热等静压温度和粉末粒度对Ti_2AlNb合金组织与性能的影响
Effect of Temperature and Powder Particle Size on Mechanical Properties and Microstructure of PM Ti_2AlNb Alloy Prepared via Hot Isostatic Pressing
查看参考文献36篇
|
文摘
|
采用无坩埚感应熔炼超声气体雾化法制备了成分为Ti-22Al-24Nb-0.5Mo(原子分数, %)的预合金粉末,通过预合金粉末热等静压工艺制备了Ti_2AlNb粉末冶金合金。研究结果表明,热等静压温度显著影响Ti_2AlNb粉末冶金合金的显微组织,需严格控制。为了对比研究,选取了平均粒度分别为70 μm和200 μm的两种Ti_2AlNb预合金粉末,制备坯料并测试性能,探讨了粉末粒度的选取原则,分析了粉末粒度对Ti_2AlNb粉末冶金合金显微组织和力学性能的影响。研究结果表明,粉末粒度对合金室温拉伸强度无显著影响,但会对高温拉伸强度和高温持久寿命产生显著影响,由粗粉(平均粒度200 μm)制成的合金高温持久寿命较细粉(平均粒度70 μm)的降低大约40%。 |
|
其他语种文摘
|
Pre-alloyed powder of Ti-22Al-24Nb-0.5Mo (atomic fraction, %) was prepared via a two step process, i.e. electrode no crucible induction melting and then gas atomization process. Powder metallurgy (PM) Ti_2AlNb alloys was prepared through a typical hot isostatic pressing (HIPing) route. Two prealloyed powders with average particle sizes of 70 and 200 μm respectively were prepared and adopted to prepare PM alloys tested for comparison. The results showed that the powder particle size had no significant effect on the tensile strength at room temperature, but a significant effect on the tensile strength and rupture life time at elevated temperature. It showed that the rupture lifetime of PM Ti_2AlNb alloys made of the coarser powders was about 40% less than that of the finer powders. |
|
来源
|
材料研究学报
,2019,33(3):161-169 【核心库】
|
|
DOI
|
10.11901/1005.3093.2018.509
|
|
关键词
|
金属材料
;
热等静压工艺
;
粉末粒度
;
Ti_2AlNb合金
;
力学性能
|
|
地址
|
1.
中国航发四川燃气涡轮研究院, 成都, 610500
2.
中国科学院金属研究所, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-3093 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:6463685
|
参考文献 共
36
共2页
|
|
1.
Banerjee D. A new ordered orthorhombic phase in a Ti3Al-Nb alloy.
Acta Materialia,1988,36(4):871
|
CSCD被引
104
次
|
|
|
|
|
2.
Germann L. Effect of composition on the mechanical properties of newly developed Ti_2AlNb-based titanium aluminide.
Intermetallics,2005,13(9):920
|
CSCD被引
46
次
|
|
|
|
|
3.
Banerjee D. The intermetallic Ti_2AlNb.
Progress in Materials Science,1997,42(1/4):135
|
CSCD被引
43
次
|
|
|
|
|
4.
沈军. Ti_2AlNb基合金微观组织调制及热成形研究进展.
金属学报,2013,49(11):1286
|
CSCD被引
30
次
|
|
|
|
|
5.
王永.
Ti_2AlNb基合金的合金化、热加工及力学性能研究,2012
|
CSCD被引
2
次
|
|
|
|
|
6.
卢正冠. 粉末Ti-22Al-24Nb-0.5Mo合金热变形能力的对比研究.
材料研究学报,2015,29(6):445
|
CSCD被引
4
次
|
|
|
|
|
7.
吴杰. 粉末冶金Ti_2AlNb合金的制备及持久寿命.
材料研究学报,2014,28(5):387
|
CSCD被引
6
次
|
|
|
|
|
8.
Wu J. Microstructure Design and Heat Response of Powder Metallurgy Ti_2AlNb Alloys.
Journal of Materials Science & Technology,2015,31(12):1251
|
CSCD被引
23
次
|
|
|
|
|
9.
Samarov V.
In Titanium powder metallurgy,2015
|
CSCD被引
1
次
|
|
|
|
|
10.
杨锐. 钛铝金属间化合物的进展与挑战.
金属学报,2015,51(2):129
|
CSCD被引
84
次
|
|
|
|
|
11.
Xu L. Effect of powder pre-treatment on the mechanical properties of powder metallurgy Ti-47Al-2Cr-2Nb-0.15B.
Gamma Titanium Aluminide Alloys 2014: A Collection of Research on Innovation and Commercialization of Gamma Alloy Technology,2014
|
CSCD被引
1
次
|
|
|
|
|
12.
吴杰. 热等静压粉末Ti_2AlNb合金的制备及电子束焊.
稀有金属材料与工程,2017,46(S1):241
|
CSCD被引
4
次
|
|
|
|
|
13.
Wegmann G. Temperature induced porosity in hot isostatically pressed gamma titanium aluminide alloy powders.
Acta Materialia,2003,51(3):741
|
CSCD被引
34
次
|
|
|
|
|
14.
Eylon D. Thermally induced porosity in Ti-6Al-4V prealloyed powder compacts.
Metallurgical Transactions A,1985,16(8):1526
|
CSCD被引
3
次
|
|
|
|
|
15.
Xu L. Effect of Hot Isostatic Pressing Conditions and Cooling Rate on Microstructure and Properties of Ti-6Al-4V Alloy from Atomized Powder.
Journal of Materials Science & Technology,2014,30(12):1289
|
CSCD被引
31
次
|
|
|
|
|
16.
程文祥.
Ti-5Al-2.5Sn ELI预合金粉末热等静压致密化行为与有限元模拟研究,2013
|
CSCD被引
7
次
|
|
|
|
|
17.
Wu J. Effect of Hot Isostatic Pressing Loading Route on Microstructure and Mechanical Properties of Powder Metallurgy Ti_2AlNb Alloys.
Journal of Materials Science & Technology,2017,33(2):172
|
CSCD被引
27
次
|
|
|
|
|
18.
Lu Z G. Hot Deformation Mechanism and Ring Rolling Behavior of Powder Metallurgy Ti_2AlNb Intermetallics.
Acta Metallurgica Sinica (English Letters),2017,30(7):621
|
CSCD被引
10
次
|
|
|
|
|
19.
Boehlert C J. Part I. The microstructural evolution in Ti-Al-Nb O + Bcc orthorhombic alloys.
Metallurgical & Materials Transactions A,1999,30(9):2305
|
CSCD被引
58
次
|
|
|
|
|
20.
Boehlert C J. Part II. The creep behavior of Ti-Al-Nb O+bcc orthorhombic alloys.
Metallurgical & Materials Transactions A,1999,30(9):2349
|
CSCD被引
18
次
|
|
|
|
|
了解气象卫星更多信息，请访问