基于均匀设计优化制备癸酸-棕榈酸/SiO_2复合相变材料
Optimized Preparation of Decanoic-palmitic Acid/Si〇_2 Composite Phase Change Materials Based on Uniform Design
查看参考文献22篇
|
文摘
|
以SiO_2作为载体材料,癸酸-棕榈酸作为相变材料制备癸酸-棕榈酸/SiO_2复合相变材料。基于均匀设计和多元非线性回归法研究了各因素对复合相变材料吸放湿性能和控温性能的影响。结果表明,各因素对性能影响的主次顺序为:溶液pH值>无水乙醇与正硅酸乙酯的物质的量比>癸酸-棕榈酸与正硅酸乙酯的物质的量比>去离子水与正硅酸乙酯的物质的量比>超声波功率;优化制备方案:溶液pH值为3.62,超声波功率为100W,去离子水与正硅酸乙酯的物质的量比为9.67,无水乙醇与正硅酸乙酯的物质的量比为5.21,癸酸-棕榈酸与正硅酸乙酯的物质的量比为0.52。 |
|
其他语种文摘
|
Decanoic-palmitic acid/SiO_2 composite phase change materials were prepared with SiO_2 as carrier material and decanoic-palmitic acid as phase change material. The effect of every factor on moisture absorbing and desorbing performance and temperature control performance of composite phase change materials was studied by uniform design and multivariate nonlinear regression. The results show that primary and secondary sequence of factors affecting performance is solution pH value >mole ratio between absolute alcohol and tetraethyl orthosilicate>mole ratio between decanoic-palmitic acid and tetraethyl orthosilicate>mole ratio between deionized water and tetraethyl orthosilicate >ultrasonic wave power. The optimized preparation plan is solution pH value 3.62,ultrasonic wave power 100W,mole ratio between deionized water and tetraethyl orthosilicate 9.67,mole ratio between absolute alcohol and tetraethyl orthosilicate 5.21,mole ratio between decanoic-palmitic acid and tetraethyl orthosilicate 0.52. |
|
来源
|
材料工程
,2015,43(9):94-102 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2015.09.015
|
|
关键词
|
癸酸-棕榈酸
;
SiO_2
;
复合相变材料
;
吸放湿性能
;
控温性能
;
优化制备
|
|
地址
|
西安建筑科技大学材料与矿资学院, 西安, 710055
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
建筑科学 |
|
基金
|
国家自然科学基金资助项目
;
陕西省科技统筹创新工程计划项目
;
陕西省重点科技创新团队项目
|
|
文献收藏号
|
CSCD:5529216
|
参考文献 共
22
共2页
|
|
1.
Sharma A. Review on thermal energy storage with phase change materials and applications.
Renewable and Sustainable Energy Reviews,2009,13(2):318-345
|
CSCD被引
302
次
|
|
|
|
|
2.
Baker J. New technology and possible advances in energy storage.
Energy Policy,2008,36(12):4368-4373
|
CSCD被引
22
次
|
|
|
|
|
3.
Pacheco R. Energy efficient design of building: a review.
Renewable and Sustainable Energy Reviews,2012,16(6):3559-3573
|
CSCD被引
19
次
|
|
|
|
|
4.
He F. New approach for sol-gel synthesis of microencapsulated n-octadecane phase change material with silica wall using sodium silicate precursor.
Energy,2014,67:223-233
|
CSCD被引
31
次
|
|
|
|
|
5.
Li B X. Fabrication and properties of microencapsulated paraffin @ SiO_2 phase change composite for thermal energy storage.
Acs Sustainable Chemistry & Energy,2013,1(3):374-380
|
CSCD被引
50
次
|
|
|
|
|
6.
Fang G Y. Synthesis and properties of microencapsulated paraffin composites with SiO_2 shell as thermal energy storage materials.
Chemical Engineering Journal,2010,163(1/2):154-159
|
CSCD被引
37
次
|
|
|
|
|
7.
Wang L Y. Preparation of silica microspheres encapsulating phase-change material by sol-gel method in O/W emulsion.
Journal of Microencapsulation,2006,23(1):3-14
|
CSCD被引
16
次
|
|
|
|
|
8.
张鸿. 月桂酸/十六醇/二氧化硅复合相变材料的结构与性能.
材料科学与工程学报,2010,28(5):672-674
|
CSCD被引
24
次
|
|
|
|
|
9.
付路军. 二元脂肪酸/SiO_2复合相变储能材料的制备与表征.
功能材料,2013,44(4):1-4
|
CSCD被引
20
次
|
|
|
|
|
10.
孟多. 脂肪酸/无机纳米颗粒基定形相变材料的制备与热性能.
建筑材料学报,2013,16(1):91-96
|
CSCD被引
21
次
|
|
|
|
|
11.
尚建丽. PAR/POL/SOD复合微胶囊的制备及热湿性能研究.
功能材料,2013,44(8):1141-1144
|
CSCD被引
17
次
|
|
|
|
|
12.
尚建丽. 微胶囊相变储能石膏基建筑材料制备及性能研究.
太阳能学报,2012,33(12):2140-2144
|
CSCD被引
27
次
|
|
|
|
|
13.
张浩. Ce-TiO_2光催化涂料降解甲醛溶液的性能研究及预测模型.
稀土,2014,35(4):18-24
|
CSCD被引
12
次
|
|
|
|
|
14.
张浩. Ce掺杂TiO2催化剂的光催化性能.
过程工程学报,2011,11(3):514-518
|
CSCD被引
24
次
|
|
|
|
|
15.
李魁山. 建筑材料等温吸放湿曲线性能实验研究.
建筑材料学报,2009,12(1):81-84
|
CSCD被引
31
次
|
|
|
|
|
16.
黄子硕. 建筑调湿材料吸放湿速度变化规律.
同济大学学报:自然科学版,2014,42(2):310-314
|
CSCD被引
21
次
|
|
|
|
|
17.
于永生. 十六醇/十六酸/十二酸三元复合相变体系研究.
建筑材料学报,2013,12(1):97-101
|
CSCD被引
16
次
|
|
|
|
|
18.
王岩.
试验设计与MATLAB数据分析,2012
|
CSCD被引
30
次
|
|
|
|
|
19.
谢素超. 薄壁结构吸能预测的多元非线性回归分析.
应用基础与工程科学学报,2010,18(4):714-721
|
CSCD被引
11
次
|
|
|
|
|
20.
周晓华. 环保型多重掺杂X7R瓷料的多元非线性回归分析.
无机材料学报,2006,21(3):683-688
|
CSCD被引
8
次
|
|
|
|
|
了解气象卫星更多信息，请访问