Effect of extrusion on corrosion behavior and corrosion mechanism of Mg-Y alloy
查看参考文献20篇
|
文摘
|
The influences of the hot extrusion process on the microstructure, corrosion behavior and corrosion mechanism for Mg-Y magnesium alloy were studied by means of the microstructure observation, weight loss test, electrochemical test and corrosion morphology test. The results showed that with increasing of the extrusion ratio, the shear flow line on the vertical section of the extruded alloy increased, the shear bands parallel lines became more clearly visible, and a large number of fine equiaxed grains distributed in parallel with the flow lines. The open circuit potential had a certain degree of improvement after extrusion, the open circuit potential increased with increment of extrusion ratio, and the corrosion potential of the vertical section was higher than that of the same alloy in the same compression ratio. The shift rate of the corrosion potential relatively became larger with increasing of the extrusion ratio, and the cathode corrosion current corresponding to the branch migration shifted to the positive direction. The high frequency capacitive arc increased with increment of the extrusion ratio, and the radius of capacitive arc of the vertical section was slightly larger than that of the transverse section. The corrosion morphologies of Mg-0.25Y alloy were uniform corrosion, and the corrosion morphologies of Mg-(2.5, 5, 8 and 15) were the pitting corrosion and the small range, deep depth localized corrosion. |
|
来源
|
Journal of Rare Earths
,2016,34(3):315-327 【核心库】
|
|
DOI
|
10.1016/S1002-0721(16)60031-5
|
|
关键词
|
extrusion
;
Mg-Y alloy
;
corrosion behavior
;
corrosion mechanism
;
rare earths
|
|
地址
|
1.
School of Materials Science and Engineering, North University of China, Taiyuan, 030051
2.
Institute of Thermal Power Generation Technology, China Datang Coporation Science and Technology Research Institute, State Key Lab for Fabrication & Processing of Non-ferrous Metals, Beijing, 102206
3.
General Research Institute for Non-ferrous Metals, State Key Lab for Fabrication & Processing of Non-ferrous Metals, Beijing, 100088
4.
Shenyang Area Military Representative Office of Armored Military Representative Office, Chinese PLA General Armament Department, Shenyang, 110016
|
|
语种
|
英文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-0721 |
|
学科
|
冶金工业 |
|
基金
|
supported by the National Key Technology R&D Program of China
|
|
文献收藏号
|
CSCD:5655253
|
参考文献 共
20
共1页
|
|
1.
Loose W S. Magnesium and magnesium alloy, 1st ed.
Corrosion Handbook,1967:218
|
CSCD被引
1
次
|
|
|
|
|
2.
Nordlien J H. A TEM investigation of naturally formed oxide films on pure magnesium.
Corros. Sci,1997,39:1397
|
CSCD被引
29
次
|
|
|
|
|
3.
Song G L. Corrosion behavior of AZ21, AZ501 and AZ91 in sodium chloride.
Corros. Sci,1998,40(10):1769
|
CSCD被引
167
次
|
|
|
|
|
4.
Ben-Haroush M. The relation between microstructure and corrosion behavior of AZ80 Mg alloy following different extrusion temperatures.
Corros. Sci,2008,50:1766
|
CSCD被引
25
次
|
|
|
|
|
5.
Jeong Y S. Enhancement of mechanical properties and corrosion resistance of Mg-Ca alloys through microstructural refinement by indirect extrusion.
Corros. Sci,2014,82:392
|
CSCD被引
46
次
|
|
|
|
|
6.
Abuleil T. Microstructure and corrosion behavior of Mg-Sn-Ca alloys after extrusion.
Trans. Nonferrous Met. Soc. China,2009,19:40
|
CSCD被引
14
次
|
|
|
|
|
7.
Mathieu S. A corrosion study of the main constituent phases of AZ91 magnesium alloys.
Corros. Sci,2003,45:2741
|
CSCD被引
66
次
|
|
|
|
|
8.
Song G L. Corrosion resistance of aged die cast magnesium alloy AZ91D.
Mater. Sci. Eng., A,2004,366:74
|
CSCD被引
92
次
|
|
|
|
|
9.
Zhou Y L. Microstructures, mechanical and corrosion properties and biocompatibility of as extruded Mg-Mn-Zn-Nd alloys for biomedical applications.
Mater. Sci. Eng., C,2015,49(1):93
|
CSCD被引
13
次
|
|
|
|
|
10.
Peng Q M. Effect of yttrium addition on lattice parameter, Young's modulus and vacancy of magnesium.
Mater. Sci. Eng., A,2011,528(4/5):2106
|
CSCD被引
12
次
|
|
|
|
|
11.
Zhang X. Effect of solid-solution treatment on corrosion and electrochemical behaviors of Mg-15Y alloy in 3.5 wt.% NaCl solution.
J. Rare Earths,2012,30(11):1158
|
CSCD被引
5
次
|
|
|
|
|
12.
Zhang G D. Homogenization heat treatment of Mg-7.68Gd-4.88Y-1.32Nd-0.63Al-0.05Zr alloy.
J. Rare Earths,2014,32(5):445
|
CSCD被引
10
次
|
|
|
|
|
13.
Liu Y.
Transient plasticity and microstructural evolution of a commercial AZ31 magnesium alloy at elevated temperatures,2003:111
|
CSCD被引
1
次
|
|
|
|
|
14.
Zhang Q L. Influence of thermal tensile deformation on microstructure of AZ31B magnesium alloy thin sheet.
J. Plast. Eng,2008,15(4):167
|
CSCD被引
1
次
|
|
|
|
|
15.
Zhang X. Corrosion behavior of Mg-Y alloy in NaCl aqueous solution.
Prog. Nat. Sci.-Mater. Int,2012,22(2):169
|
CSCD被引
15
次
|
|
|
|
|
16.
Zhang X.
Study on Microstructure, Properties and Corrosion Behavior of Mg-Y Binary Magnesium Alloys,2013:7
|
CSCD被引
1
次
|
|
|
|
|
17.
Zhang F. Improving in-vitro biocorrosion resistance of Mg-Zn-Mn-Ca alloy in Hank’s solution through addition of cerium.
J. Rare Earths,2015,33(1):93
|
CSCD被引
7
次
|
|
|
|
|
18.
Aung N. Effect of grain size and twins on corrosion behaviour of AZ31B magnesium alloy.
Corros. Sci,2010,52:589
|
CSCD被引
101
次
|
|
|
|
|
19.
Song G. The surface, microstructure and corrosion of magnesium alloy AZ31 sheet.
Electrochim. Acta,2010,55:4148
|
CSCD被引
36
次
|
|
|
|
|
20.
Song G. Galvanic corrosion of magnesium alloy AZ91D in contact with an aluminum alloy steel and zinc.
Corros. Sci,2004,46:955
|
CSCD被引
70
次
|
|
|
|
|
了解气象卫星更多信息，请访问