7B04铝合金在模拟海洋大气环境下的腐蚀行为
Corrosion Behavior of 7B04 Al-alloy in Simulated Marine Atmospheric Environment
查看参考文献22篇
|
文摘
|
海洋大气环境下铝合金的腐蚀本质上是薄液膜下的电化学腐蚀,与本体溶液中的腐蚀有很大不同,腐蚀速率与薄液膜的厚度及成分有关。建立并实验验证了薄液膜厚度、大气相对湿度和铝合金表面盐沉积量3者之间的关系,研究7B04铝合金在不同厚度和不同NaCl浓度薄液膜下的电化学性能。结果表明,薄液膜下7B04铝合金的自然腐蚀电位较本体溶液中更容易达到稳定,且电位更正,自然腐蚀速率更大;液膜厚度减小,7 B04铝合金阴极极化电流密度增加,阳极反应受到抑制;薄液膜中NaCl浓度升高,7 B04铝合金的自然腐蚀电位降低,腐蚀速率上升,而阴阳极极化过程受NaCl浓度变化影响不大,当NaCl质量分数达到5%后,自然腐蚀电位基本不再变化。 |
|
其他语种文摘
|
The corrosion of aluminum alloy in marine atmospheric environment was an essential electrochemical corrosion under thin electrolyte film,which was different from the corrosion in bulk solution,the corrosion rate was related to the thickness and composition of thin electrolyte film. The relationship among film thickness,relative humidity and salt deposit on aluminum alloy surface was established and verified by experiment. The electrochemical properties of 7B04 Al-alloy under thin electrolyte film with different thickness and different NaCl concentration were studied. The results indicate that the free-corrosion potential of 7B04 Al-alloy under thin electrolyte film is easier to reach steady state than that in bulk solution,both free-corrosion potential and corrosion rate are higher under thin electrolyte film. With the decrease of film thickness,the cathodic polarization current density of 7B04 Al-alloy increases,and the anode reaction is suppressed. With the increase of NaCl concentration in thin electrolyte film,the free-corrosion potential of 7B04 Al-alloy decreases,and the corrosion rate increases,but the polarization of the anode and cathode have little effect on the change of NaCl concentration. The free-corrosion potential of 7B04 Al-alloy is no longer changed when the mass fraction of NaCl reaches 5%. |
|
来源
|
航空材料学报
,2017,37(1):59-64 【核心库】
|
|
DOI
|
10.11868/j.issn.1005-5053.2016.000120
|
|
关键词
|
7B04铝合金
;
大气腐蚀
;
薄液膜
;
盐沉积量
;
相对湿度
|
|
地址
|
海军航空工程学院青岛校区, 山东, 青岛, 266041
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-5053 |
|
学科
|
金属学与金属工艺;航空 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:5921614
|
参考文献 共
22
共2页
|
|
1.
陈跃良.
海军飞机结构腐蚀控制及强度评估,2009:1-3
|
CSCD被引
3
次
|
|
|
|
|
2.
黄领才. 沿海环境下服役飞机铝合金零件的表面涂层破坏与腐蚀.
航空学报,2009,30(6):1144-1149
|
CSCD被引
13
次
|
|
|
|
|
3.
李晓刚.
金属大气腐蚀初期行为与机理,2009:239-249
|
CSCD被引
1
次
|
|
|
|
|
4.
林翠. 碳钢在NaCl薄液膜下的电化学腐蚀行为.
腐蚀与防护,2014,35(4):316-320
|
CSCD被引
12
次
|
|
|
|
|
5.
Huang H. The effects of temperature and electric field on atmospheric corrosion behaviour of PCB-Cu under absorbed thin electrolyte layer.
Corrosion Science,2011,53(5):1700-1707
|
CSCD被引
9
次
|
|
|
|
|
6.
Jiang J. Effect of length of gas / liquid /solid three-phase boundary zone on cathodic and corrosion behavior of metals.
Electrochimica Acta,2009,54(5):1426-1435
|
CSCD被引
9
次
|
|
|
|
|
7.
Zhang T. Corrosion of pure magnesium under thin electrolyte layers.
Electrochimica Acta,2008,53(27):7921-7931
|
CSCD被引
20
次
|
|
|
|
|
8.
Cheng Y L. A study of the corrosion of aluminum alloy 2024-T3 under thin electrolyte layers.
Corrosion Science,2004,46(7):1649-1667
|
CSCD被引
47
次
|
|
|
|
|
9.
Zhou H R. Dependence of the corrosion behavior of aluminum alloy 7075 on the thin electrolyte layers.
Materials Science & Engineering B,2009,162(1):1-8
|
CSCD被引
16
次
|
|
|
|
|
10.
周和荣. 7A04铝合金在薄液膜下腐蚀行为.
北京科技大学学报,2008,30(8):880-887
|
CSCD被引
4
次
|
|
|
|
|
11.
李亚坤.
薄液层下金属电化学腐蚀行为研究,2007:19-24
|
CSCD被引
1
次
|
|
|
|
|
12.
张际标. 大气腐蚀起始过程中的微液滴现象研究.
装备环境工程,2005,2(5):14-17
|
CSCD被引
3
次
|
|
|
|
|
13.
王正烈.
物理化学,2001:262-265
|
CSCD被引
2
次
|
|
|
|
|
14.
Frazier J C W.
International critical tables of numerical data,physics,chemistry and technology:Vol. III,1928:292-297
|
CSCD被引
1
次
|
|
|
|
|
15.
王佳. 无机盐微粒沉积和大气腐蚀的发生与发展.
中国腐蚀与防护学报,2004,24(3):155-158
|
CSCD被引
10
次
|
|
|
|
|
16.
Chen Z Y. Calculations of the cathodic current delivery capacity and stability of crevice corrosion under atmospheric environments.
Journal of the Electrochemical Society,2008,155(7):C360-C368
|
CSCD被引
4
次
|
|
|
|
|
17.
Song L. The role of UV illumination on the NaCl-induced atmospheric corrosion of Q235 carbon steel.
Corrosion Science,2014,86(9):318-325
|
CSCD被引
2
次
|
|
|
|
|
18.
Song L. The role of UV illumination on the initial atmospheric corrosion of 09CuPCrNi weathering steel in the presence of NaCl particles.
Corrosion Science,2014,87(1):427-437
|
CSCD被引
2
次
|
|
|
|
|
19.
杨英炎. 基于环境试验的某发动机舰面清洗时机影响分析.
海军航空工程学院学报,2014,29(2):168-172
|
CSCD被引
1
次
|
|
|
|
|
20.
唐晓. NaCl薄液膜下不锈钢腐蚀行为研究.
腐蚀科学与防护技术,2009,21(3):227-229
|
CSCD被引
4
次
|
|
|
|
|
了解气象卫星更多信息，请访问