Zn在模拟酸雨大气环境中的腐蚀行为
Corrosion behavior of Zn in simulated acid rain atmospheric environment
查看参考文献36篇
|
文摘
|
利用自制的降雨喷淋装置模拟Zn在酸雨条件下的大气腐蚀行为,采用扫描电镜(SEM)、X射线能谱(EDS)、X射线衍射(XRD)和电化学测试技术分别研究Zn腐蚀48、96、144、192和240 h后的腐蚀产物成分、锈层截面形貌以及表面锈层的电化学特性,分析了锈层对Zn腐蚀行为的影响。结果表明:主要的腐蚀产物为Zn(OH)_2、ZnSO_4、Zn_4SO_4(OH)_6·3H_2O和Zn_5(OH)_8Cl_2·H_2O;腐蚀过程中,Zn的表面形成了具有较好保护性的锈层,随着腐蚀时间的延长,锈层对Zn的保护作用先增强后减弱。 |
|
其他语种文摘
|
The corrosion behavior of Zn in simulated acid rain atmospheric environment was studied with a simulating raining system self-designed, which can control rainfall and pressure close to the actual level. After zinc corroded in simulated acid rain atmospheric environment corrosion time of 48, 96, 144, 192 and 240 h, the morphologies and the composition of corrosion products, cross section of rust layers and the electrochemical characters of rust layers were investigated by scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), X-ray diffractometry (XRD) and electrochemical techniques. The results show that the corrosion products formed on the surface of zinc have good protection, but the degree of protection is limited, with the main product components for Zn(OH)_2, ZnSO_4, Zn_4SO_4(OH)_6·3H_2O and Zn_5(OH)_8Cl_2·H_2O. The protective effect of the rust layers is first enhanced, and then weakened as increasing the corrosion time. |
|
来源
|
中国有色金属学报
,2015,25(2):375-383 【核心库】
|
|
关键词
|
模拟酸雨
;
大气腐蚀
;
腐蚀产物
;
电化学技术
|
|
地址
|
1.
中国科学院金属研究所, 沈阳, 110016
2.
广东电网公司电力科学研究院, 广州, 510080
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1004-0609 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国防技术资助项目
;
南网科技项目
|
|
文献收藏号
|
CSCD:5379465
|
参考文献 共
36
共2页
|
|
1.
许新辉. 中国南方酸雨的分布特征及其成因分析.
四川环境,2011,30(4):135-139
|
CSCD被引
10
次
|
|
|
|
|
2.
张学元. 中国的酸雨对材料腐蚀的经济损失估算.
中国腐蚀与防护学报,2002,22(5):316-319
|
CSCD被引
19
次
|
|
|
|
|
3.
Ei-Mahdy G A. Advanced laboratory study on the atmospheric corrosion of zinc under thin electrolyte layers.
Corrosion,2003,59(6):505-510
|
CSCD被引
6
次
|
|
|
|
|
4.
Azmat N S. Corrosion of Zn under fine size aerosols and droplets using inkjet printer deposition and optical profilometry quantification.
Corrosion Science,2011,53(11):1604-1615
|
CSCD被引
28
次
|
|
|
|
|
5.
Thomas S. Corrosion of zinc as a function of pH.
Corrosion,2012,68(1):015009-1-015009-9
|
CSCD被引
8
次
|
|
|
|
|
6.
原徐杰. 镀锌层破损输电杆塔用镀锌钢在干湿交替作用下的腐蚀行为.
腐蚀科学与防护技术,2013,33(5):395-399
|
CSCD被引
1
次
|
|
|
|
|
7.
宋卓. 环境对电网材料的腐蚀影响分析及评价.
山西电力,2008,149(5):7-9
|
CSCD被引
5
次
|
|
|
|
|
8.
默增禄. 输电线路杆塔的腐蚀与防治对策.
电力建设,2004,25(1):22-23
|
CSCD被引
14
次
|
|
|
|
|
9.
Keitelman A D. Localized acidification as the cause of passivity breakdown of high purity zinc.
Corrosion Science,1984,24(6):535-545
|
CSCD被引
2
次
|
|
|
|
|
10.
Suxuki I. The behavior of corrosion products on zinc in sodium chloride solution.
Corrosion Science,1985,25(11):1029-1034
|
CSCD被引
4
次
|
|
|
|
|
11.
Fiauda C. Electrochemical impedance in a thin surface electrolyte layer influence of the potential probe location.
Electrochimica Acta,1987,32(3):445-448
|
CSCD被引
2
次
|
|
|
|
|
12.
Deslouis C. The kinetics of zinc dissolution in aerated sodium sulfate solutions a measurement of the corrosion rate by impedance techniques.
Corrosion Science,1989,29(1):13-30
|
CSCD被引
4
次
|
|
|
|
|
13.
Quintana P. Study of the composition and morphology of initial stage of corrosion products formed on Zn plates exposed to the atmosphere of Southeast Mexico.
Applied Surface Science,1996,99(4):325-334
|
CSCD被引
7
次
|
|
|
|
|
14.
Aleida E. Atmospheric corrosion of zinc Part:Rural and urban atmospheres.
British Corrosion Journal,2000,35(4):284-288
|
CSCD被引
6
次
|
|
|
|
|
15.
Almeida E. Atmospheric corrosion of zinc PartⅡ:Marine atmospheres.
British Corrosion Journal,2000,35(4):289-296
|
CSCD被引
9
次
|
|
|
|
|
16.
Odnevall I. Formation of Zn_4SO_4(OH)_6?4H_2O in a rural atmosphere.
Corrosion Science,1994,36(6):1077-1091
|
CSCD被引
7
次
|
|
|
|
|
17.
Odnevall I. Formation of NaZn_2Cl(OH)_6-SO_4?6H_2O in a marine atmosphere.
Corrosion Science,1993,34(7):1213-1229
|
CSCD被引
15
次
|
|
|
|
|
18.
Azmat N S. Corrosion of Zn under acidified marine droplets.
Corrosion Science,2011,53(4):1604-1615
|
CSCD被引
28
次
|
|
|
|
|
19.
王振尧. 我国若干典型大气环境中的锌腐蚀.
腐蚀科学与防护技术,2003,15(4):191-195
|
CSCD被引
12
次
|
|
|
|
|
20.
严川伟. Zn在SO_2环境中大气腐蚀初期表面特性研究.
腐蚀科学与防护技术,2000,12(3):151-153
|
CSCD被引
7
次
|
|
|
|
|
了解气象卫星更多信息，请访问