超厚板TC4钛合金电子束焊接接头应力腐蚀敏感性
Stress corrosion crack sensitivity of ultra-thick TC4 titanium alloy electron beam welding joints
查看参考文献24篇
|
文摘
|
针对100 mm超厚板TC4钛合金电子束焊接接头,采用慢应变速率拉伸方法评价接头在人造海水中的应力腐蚀敏感性,分析接头的显微组织和断口形貌,对接头的腐蚀机制进行研究.结果表明,室温条件下应变速率为 ε = 1 × 10~(–6) s~(–1)时,母材在海水中未表现出应力腐蚀敏感性;焊缝上部、中部和下部具有轻微应力腐蚀敏感性.焊缝在海水中发生阳极溶解,产生氢吸附,导致裂纹的萌生.同时氢扩散诱导α'相界及α'相内发生位错塞积,进而使裂纹在更低的应力水平下发生扩展. |
|
其他语种文摘
|
Slow strain rate tensile method was adopted to evaluate the stress corrosion crack (SCC)sensitivity of 100 mm ultra-thick TC4 titanium alloy electron beam welded(EBW)joints under artificial seawater. The corrosion mechanism was studied by observing the microstructure and fracture morphology of the joint. The results showed that the base metal have no SCC sensitivity in seawater. However, the upper, middle and lower parts of the weld showed slight SCC sensitivity at room temperature under the condition of strain rate ε = 1 × 10~(–6) s~(–1). In seawater, anodic dissolution accursed in the weld metal, which increased the Ti ion concentration in the solution at the crack tip, then, H atoms are evolved and absorbed at the crack tip. The diffused hydrogen then promotes dislocation emission and increases the dislocation density at the α' phase boundaries and in the α' phase. The crack initiation and propagation are results of the accumulation of highly hydrogen. At the same time, hydrogen enhances mobility of dislocations, then the crack propagates at a lower stress level. |
|
来源
|
焊接学报
,2019,40(12):121-128 【核心库】
|
|
DOI
|
10.12073/j.hjxb.2019400324
|
|
关键词
|
电子束焊接
;
钛合金
;
应力腐蚀
;
显微组织
;
断口形貌
|
|
地址
|
1.
广东省焊接技术研究所(广东省中乌研究院), 广东省现代焊接技术重点实验室, 广州, 510650
2.
中国科学院金属研究所, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0253-360X |
|
学科
|
金属学与金属工艺 |
|
基金
|
广东省广州市项目
;
广东省科技计划项目
;
攀钢集团项目
|
|
文献收藏号
|
CSCD:6658733
|
参考文献 共
24
共2页
|
|
1.
Lutjering G.
Titanium. 2nd ed,2007
|
CSCD被引
19
次
|
|
|
|
|
2.
赵永庆. 我国创新研制的主要船用钛合金及其应用.
中国材料进展,2014,33(7):398-404
|
CSCD被引
28
次
|
|
|
|
|
3.
常辉. 钛材料在海洋工程中的应用.
中国有色金属报,2018
|
CSCD被引
1
次
|
|
|
|
|
4.
赵凤桐. 钛及钛合金在氯碱工业上的应用.
氯碱工业,1991,6:33-42
|
CSCD被引
1
次
|
|
|
|
|
5.
余存烨. 耐蚀钛合金的发展.
钛工业进展,2003,20(1):12-19
|
CSCD被引
8
次
|
|
|
|
|
6.
Atapour M. Corrosion behavior of Ti-8Al-1Mo-1V alloy compared to Ti-6Al-4V.
Material Design,2011,32(3):1692-1696
|
CSCD被引
7
次
|
|
|
|
|
7.
Raja V S.
Stress corrosion cracking,2011:381-408
|
CSCD被引
2
次
|
|
|
|
|
8.
Wanhill R J H. Aqueous stress corrosion in titanium alloys.
British Corrosion Journal,1975,10:69-78
|
CSCD被引
1
次
|
|
|
|
|
9.
李晓延. 大厚度钛合金结构电子束焊接制造基础研究.
焊接学报,2010,31(2):107-112
|
CSCD被引
11
次
|
|
|
|
|
10.
Weglowski M S. Electron beam weldingtechniques and trends-review.
Vacuum,2016,130:72-92
|
CSCD被引
12
次
|
|
|
|
|
11.
石铭霄.
钛合金电子束深熔焊传热传质及质量控制研究,2013
|
CSCD被引
3
次
|
|
|
|
|
12.
侯江涛.
TC4钛合金高能束流焊接焊缝组织研究,2009
|
CSCD被引
2
次
|
|
|
|
|
13.
吴会强. 电子束焊接热输入对Ti-6Al-4V组织结构的影响.
焊接学报,2004,25(5):41-44
|
CSCD被引
7
次
|
|
|
|
|
14.
龚玉兵. 厚板TC4钛合金电子束焊接头组织演变规律.
焊接学报,2017,38(9):91-96
|
CSCD被引
6
次
|
|
|
|
|
15.
安飞鹏. 深潜器用Ti80电子束焊接接头精细组织结构特征.
焊接学报,2017,38(5):96-99
|
CSCD被引
4
次
|
|
|
|
|
16.
旷小聪.
超大厚度TA15钛合金电子束焊接及热处理工艺研究,2017
|
CSCD被引
1
次
|
|
|
|
|
17.
余陈. 焊后热处理对100 mm TC4钛合金电子束焊接头残余应力的影响.
材料热处理学报,2018,39(7):151-155
|
CSCD被引
4
次
|
|
|
|
|
18.
吴冰. 厚板钛合金电子束焊接残余应力分布特征.
焊接学报,2010,31(2):10-12
|
CSCD被引
5
次
|
|
|
|
|
19.
Han W. Effect of Welding Speed on Fatigue Properties of TC18 Thick Plate by Electron Beam Welding.
Rare Metal Materials and Engineering,2018,47(8):2335-2340
|
CSCD被引
6
次
|
|
|
|
|
20.
吴俊升. Q345D低合金钢在海洋潮差区的腐蚀规律及电化学行为研究.
机械工程学报,2016,52(20):30-36
|
CSCD被引
7
次
|
|
|
|
|
了解气象卫星更多信息，请访问