宏. 鞍钢铁路货车车体用钢研发历程.
鞍钢技术,2018(4):9-14
|
CSCD被引
4
次
|
|
|
|
|
2.
宋凤明. 铁道车辆用耐大气腐蚀钢的现状及研发方向.
世界钢铁,2009,9(5):11
|
CSCD被引
7
次
|
|
|
|
|
3.
张琳. 模拟海洋工业大气环境中Q235钢及耐候钢的腐蚀行为.
材料保护,2015,48(2):19-22
|
CSCD被引
5
次
|
|
|
|
|
4.
汪兵. Cr含量对耐候钢耐候性的影响.
材料保护,2014,47(5):61-63
|
CSCD被引
7
次
|
|
|
|
|
5.
汪兵. 组织类型对耐候钢耐大气腐蚀性能的影响.
材料保护,2013,46(7):62-63
|
CSCD被引
2
次
|
|
|
|
|
6.
Wang Y F. Effect of pH and chloride on the micro-mechanism of pitting corrosion for high strength pipeline steel in aerated NaCl solutions.
Applied Surface Science,2015,349:746-756
|
CSCD被引
29
次
|
|
|
|
|
7.
郝献超. 不同NaCl浓度对耐候钢腐蚀产物的影响.
腐蚀与防护,2009,30(5):297-299
|
CSCD被引
8
次
|
|
|
|
|
8.
王志奋. 环境中氯离子浓度对耐候钢耐腐蚀性能的影响.
武汉科技大学学报,2013,36(3):190-194
|
CSCD被引
3
次
|
|
|
|
|
9.
游明锐. 温度和氯离子浓度对30CrMnSiNiA腐蚀速率的影响研究.
装备环境工程,2017,14(9):93-98
|
CSCD被引
4
次
|
|
|
|
|
10.
Nam N D. Effect of tin on the corrosion behavior of low-alloy steel in an acid chloride solution.
Corrosion Science,2010,52(1):14-20
|
CSCD被引
24
次
|
|
|
|
|
11.
Park S A. Effect of chloride ions on the corrosion behavior of low-alloy steel containing copper and antimony in sulfuric acid solution.
Metals and Materials International,2015,21(3):470-478
|
CSCD被引
5
次
|
|
|
|
|
12.
黄涛. 高强耐候钢在NaCl溶液中的腐蚀锈层特征和耐腐蚀性研究.
机械工程学报,2017,53(20):45-53
|
CSCD被引
9
次
|
|
|
|
|
13.
陈小平. 耐候钢锈层组织成分及其耐腐蚀机制分析.
材料保护,2009,42(1):18-20
|
CSCD被引
9
次
|
|
|
|
|
14.
Dong J H.
The Synergistic Inhibition to Atmospheric Corrosion in Mn-Cu Alloying Steel: Second International Conference On Advanced Structural Steels,2004:332-335
|
CSCD被引
1
次
|
|
|
|
|
15.
刘国超. Cu、Mn的协同作用对低合金钢在模拟海洋大气环境中腐蚀的影响.
腐蚀科学与防护技术,2008(4):235-238
|
CSCD被引
17
次
|
|
|
|
|
16.
张飘飘. 含铬耐候钢在模拟海洋大气环境中的腐蚀行为.
中国腐蚀与防护学报,2017,37(2):93-100
|
CSCD被引
13
次
|
|
|
|
|
17.
Le D P. Effect of antimony on the corrosion behavior of low-alloy steel for flue gas desulfurization system.
Corrosion Science,2008,50(4):1195-1204
|
CSCD被引
20
次
|
|
|
|
|
18.
Lin B. A study on the initiation of pitting corrosion in carbon steel in chloride-containing media using scanning electrochemical probes.
Electrochimica Acta,2010,55(22):6542-6545
|
CSCD被引
11
次
|
|
|
|
|
了解气象卫星更多信息，请访问