镁合金热辊轧制温升效应研究
Temperature Rise Effect of AZ31B Mg Alloy during Rolling with Heated Rolls
查看参考文献15篇
|
文摘
|
研究了热辊轧制中AZ31B镁合金不同工艺条件下厚度方向温度分布及其与组织的关系,并在此基础上建立了能量守恒的简化方程来预测温升。结果表明:变形过程中各层金属的温升均与压下率正相关,而与初轧温度反相关。辊温显著影响轧制时的表面温降和总体温升,使得热辊轧制表层组织中孪晶明显减小,轧板中再结晶更加充分。此外,基于能量守恒的简化方程的计算结果与实测数据吻合较好。 |
|
其他语种文摘
|
The temperature distribution along the thickness direction of AZ3lB Mg alloy was measured during rolling with heated rolls, based on the previous study of temperature rise effect during rolling with cold (RT) rolls. The effects of different rolling conditions on temperature distribution and its relation with microstructure were investigated. On this basis, simplified energy-based state equations were established to predict temperature rises. The results show that the two temperature rises of metal layers in different thickness both increase with either increased reduction or decreased initial rolling temperature. The roll temperature has obvious effects on surface temperature and overall temperature rise. As a result, the amount of twin in surface layer decreases sharply and the overall recrystallization zone increases during rolling with heated roll, compared with those with cold rolls. The calculated results by energy-based state equations are in good agreement with the experimental ones. |
|
来源
|
稀有金属材料与工程
,2017,46(9):2481-2486 【核心库】
|
|
关键词
|
镁合金
;
变形热
;
轧制
;
温升
;
微观组织
|
|
地址
|
东北大学, 材料电磁过程研究教育部重点实验室, 辽宁, 沈阳, 110819
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-185X |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家973计划
;
辽宁省自然科学基金
;
中央高校基本科研业务费专项资金
|
|
文献收藏号
|
CSCD:6077234
|
参考文献 共
15
共1页
|
|
1.
吴菊英. 均匀化退火对Mg-3Al-1Zn-2.2/5Sr镁合金中第二相的影响.
稀有金属材料与工程,2014,43(7):1638
|
CSCD被引
4
次
|
|
|
|
|
2.
Pereira P H R.
Materials Science and Engineering A,2014,593:185
|
CSCD被引
2
次
|
|
|
|
|
3.
Nishida Y.
Scripta Materialia,2002,46(3):211
|
CSCD被引
1
次
|
|
|
|
|
4.
Yu H.
Journal of Materials Engineering and Performance,2012,21(9):1841
|
CSCD被引
2
次
|
|
|
|
|
5.
张丁非.
中国科技论文在线,2009,4(11):813
|
CSCD被引
5
次
|
|
|
|
|
6.
Valiev R Z.
Progress in Materials Science,2000,45(2):103
|
CSCD被引
506
次
|
|
|
|
|
7.
Galantucci L M.
Journal of Materials Processing Technology,1999,92:494
|
CSCD被引
15
次
|
|
|
|
|
8.
丁云鹏. AZ31B镁合金轧制过程中的温升效应.
稀有金属材料与工程,2017,46(3):722
|
CSCD被引
6
次
|
|
|
|
|
9.
Chen W C.
Metallurgical Transactions A,1993,24(6):1307
|
CSCD被引
5
次
|
|
|
|
|
10.
Chen W C.
Ironmaking and Steelmaking,1993,20(2):113
|
CSCD被引
4
次
|
|
|
|
|
11.
刘祖岩.
稀有金属材料与工程,2007,36(S3):304
|
CSCD被引
8
次
|
|
|
|
|
12.
孙朝阳. AZ31镁合金热变形流动应力预测模型.
金属学报,2012,48(7):853
|
CSCD被引
16
次
|
|
|
|
|
13.
Zhang D.
Transactions of Nonferrous Metals Society of China,2011,21(5):1112
|
CSCD被引
1
次
|
|
|
|
|
14.
余琨. 热轧AZ31镁合金板材高温塑性变形行为.
中南大学学报, 自然科学版,2010,41(5):1749
|
CSCD被引
5
次
|
|
|
|
|
15.
Cho J.
Materials Science and Engineering A,2013,566:40
|
CSCD被引
11
次
|
|
|
|
|
了解气象卫星更多信息，请访问