钨基面对等离子体材料的制备和性能
Fabrication of Tungsten as Plasma Facing Material

种法力 ¹ 陈勇 ² 于福文 ² 陈俊凌 ³ 郑学斌 ⁴

文摘	利用等离子体喷涂技术和弥散增强粉末冶金方法制备钨基面对等离子体材料,并对其基本物理属性进行了分析,包括气孔率及其分布、硬度、抗弯强度、结合强度。同时,利用电子束实验装置对钨基复合材料高热负荷性能进行了研究。研究发现,VPS-W涂层能够承受10MW/m~2、100s的热负荷沉积,涂层开裂、分层是其失效原因;TiC和La_2O_3弥散相增强了钨基复合材料性能,在表面温度控制在1500℃以下可作为面对等离子体材料。
其他语种文摘	Tungsten plasma facing materials (PFM)were fabricated by means of plasma spraying technology and powder metallurgy,respectively.And the main characteristics including porosity and pore size distribution,Vickers hardness,flexural strength,bonding strength between W coating and the substrate,of the tungsten PFM were tested..The performance of the PS-W coating under high heat loading was investigated using the electron beam facility with the water cooling.The results indicate that VPS-W coating can withstanding the heat load of 10MW/m~2 for 100sexhibiting the transfer-heat capability better than the APS-W coating.The failure behavior is due to the macro-cracks and delamination.Both of TiC and La_2O_3particles can effectively improve the heat performance,the suitable PFM at temperature less than 1500℃for the coating surface.
来源	材料科学与工程学报 ,2019,37(6):986-990 【核心库】
DOI	10.14136/j.cnki.issn1673-2812.2019.06.022
关键词	钨基复合材料 ; 面对等离子体材料 ; 热负荷性能
地址	1. 徐州工程学院, 江苏, 徐州, 221000 2. 合肥工业大学材料科学与工程学院, 安徽, 合肥, 230009 3. 中国科学院合肥物质研究院, 安徽, 合肥, 230031 4. 中国科学院上海硅酸盐研究所, 上海, 200050
语种	中文
文献类型	研究性论文
ISSN	1673-2812
学科	一般工业技术
基金	国家自然科学基金资助项目 ; 江苏省教育厅“青蓝工程”资助项目
文献收藏号	CSCD:6698412