水性无铬达克罗涂料的制备与性能研究
Preparation and Performance ofWater-based Chromiumfree Dacromet Coating
查看参考文献15篇
|
文摘
|
采用片状锌粉和铝粉为填料,硅烷A-187为成膜物,制备了一种水性无铬达克罗涂料,通过扫描电子显微镜(SEM)、能谱(EDS)、X射线光电子能谱(XPS)、中性盐雾实验、动电位极化曲线和电化学阻抗谱对涂层的表面形貌、成分及耐蚀性能进行了表征和分析。结果表明:制备的水性无铬达克罗涂料具有优异的储存稳定性, 50 ℃/48 h涂料无变化;涂装后的无铬水性涂层表面均匀平整,无明显缺陷,经480 h中性盐雾实验,表面无红锈产生;水性无铬达克罗涂层腐蚀电位负移,腐蚀电流减小了两个数量级,腐蚀电阻增加,涂层具有较好的防护性能。 |
|
其他语种文摘
|
A water-based chromium-free Dacromet coating was prepared with powders of Zn and Al as filler and silane A-187 as film forming material. The coatings were characterized by means of SEM with EDS and XRD, while their corrosion performance was investigated by using potentiodynamic measurement, NSS test and AC impedance spectra. The results showed that the water-based chromium-free Dacromet paint had excellent stability with no obvious change even after storage at 50 ℃ for 48 h; the surface of the applied coatings was smooth and compact without defects, while no tarnish spots could be observed after 480 h salt spray test. The E_(corr) of the water-based chromiumfree Dacromet coating shifts positively while its I_(corr) is two magnitudes lower in comparison to those of the bare substrate which indicated that the water-based chromium-free Dacromet coating had excellent corrosion resistance. |
|
来源
|
中国腐蚀与防护学报
,2016,36(6):559-565 【核心库】
|
|
DOI
|
10.11902/1005.4537.2016.124
|
|
关键词
|
锌粉
;
铝粉
;
稳定性
;
水性无铬
;
达克罗涂料
|
|
地址
|
1.
东北大学材料与冶金学院, 沈阳, 110142
2.
中国科学院金属研究所金属腐蚀与防护实验室, 沈阳, 110016
3.
沈阳市航达科技有限责任公司, 沈阳, 110043
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-4537 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:5893254
|
参考文献 共
15
共1页
|
|
1.
宋积文. 无铬锌铝涂层发展现状.
腐蚀与防护,2007,28(8):411
|
CSCD被引
19
次
|
|
|
|
|
2.
王典. 钛添加剂对无铬达克罗防护性能的影响.
腐蚀科学与防护技术,2009,21(4):427
|
CSCD被引
2
次
|
|
|
|
|
3.
王典. 不同添加剂对锌粉的析氢抑制及无铬达克罗稳定性的影响.
腐蚀科学与防护技术,2009,21(2):176
|
CSCD被引
6
次
|
|
|
|
|
4.
李庆鹏. 不同钝化剂对锌铝混合粉的析氢抑制及无铬达克罗性能影响.
腐蚀科学与防护技术,2011,23(2):121
|
CSCD被引
5
次
|
|
|
|
|
5.
蒋育. 片状Al-Zn-Si合金粉的析氢行为与抑制剂研究.
中国腐蚀与防护学报,2013,33(1):61
|
CSCD被引
2
次
|
|
|
|
|
6.
邵红红. 无铬达克罗涂层的制备及其耐蚀性能.
材料保护,2014,47(11):43
|
CSCD被引
6
次
|
|
|
|
|
7.
朱俊谋. 无铬纳米锌铝涂层的微观组织及腐蚀性能.
中国腐蚀与防护学报,2013,33(5):425
|
CSCD被引
6
次
|
|
|
|
|
8.
Hu H L. Corrosion behavior of chromiumfree dacromet coating in seawater.
J. Alloy. Compd,2009,472(1/2):219
|
CSCD被引
18
次
|
|
|
|
|
9.
Liu J G. EIS study of corrosion behaviour of organic coating/dacromet composite systems.
Electrochim. Acta,2005,50:3320
|
CSCD被引
23
次
|
|
|
|
|
10.
鲁俊. 无铬达克罗涂料工艺及耐蚀性能研究.
应用化工,2011,40(4):612
|
CSCD被引
8
次
|
|
|
|
|
11.
郭增昌. 铝合金表面不同硅烷化预处理的耐蚀性研究.
中国腐蚀与防护学报,2007,27(3):172
|
CSCD被引
11
次
|
|
|
|
|
12.
Moulder J F.
Handbook of X-ray Photo-electron Spectroscopy. 2nd Ed,1992
|
CSCD被引
1
次
|
|
|
|
|
13.
Mansfeild F. Recording and analysis of AC impedance data for corrosion studies II. Experimental approach and results.
Corrosion,1982,38(11):570
|
CSCD被引
8
次
|
|
|
|
|
14.
Liu J G. Electrochemical characteristics of corrosion behavior of organic/dacromet composite systems pretreated with gamma-aminopropyltriethoxysilane.
Surf. Coat. Technol,2006,200:4967
|
CSCD被引
5
次
|
|
|
|
|
15.
曹楚南.
电化学阻抗谱导论,2002
|
CSCD被引
367
次
|
|
|
|
|
了解气象卫星更多信息，请访问