2024铝合金表面无铬硅烷膜的制备与性能研究
Preparation and Performance of Silane Coating on 2024 Aluminum Alloy
查看参考文献17篇
|
文摘
|
采用硅烷A-187为前驱体,制备了一种应用于2024铝合金基体表面的无铬硅烷转化膜。通过扫描电子显微镜(SEM)、能谱(EDS)、表面分析系统(XPS)、中性盐雾实验、动电位极化曲线和电化学阻抗谱对硅烷膜的表面/截面形貌、成分及耐蚀性能进行了表征和分析。结果表明:制备的无铬硅烷水解液处理后的2024铝合金具有优异的耐蚀性能,中性盐雾实验168 h,无腐蚀产物产生,硅烷膜使铝合金的腐蚀电位正移154 mV;硅烷膜下基体腐蚀反应的阻抗值随浸泡时间逐渐升高,说明硅烷膜可以有效抑制基体的腐蚀,为2024铝合金提供良好防护。 |
|
其他语种文摘
|
A novel Cr-free silane film on 2024 aluminum alloy was prepared with the hydrolysate of silane A-187 as precursors. The corrosion resistance, as well as the composition and morphology of the coatings were characterized by means of potentiodynamic measurement, NSS test and AC impedance spectra, as well as by EDS, XPS and SEM respectively. The results showed that the Cr-free silane coating had excellent corrosion resistance and there were no obvious corrosion observed after 168 h salt spray test. The silane coating enables the corrosion potential (Ecorr) increased of the alloy to be shifted positively ca 154 mV, while the resistance of the coating increased gradually with the immersion time. It follows that the silane coating can provide effectively good protection for 2024 aluminum alloy. |
|
来源
|
腐蚀科学与防护技术
,2017,29(2):145-150 【核心库】
|
|
DOI
|
10.11903/1002.6495.2016.111
|
|
关键词
|
2024铝合金
;
硅烷膜
;
水解液
;
耐蚀性
|
|
地址
|
1.
沈阳飞机工业(集团)有限公司, 沈阳, 110850
2.
中国人民解放军驻沈阳飞机工业(集团)有限公司军事代表室, 沈阳, 110034
3.
中国科学院金属研究所金属腐蚀与防护实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-6495 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:5956630
|
参考文献 共
17
共1页
|
|
1.
刘希燕. 铝合金防腐保护研究进展.
现代涂料与涂装,2007,10(12):11
|
CSCD被引
12
次
|
|
|
|
|
2.
胡敏英. 铝合金表面防腐处理技术研究.
铝加工,2010(2):36
|
CSCD被引
4
次
|
|
|
|
|
3.
Yu H C. Improved electrochemical performance of trivalentchrome coating on Al 6063 alloy via urea and thiourea addition.
Electrochim. Acta,2008,54:720
|
CSCD被引
11
次
|
|
|
|
|
4.
胡吉明. 铝合金表面BTSE硅烷化处理研究.
金属学报,2004,40:1189
|
CSCD被引
39
次
|
|
|
|
|
5.
郭增昌. 铝合金表面不同硅烷化预处理的耐蚀性研究.
中国腐蚀与防护学报,2007,27:172
|
CSCD被引
11
次
|
|
|
|
|
6.
李红玲. 金属表面无铬替代处理技术的研究进展.
表面技术,2013,42(2):112
|
CSCD被引
11
次
|
|
|
|
|
7.
汪亮. 铝合金表面新型硅烷膜的制备及表面形貌研究.
电镀与精饰,2012,34(3):13
|
CSCD被引
13
次
|
|
|
|
|
8.
Hamdy A S. Environmentally compliant silica conversion coatings prepared by sol-gel method for aluminum alloys.
Surf. Coat. Technol,2006,201:401
|
CSCD被引
10
次
|
|
|
|
|
9.
Recloux I. Silica mesoporous thin films as containers for benzotriazole for corrosion protection of 2024 aluminium alloys.
Appl. Surf. Sci,2015,346:124
|
CSCD被引
4
次
|
|
|
|
|
10.
徐以兵. 表面活性剂对铝合金表面电化学沉积硅烷膜层的影响.
表面技术,2008,37(3):1
|
CSCD被引
3
次
|
|
|
|
|
11.
陈雷. Si-69应用于2024铝合金表面硅烷化防腐蚀处理的工艺研究.
表面技术,2012,41(1):79
|
CSCD被引
3
次
|
|
|
|
|
12.
Moulder J F.
Handbook of X-ray Photoelectron Spectroscopy,1992
|
CSCD被引
120
次
|
|
|
|
|
13.
李庆鹏. 不同钝化剂对锌铝混合粉的析氢抑制及无铬达克罗性能影响.
腐蚀科学与防护技术,2011,23:121
|
CSCD被引
5
次
|
|
|
|
|
14.
张金涛. LY12铝合金表面硅烷杂化膜的电化学性能研究.
电镀与涂饰,2008,27(9):22
|
CSCD被引
5
次
|
|
|
|
|
15.
张金涛. 2A12铝合金表面铈盐掺杂硅烷杂化膜在3.5%NaCl溶液中耐蚀性能的电化学研究.
金属学报,2008,44:1372
|
CSCD被引
17
次
|
|
|
|
|
16.
曹楚南.
电化学阻抗谱导论,2002:26
|
CSCD被引
47
次
|
|
|
|
|
17.
Liu J G. Electrochemical characteristics of corrosion behavior of organic/Dacromet composite systems pretreated with gamma-aminopropyltriethoxysilane.
Surf. Coat. Technol,2006,200:4976
|
CSCD被引
11
次
|
|
|
|
|
了解气象卫星更多信息，请访问