Nd对Mg-6Zn-Mn镁合金显微组织和力学性能的影响
Effect of Nd Addition on the Microstructure and Mechanical Properties of Mg-6Zn-Mn Magnesium Alloy
查看参考文献16篇
|
文摘
|
利用光学显微镜、X射线衍射仪、扫描电子显微镜、万能力学试验机等手段,系统研究了稀土Nd的含量对Mg-6Zn-Mn镁合金的显微结构和力学性能的影响。结果表明,稀土Nd对铸态Mg-6Zn-Mn镁合金具有明显的细化枝晶作用。经过360℃挤压后,合金显微组织发生明显变化。当Nd含量较低时(低于0.4%,质量分数),合金的动态再结晶率较低,合金的室温综合力学性能最好,与初始合金相比,其屈服强度提高了17%,达到250MPa,抗拉强度超过300MPa。然而,随着Nd含量的进一步增加,合金的动态再结晶率升高,发生完全动态再结晶,在其晶界上析出粗大的T相,而导致合金综合力学性能下降。 |
|
其他语种文摘
|
The microstructure and mechanical properties of as-extruded Mg-6Zn-Mn magnesium alloy with different Nd content were investigated by OM, XRD and tensile testing, respectively. It was found that the dendrite arm spacing of as-cast Mg-6Zn-Mn magnesium alloys was effectively decreased with Nd addition. Furthermore, the microstructure of Mg-6Zn-Mn magnesium alloys changed significantly after hot extrusion at 360℃ with Nd doped under extrusion ratios of 25. The Mg-6Zn-Mn magnesium alloy with 0.2% Nd shows the highest yield strength (about 250 MPa) and ultimate strength (above 300MPa) by tensile tests at room temperature. |
|
来源
|
材料工程
,2013(3):1-5 【核心库】
|
|
DOI
|
10.3969/j.issn.1001-4381.2013.03.001
|
|
关键词
|
Mg-6Zn-Mn镁合金
;
稀土Nd
;
显微组织
;
力学性能
|
|
地址
|
重庆大学材料科学与工程学院, 国家镁合金材料工程技术研究中心, 重庆, 400045
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家973计划
;
国家“十二五”科技支撑计划项目
;
中央高校基本科研业务费
|
|
文献收藏号
|
CSCD:4774823
|
参考文献 共
16
共1页
|
|
1.
张丁非. 重庆镁合金研究与产业的发展现状与建议.
材料导报,2004,18(8A):16-19
|
CSCD被引
1
次
|
|
|
|
|
2.
丁文江. 高性能镁合金及其成形加工技术与应用研究进展.
新材料产业,2008(2):58-63
|
CSCD被引
10
次
|
|
|
|
|
3.
丁文江. 高性能镁合金研究及应用的新进展.
中国材料进展,2010,29(8):37-45
|
CSCD被引
101
次
|
|
|
|
|
4.
余琨. 变形镁合金材料的研究进展.
轻金属加工技术,2001,29(7):6-11
|
CSCD被引
1
次
|
|
|
|
|
5.
彭建. 高塑性Mg-Zn系稀土镁合金的研究进展.
热加工工艺,2010,39(18):15-19
|
CSCD被引
7
次
|
|
|
|
|
6.
戴庆伟. 新型Mg-Zn-Mn变形镁合金的挤压特性与组织性能研究.
材料工程,2008(4):38-42
|
CSCD被引
11
次
|
|
|
|
|
7.
Le Q C. Microstructures and mechanical properties of Mg-2%Zn-0.4%RE alloys.
Trans Nonferrous Met Soc China,2010,20(2):352-356
|
CSCD被引
5
次
|
|
|
|
|
8.
Zou H H. Effects of Nd on the microstructure of ZA52 alloy.
Materials Science and Engineering A,2005,392(1/2):229-234
|
CSCD被引
13
次
|
|
|
|
|
9.
Fu P H. Effects of heat treatments on the microstructures and mechanical properties of Mg-3Nd-0.2Zn-0.4%Zr(wt.%) alloy.
Materials Science and Engineering A,2008,486(1/2):183-192
|
CSCD被引
45
次
|
|
|
|
|
10.
Ding W J. Microstructure and mechanical properties of hot-rolled Mg-Zn-Nd-Zr alloys.
Materials Science and Engineering A,2008,483/484(15):228-230
|
CSCD被引
8
次
|
|
|
|
|
11.
Zhang D F. Microstructure evolution and mechanical properties of Mg-x%Zn-1%Mn(x=4, 5, 6, 7, 8, 9).
Trans Nonferrous Met Soc China,2011,21(1):15-25
|
CSCD被引
22
次
|
|
|
|
|
12.
Yang J. Microstructure and mechanical properties of Mg-4.5Zn-xNd (x=0, 1 and 2, wt.%) alloys.
Materials Science and Engineering A,2008,479(1/2):339-344
|
CSCD被引
11
次
|
|
|
|
|
13.
Li Q. Effect of Nd and Y addition on microstructure and mechanical properties of as-cast Mg-Zn-Zr alloy.
J Alloy Compd,2007,427(1/2):115-123
|
CSCD被引
42
次
|
|
|
|
|
14.
Gao X. Structure and thermal stability of primary intermetallic particles in an Mg-Zn casting alloy.
Scripta Materialia,2007,57(7):655-658
|
CSCD被引
35
次
|
|
|
|
|
15.
Wagner F. Evolution of recrystallisation texture and microstructure in low alloyed titanium sheets.
Acta Materialia,2002,50(5):1245-1259
|
CSCD被引
22
次
|
|
|
|
|
16.
Bozzolo N. Texture evolution during grain growth in recrystallized commercially pure titanium.
Materials Science and Engineering A,2005,397(1/2):346-355
|
CSCD被引
23
次
|
|
|
|
|
了解气象卫星更多信息，请访问