有机膦酸锈转化剂的腐蚀保护机制研究
Study on Corrosion Protection Mechanism of Organic Phosphonic Acid Rust Converter
查看参考文献13篇
|
文摘
|
制备了一种以羟基乙叉二膦酸(HEDP)作为锈转化剂的转化型带锈涂料,通过对添加不同质量分数的HEDP的涂料样板的盐雾试验、电化学测试及分析,研究了HEDP作为锈转化剂的带锈涂料的耐腐蚀性能。综合评定HEDP质量分数为5%时,防腐蚀效果最好。利用能谱(EDS)分析和红外光谱(FT-IR)技术,对HEDP的防锈机理和与铁锈的反应情况进行了研究。EDS线扫描结果表明:当HEDP加入到水性涂料中时,磷元素集中在锈层和涂层的交界处;红外测试结果表明:HEDP主要与铁锈中疏松的纤铁矿反应生成螯合物,形成稳定的络合物保护膜,对基底进行保护。 |
|
其他语种文摘
|
A rust-converting coating was prepared using 1-Hydroxyethylidene-1,1-diphosphonic acid (HEDP) as rust converter. The influence of HEDP on the anticorrosive performance of coatings was studied via salt spray tests,electrochemical impedance spectroscopy (EIS) tests and analysis. When the mass fraction of HEDP in the coating was 5%, the best anticorrosive effect was obtained. The reaction of HEDP with rust was studied through EDS and FT-IR. The results of EDS showed that the phosphorus was concentrated in the boundary between the rust and the coating when HEDP was added into the coating. The FT-IR showed thai HEDP was mainly reacted with the loosened lepidocrocite of rust to produce a chelated compound,which further formed a stable protective layer on the steel substrate. |
|
来源
|
涂料工业
,2016,46(12):1-6,15 【扩展库】
|
|
关键词
|
带锈涂料
;
羟基乙叉二膦酸
;
锈转化剂
;
防腐蚀
;
电化学阻抗谱
|
|
地址
|
1.
中国科学院金属研究所, 中国科学院核用材料与安全评价重点实验室, 沈阳, 110026
2.
中国电器科学研究院有限公司, 工业产品环境适应性国家重点实验室, 广州, 510663
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0253-4312 |
|
学科
|
化学工业 |
|
基金
|
国家电网公司科技项目
;
广东省中国电器院风电装备腐蚀控制关键技术院士工作站项目
|
|
文献收藏号
|
CSCD:5864861
|
参考文献 共
13
共1页
|
|
1.
Ocampo L M. Performance of rust converter based in phosphoric and tannic acids.
Corrosion Science,2004,46(6):1515-1525
|
CSCD被引
11
次
|
|
|
|
|
2.
Singh D. Role of tannic acid based rust converter on formation of passive film on zinc rich coating exposed in simulated concrete pore solution.
Surface & Coatings Technology,2008,202(8):1526-1542
|
CSCD被引
13
次
|
|
|
|
|
3.
Rahim A A. Inhibitive action of mangrove tannins and phosphoric acid on pre-rus-ted steel via electrochemical methods.
Corrosion Science,2008,50(6):1546-1550
|
CSCD被引
13
次
|
|
|
|
|
4.
张洪生. 无毒植酸在金属防护中的应用.
电镀与精饰,2000,22(1):1-4
|
CSCD被引
9
次
|
|
|
|
|
5.
Collazo A. EIS study of the rust converter effectiveness under different conditions.
Electrochimica Acta,2008,53(25):7565-7574
|
CSCD被引
22
次
|
|
|
|
|
6.
Barrero C A. Possible improvements in the action of some rust convters.
Corrosion Science,2001,43(6):1003-1018
|
CSCD被引
7
次
|
|
|
|
|
7.
Boulahlib-Bendaoud Y. Use of the HEDP for the inhibition of the tartar of ground waters.
Energy Procedia,2012,18:1501-1510
|
CSCD被引
1
次
|
|
|
|
|
8.
蒋守红. 有机膦酸对碳钢缓蚀性能及机理研究.
山东化工,2013,42(12):9-11
|
CSCD被引
3
次
|
|
|
|
|
9.
黄金营. HEDP在中央空调酸洗中除锈效果的研究.
工业水处理,2003,23(3):43-45
|
CSCD被引
2
次
|
|
|
|
|
10.
Maege I. Self-assembling adhesion promoters for corrosion resistant metal polymer in-terfaces.
Progress in Organic Coatings,1998,34(1):1-12
|
CSCD被引
8
次
|
|
|
|
|
11.
Salasi M. The electrochemical behaviour of environment-friendly inhibitors of silicate and phosphonate in corrosion control of carbon steel in soft water media.
Materials Chemistry and Physics,2007,104(1):183-190
|
CSCD被引
6
次
|
|
|
|
|
12.
赵晓洋. 有机膦酸溶解铁垢的理论研究.
计算机与应用化学,2014,31(7):821-824
|
CSCD被引
1
次
|
|
|
|
|
13.
解庆范. 镍与HEDP配位化合物的制备及红外光谱表征.
泉州师范学院学报(自然科学),2000,18(6):28-31
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问