冷变形和时效热处理对TB9钛合金组织和性能影响
Influence of Cold Deformation and Aging Heat Treatment on Microstructure and Mechanical Property of TB9 Titanium Alloy

查看参考文献20篇

任德春 1,2   刘玉敬 1   张慧博 1   王健 1   金伟 1 *   杨锐 1  
文摘 利用XRD、OM和SEM等手段研究和分析了冷变形和时效热处理对TB9钛合金组织和性能的影响。结果表明:随变形量的增大,在合金棒材横截面形成旋涡状组织,而沿纵截面形成纤维状组织;合金径向和轴向的显微硬度均随着变形量的增大而增大;合金450 ℃/8 h/AC时效热处理后由α相和β相组成,且随变形量的增大,合金室温抗拉强度增加,塑性降低;同时冷变形过程中引入的位错等缺陷为时效过程中α相的析出提供形核位置,使α相无析出区消失,α相尺寸达到纳米级;合金70%冷变形样品经时效热处理后最高抗拉强度可达1809 MPa,此时还有4%的延伸率,断裂方式为韧性断裂和脆性断裂混合模式。
其他语种文摘 The properties of titanium alloys can be improved by cold deformation and aging heat treatment.However,there are limited reports on the performance transformation of titanium alloys under the combination of cold deformation and aging heat treatment.In this work,the influence of prior cold deformation and the subsequent aging heat treatment on the phase types,α precipitation behaviors and the tensile properties of TB9 titanium alloy were studied by the X-ray diffraction,optical microstructure,scanning electron microscope and uniaxial tensile.The results show that longitudinal and cross section of the bars form different type macro textures through produced different microstructures and affect the microhardness.TB9 titanium alloy is consisted of α and β phases after aging heat treatment.With the increase of the cold deformation rate,the tensile strength is increased and the ductile is reduced.Due to the defects during the cold deformation process,the precipitation free zones disappear in cold deformation samples and the maximum tensile strength reaches 1809 MPa with an elongation of 4%.
来源 稀有金属材料与工程 ,2020,49(3):1083-1089 【核心库】
关键词 TB9钛合金 ; 冷变形 ; 时效热处理 ; 显微组织 ; 力学性能
地址

1. 中国科学院金属研究所, 辽宁, 沈阳, 110016  

2. 中国科学技术大学, 辽宁, 沈阳, 110016

语种 中文
文献类型 研究性论文
ISSN 1002-185X
学科 金属学与金属工艺
文献收藏号 CSCD:6688028

参考文献 共 20 共1页

1.  Leyens C. Titanium and Titanium Alloys,2003:9 CSCD被引 1 次    
2.  Yu K O. Journal of Materials Engineering and Performance,2005,14(6):697 CSCD被引 3 次    
3.  王健. 稀有金属材料与工程,2017,46(S1):129 CSCD被引 3 次    
4.  Xu X. Hot deformation behavior and microstructural evolution of beta C titanium alloy in β phase field. Transactions of Nonferrous Metals Society of China,2016,26(11):2874 CSCD被引 19 次    
5.  Xu T W. Journal of Alloys and Compounds,2016,682:404 CSCD被引 8 次    
6.  罗丽娟. 冷轧及退火工艺对近β钛合金管材组织与力学性能的影响. 稀有金属材料与工程,2006,35(5):787 CSCD被引 5 次    
7.  任德春. 金属学报,2019,45(5):480 CSCD被引 1 次    
8.  Xu Tiewei. Microstructure Evolution during Cold-Deformation and Aging Response after Annealing of TB8 Titanium Alloy. Rare Metal Materials and Engineering,2016,45(3):575 CSCD被引 10 次    
9.  Gupta R K. Journal of Materials Engineering and Performance,2018,27(9):4405 CSCD被引 2 次    
10.  Wan Mingpan. Journal of Alloys and Compounds,2015,619:383 CSCD被引 14 次    
11.  宋振亚. 预变形对TB3合金时效析出行为及其力学性能的影响. 稀有金属材料与工程,2010,39(5):791 CSCD被引 9 次    
12.  陈福文. 冷轧对Ti-55531组织特征及时效行为和力学性能的影响. 稀有金属材料与工程,2015,44(7):1719 CSCD被引 6 次    
13.  黄鎏杰. 中国有色金属学报,2013,23(Z1):S11 CSCD被引 2 次    
14.  李雷. 钛工业进展,2012,29(5):30 CSCD被引 4 次    
15.  Zhang J L. Journal of Materials Science,2015,50:5694 CSCD被引 1 次    
16.  Park N J. Solid State Phenomena,2005,105:213 CSCD被引 1 次    
17.  王雪萌. 时效处理对Ti-3Al-8V-6Cr-4Mo-4Zr合金力学性能的影响. 材料研究学报,2017,31(6):409 CSCD被引 7 次    
18.  Schmidt P. Procedia Engineering,2010,39(2):1973 CSCD被引 1 次    
19.  Schmidt P. Metallurgical and Materials Transactions A,2011,42:26 CSCD被引 1 次    
20.  陈强. 固溶温度对新型亚稳β钛合金组织与性能的影响. 材料热处理学报,2016,37(8):29 CSCD被引 6 次    
引证文献 6 篇

1 王立颖 热机械加工Ti-6Al-4V钛合金的流变行为和显微组织演变 锻压技术,2020,45(12):183-190
CSCD被引 5 次

2 史丽晨 TB9钛合金车削系统振动特性与表面粗糙度关系的试验研究 表面技术,2022,51(6):354-363
CSCD被引 2 次

显示所有6篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护：中国科学院文献情报中心
地址：北京中关村北四环西路33号 邮政编码：100190 联系电话：(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号