烧结矿抗压及跌落强度试验研究
Experimental Study on Compression and Drop Strength of Sinter
查看参考文献10篇
|
文摘
|
烧结矿制备及冷却是钢铁行业的重要工艺过程,烧结矿抗压和高位跌落强度是影响烧结矿成品率的重要参数。以烧结矿为试验样品,获取了烧结矿抗压和跌落强度。研究结果表明,对于试验样品烧结矿来说,20~30mm粒度烧结矿平均抗压强度为5.02MPa;500~700℃高温烧结矿2m高位跌落产生的10mm以下粒度的烧结矿最高增加2.70%,5mm以下粒度的烧结矿最高增加1.11%。 |
|
其他语种文摘
|
Sintering and cooling of sinter are important processes in steel industry. Compression strength and drop strength of sinter are important parameters that influence the rate of finished products of sinter. With sinter of a steel plant as experimental sample, the compression strength and drop strength of sinter was obtained. The results show that, for sinter sample with granularity between 20mm and 30mm, average compression strength is 5.02MPa; when sinter with temperature between 500℃ and 700℃ drops from 2m height to ground, sinter whose granularity is lower than 10mm increases by 2.70%, while sinter whose granularity is lower than 5mm increases by 1.11%. |
|
来源
|
钢铁研究学报
,2014,26(3):5-9 【核心库】
|
|
关键词
|
烧结矿
;
抗压强度
;
跌落强度
;
试验研究
|
|
地址
|
1.
中国科学院力学研究所, 高温气体动力学国家重点实验室, 北京, 100190
2.
中信重工机械股份有限公司, 河南, 洛阳, 471039
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-0963 |
|
基金
|
国家863计划
;
中国科学院知识创新工程重要方向项目
|
|
文献收藏号
|
CSCD:5098858
|
参考文献 共
10
共1页
|
|
1.
杨光亮. 原料组成和燃耗对烧结矿强度影响的试验研究.
贵州工业大学学报,2006,35(1):10
|
CSCD被引
1
次
|
|
|
|
|
2.
张金柱. 熔剂对阳春粉熔化性及烧结质量的影响.
钢铁研究学报,2010,22(12):7
|
CSCD被引
2
次
|
|
|
|
|
3.
黄建平. 组织结构对烧结矿强度影响.
过程工程学报,2009,9(增1):258
|
CSCD被引
1
次
|
|
|
|
|
4.
王文山. 冷却方式对钒钛磁铁矿烧结过程和烧结矿强度的影响.
河北理工学院学报,2007,29(1):12
|
CSCD被引
1
次
|
|
|
|
|
5.
范晓慧. MgO对高碱度烧结矿强度的影响及机理.
中南大学学报,2012,43(9):3325
|
CSCD被引
16
次
|
|
|
|
|
6.
王文山. 碱度对钒钛烧结矿强度和烧结过程的影响.
烧结球团,2006,31(5):11
|
CSCD被引
5
次
|
|
|
|
|
7.
朱亚东. 提高包钢低硅烧结矿强度的试验研究.
钢铁研究学报,2010,22(10):16
|
CSCD被引
1
次
|
|
|
|
|
8.
蒋大军. 采用多元非线性回归预测钒钛烧结矿强度.
烧结球团,2006,31(2):5
|
CSCD被引
6
次
|
|
|
|
|
9.
乔瑞庆. 低氟烧结矿微气孔的形成机理及对烧结矿强度的影响.
钢铁研究学报,1999,11(6):1
|
CSCD被引
3
次
|
|
|
|
|
10.
李光森.
粘结相对烧结矿强度的影响机理,2008
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问