Y、Gd、La和Ce对Zr(-Ti)-Cu-Ni-Al非晶形成能力和力学性能的影响
Effect of Y, Gd, La and Ce on the Glass Forming Ability and Mechanical Properties of Zr(-Ti)-Cu-Ni-Al Metallic Glasses
查看参考文献23篇
|
文摘
|
为了控制Zr(-Ti)-Cu-Ni-Al非晶合金中的O含量,进而改善其玻璃形成能力和力学性能,本研究基于稀土元素与O的强相互作用,向合金中添加Y、Gd、La和Ce等元素。使用铜模浇铸制备非晶合金,利用DSC、XRD和TEM对其非晶形成能力和微观结构进行分析,通过压缩试验和SEM对其力学性能及断裂方式进行表征。结果表明:Y的添加对合金的非晶形成能力具有较大的提升,在相对较低真空的气氛下,可制备出直径10 mm以上的块体非晶,抗压缩断裂强度达1950 MPa。 |
|
其他语种文摘
|
Y, Gd, La and Ce were added into Zr(-Ti)-Cu-Ni-Al metallic glasses based on the mechanism of strong interaction between O and rare earth elements in order to control the O content and further to improve the glass forming ability and mechanical properties of the alloys. Metallic glasses were prepared by a copper mold casting method. The glass forming ability and microstructure of the alloys were studied by differential scanning calorimetry (DSC), X-ray Diffraction (XRD) and transmission electron microscopy (TEM), and the mechanical properties and corresponding fracture modes were investigated by quasi-static compressive tests and scanning electron microscope (SEM). The results show that the addition of Y improves the glass forming ability greatly. Bulk metallic glasses with the diameter over 10 mm can be prepared under relatively low vacuum. The compressive strength is up to 1950 MPa. |
|
来源
|
稀有金属材料与工程
,2018,47(9):2755-2760 【核心库】
|
|
关键词
|
非晶
;
玻璃形成能力
;
力学性能
;
Y
|
|
地址
|
1.
中国科学院金属研究所, 沈阳材料科学国家(联合)实验室, 辽宁, 沈阳, 110016
2.
东莞宜安科技股份有限公司, 广东, 东莞, 523662
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-185X |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
广东省省级科技计划项目
;
中国载人空间站工程
;
江苏省创新人才计划项目
|
|
文献收藏号
|
CSCD:6337276
|
参考文献 共
23
共2页
|
|
1.
Qiao J W.
Materials Science & Engineering R-Reports,2016,100:1
|
CSCD被引
79
次
|
|
|
|
|
2.
Schroers J.
Physics Today,2013,66(2):32
|
CSCD被引
20
次
|
|
|
|
|
3.
Johnson W L.
US Patent, US5288344-A,1994
|
CSCD被引
1
次
|
|
|
|
|
4.
Peker A.
Applied Physics Letters,1993,63(17):2342
|
CSCD被引
290
次
|
|
|
|
|
5.
Inoue A.
Materials Transactions Jim,1996,37(2):185
|
CSCD被引
63
次
|
|
|
|
|
6.
Yokoyama Y.
Materials Transactions,2007,48(12):3190
|
CSCD被引
6
次
|
|
|
|
|
7.
Wang W H.
Progress in Materials Science,2007,52(4):540
|
CSCD被引
117
次
|
|
|
|
|
8.
Kui H W.
Applied Physics Letters,1984,45(6):615
|
CSCD被引
41
次
|
|
|
|
|
9.
Qiao D C.
Intermetallics,2012,24:115
|
CSCD被引
1
次
|
|
|
|
|
10.
Jiang F.
Scripta Materialia,2005,53(5):487
|
CSCD被引
5
次
|
|
|
|
|
11.
Ma D.
Applied Physics Letters,2005,87(17):171914
|
CSCD被引
9
次
|
|
|
|
|
12.
Zhao D Q.
Materials Transactions Jim,2000,41(11):1427
|
CSCD被引
4
次
|
|
|
|
|
13.
Heinrich J.
Applied Physics Letters,2012,100(7):071909
|
CSCD被引
1
次
|
|
|
|
|
14.
Luo J.
Materials Transactions,2006,47(2):450
|
CSCD被引
7
次
|
|
|
|
|
15.
Yan M.
Journal of Non-Crystalline Solids,2006,352(28/29):3109
|
CSCD被引
7
次
|
|
|
|
|
16.
Yan M.
Acta Materialia,2006,54(13):3627
|
CSCD被引
7
次
|
|
|
|
|
17.
Zhang Y.
Materials Transactions Jim,2000,41(11):1410
|
CSCD被引
18
次
|
|
|
|
|
18.
Hao G J. Role of yttrium in glass formation of Ti-based bulk metallic glasses.
Rare Metals,2009,28(1):68
|
CSCD被引
4
次
|
|
|
|
|
19.
Zhao X.
Philosophical Magazine Letters,2009,89(1):11
|
CSCD被引
1
次
|
|
|
|
|
20.
Xu D H.
Physical Review Letters,2004,92(24):245504
|
CSCD被引
46
次
|
|
|
|
|
了解气象卫星更多信息，请访问