受力的LY12和LC4铝合金在中国西部盐湖大气环境中的腐蚀行为
Atmospheric Corrosion Behavior of Pre-strained Aluminum Alloys LY12 and LC4 in Salt Lake Environment inWestern China
查看参考文献29篇
|
文摘
|
通过现场大气暴露实验,利用金相显微镜和SEM等手段分析试样表面和截面形貌,研究了U弯受力状态下包铝与无包铝的LY12和LC4两种铝合金在我国西部盐湖大气环境中的腐蚀行为。结果表明,包铝的两种铝合金的腐蚀主要发生在包铝层,以点蚀为主,未观察到包铝层被穿透现象。无包铝的铝合金试样都发生了明显的沿晶应力腐蚀开裂,其中LY12铝合金在拉应力和压应力下都有较多的应力腐蚀裂纹,LC4铝合金只在拉应力下观察到了裂纹;两种铝合金在压应力下都发生了剥层腐蚀,拉应力下剥层腐蚀受到抑制。 |
|
其他语种文摘
|
Atmospheric corrosion behavior of U-bended aluminum alloy plates of LY12 and LC4 with/without Al cladding was investigated by field exposure in salt lake environment in Western China for 2 a. Then their surface and cross- sectional morphology was examined by metalloscope and SEM. The results showed that the corrosion behavior of the Al clad alloys LY12 and LC4 was mainly pitting corrosion within the cladding and no pits penertrating the cladding could be observed after 2 a exposure. For the bare alloys LY12 and LC4, severe stress corrosion cracking (SCC) was observed in the test. Both tensile- and compressive- stress could lead to SCC in for LY12, while only tensile stress could induce SCC for LC4 during the exposure. Exfoliation corrosion (EFC) of LY12 and LC4 occurred under compressive stress but not under tensile stress. |
|
来源
|
中国腐蚀与防护学报
,2014,34(3):287-293 【核心库】
|
|
关键词
|
LY12铝合金
;
LC4铝合金
;
盐湖大气环境
;
应力腐蚀开裂
;
剥层腐蚀
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-4537 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金重点项目
;
国防技术基础项目
;
国家电网科技项目
|
|
文献收藏号
|
CSCD:5179562
|
参考文献 共
29
共2页
|
|
1.
刘静安.
铝合金材料应用与开发,2011:71-74
|
CSCD被引
4
次
|
|
|
|
|
2.
Vargel C.
Corrosion of Aluminium,2004:235-289
|
CSCD被引
3
次
|
|
|
|
|
3.
Ailor W H.
Atmospheric Corrosion,1982:353-364
|
CSCD被引
2
次
|
|
|
|
|
4.
Lee T S.
Degradation of metals in atmosphere, STP 965,1988:191-205
|
CSCD被引
1
次
|
|
|
|
|
5.
曹楚南.
中国材料的自然环境腐蚀,2005:108-122
|
CSCD被引
5
次
|
|
|
|
|
6.
Sun S Q. Long-term atmospheric corrosion behaviour of aluminium alloys 2024 and 7075 in urban, coastal and industrial environments.
Corros. Sci,2009,51:719-727
|
CSCD被引
44
次
|
|
|
|
|
7.
Sun S Q. Exfoliation corrosion of extruded 2024-T4 in the coastal environments in China.
Corros. Sci,2011,53:2527-2538
|
CSCD被引
17
次
|
|
|
|
|
8.
Cheng Y L. A study of the corrosion of aluminium alloy 2024-T3 under thin electrolyte layers.
Corros. Sci,2004,46:1649-1667
|
CSCD被引
48
次
|
|
|
|
|
9.
Shi Y Y. Electrochemical noise study on 2024-T3 Aluminium alloy corrosion in simulated acid rain under cyclic wet-dry condition.
Electrochim. Acta,2006,51:4977-4986
|
CSCD被引
22
次
|
|
|
|
|
10.
Wang Z Y. Corrosion behavior on aluminum alloy LY12 in simulated atmospheric corrosion process.
Chin. J. Nonferrous Met,2007,17:326-334
|
CSCD被引
19
次
|
|
|
|
|
11.
王振尧. LC4铝合金在模拟污染大气环境中的腐蚀行为.
中国腐蚀与防护学报,2005,25(6):321-326
|
CSCD被引
15
次
|
|
|
|
|
12.
韩薇. 两种包铝的高强铝合金受力状态下的大气腐蚀行为.
腐蚀科学与防护技术,2003,15(5):254-258
|
CSCD被引
4
次
|
|
|
|
|
13.
安百刚. LYl2铝合金在模拟酸雨溶液中的阻抗谱研究.
中国腐蚀与防护学报,2003,23(3):167-170
|
CSCD被引
11
次
|
|
|
|
|
14.
蔡健平. 航空铝合金大气腐蚀加速试验研究.
中国腐蚀与防护学报,2005,25(5):262-266
|
CSCD被引
13
次
|
|
|
|
|
15.
孙霜青. 包铝的7075和2024合金在海洋大气环境中的点蚀演化机制.
中国腐蚀与防护学报,2012,32(3):195-202
|
CSCD被引
7
次
|
|
|
|
|
16.
张晓云. 环境对高强度铝合金应力腐蚀行为的影响.
中国腐蚀与防护学报,2007,27(6):354-362
|
CSCD被引
11
次
|
|
|
|
|
17.
郑喜玉.
中国盐湖志,2002:1-43
|
CSCD被引
8
次
|
|
|
|
|
18.
王遵亲.
中国盐渍土,1993:251-310
|
CSCD被引
3
次
|
|
|
|
|
19.
何明山.
GB/T15970.3-1995.《金属和合金的腐蚀应力腐蚀试验第3部分: U型弯曲试样的制备和应用》
|
CSCD被引
1
次
|
|
|
|
|
20.
Wang B B. Atmospheric corrosion of aluminium alloy 2024-T3 exposed to salt lake environment in western China.
Corros. Sci,2012,59:63-70
|
CSCD被引
31
次
|
|
|
|
|
了解气象卫星更多信息，请访问