Effect of squeeze casting process on microstructures and flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy
查看参考文献15篇
|
文摘
|
The effects of squeeze casting process on microstructure and flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy were investigated and the hot-compression tests of gravity casting and squeeze casting alloy were carried out at 350-500 ℃ and 0.001-5 s~(-1). The results show that microstructures of Al-17.5Si-4Cu-0.5Mg alloys were obviously improved by squeeze casting. Due to the decrease of coarse primary Si particles, soft a-Al dendrite as well as the fine microstructures appeared, and the mechanical properties of squeeze casting alloys were improved. However, when the strain rate rises or the deformation temperature decreases, the flow stress increases and it was proved that the alloy is a positive strain rate sensitive material. It was deduced that compared with the gravity casting alloy, squeeze casting alloy (solidified at 632 MPa) is more difficult to deform since the flow stress of squeeze casting alloy is higher than that of gravity casting alloy when the deformation temperature exceeds 400 ℃. Flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy can be described by a hyperbolic sine form with Zener-Hollomon parameter, and the average hot deformation activation energy Q of gravity casting alloy and squeeze casting alloy is 278.97 and 308.77 kj/mol, respectively. |
|
来源
|
Journal of Iron and Steel Research
, International,2017,24(9):957-965 【核心库】
|
|
DOI
|
10.1016/s1006-706x(17)30139-5
|
|
关键词
|
Squeeze casting Al-Si-Cu-Mg alloy
;
Hot compression deformation
;
Flow stress
;
Constitutive equation
|
|
地址
|
School of Materials Science and Engineering, Shenyang University of Technology, Liaoning, Shenyang, 110870
|
|
语种
|
英文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1006-706X |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
Shenyang City Application Basic Research Foundation
|
|
文献收藏号
|
CSCD:6077477
|
参考文献 共
15
共1页
|
|
1.
Gupta M.
J. Alloy. Compd,1999,287:284-294
|
CSCD被引
13
次
|
|
|
|
|
2.
Zhang H H. Microstructure and mechanical properties of hypereutectic Al-Si alloy modified with Cu-P.
Rare Metals,2008,27:59-63
|
CSCD被引
28
次
|
|
|
|
|
3.
Rahvard M M.
Mater. Des,2014,56:105-114
|
CSCD被引
2
次
|
|
|
|
|
4.
Shi H.
Mater. Sci. Technol,1997,13:210-216
|
CSCD被引
108
次
|
|
|
|
|
5.
Liu T. Microstructure and Mechanical Properties of Overcast 6101–6101 Wrought Al Alloy Joint by Squeeze Casting.
J. Mater. Sci. Technol,2016,32:298-304
|
CSCD被引
11
次
|
|
|
|
|
6.
Fang L.
China Foundry,2015,12:367-374
|
CSCD被引
1
次
|
|
|
|
|
7.
Huang F. Effects of Strain Rate and Deformation Temperature on Microstructures and Hardness in Plastically Deformed Pure Aluminum.
J. Mater. Sci. Technol,2011,27:1-7
|
CSCD被引
15
次
|
|
|
|
|
8.
Gan C L. Constitutive equations for high temperature flow stress prediction of 6063 Al alloy considering compensation of strain.
Trans. Nonferrous Met. Soc. China,2014,24:3486-3491
|
CSCD被引
16
次
|
|
|
|
|
9.
Zhang D H.
Chinese J. Nonferrous Met., (in Chinese),2000,10:132-134
|
CSCD被引
1
次
|
|
|
|
|
10.
Jiang J F. Compression Mechanical Behaviour of 7075 Aluminium Matrix Composite Reinforced with Nano-sized SiC Particles in Semisolid State.
J. Mater. Sci. Technol,2016,32:1197-1203
|
CSCD被引
1
次
|
|
|
|
|
11.
Jie J C.
Scripta Mater,2011,64:588-591
|
CSCD被引
9
次
|
|
|
|
|
12.
Zhang C Y. Mechanical and fatigue properties of self-piercing riveted joints in high-strength steel and aluminium alloy.
J. Iron Steel Res. Int,2017,24:214-221
|
CSCD被引
9
次
|
|
|
|
|
13.
Dang X L.
J. Central South Univ,2012,43:4234-4241
|
CSCD被引
1
次
|
|
|
|
|
14.
Sheppard T.
Met. Sci,1983,17:481-490
|
CSCD被引
39
次
|
|
|
|
|
15.
Zener C.
J. Appl. Phys,1944,15:22-27
|
CSCD被引
704
次
|
|
|
|
|
了解气象卫星更多信息，请访问