激光熔覆Ta-W合金组织及高温气动烧蚀性能
Microstructure and High Temperature Aerodynamic Ablation Property of Ta-W Alloy Deposited by Coaxial Laser Cladding
查看参考文献11篇
|
文摘
|
以纯W粉末为熔覆材料,纯Ta为基底,采用同轴送粉激光熔覆技术在Ta板侧面制备了Ta-W合金涂层。利用扫描电镜(SEM)、能谱(EDS)及显微硬度计对熔覆层的微观组织和显微硬度进行了分析,在直联式自由射流风洞试验台上对涂层的抗高温高速气流烧蚀性能进行了测试。结果表明,熔覆层与基底冶金结合,涂层内部为致密的树枝状Ta-W合金固溶体,大致均匀地分布于Ta中。Ta-W合金涂层平均HV硬度8GPa,为基材的5倍,同时抗烧蚀性能得到了显著提高。 |
|
其他语种文摘
|
A Ta-W alloy coating was deposited on pure Ta plate by coaxial laser cladding, using tungsten powder as cladding material. The microstructure of the coating was analyzed by scanning electron microscopy (SEM) and energy disperse spectroscopy (EDS). The microhardness was examined by hardness tester. The high temperature hypersonic flow ablation property was tested in the wind tunnel system. It is found that the coating is metallurgically bonded with the substrate. The clad layer has a microstructure consisting of dendrite Ta-W solid solution uniformly dispersed in the Ta matrix. The average microhardness of the clad layer is approximately 8 GPa and it is 5 times greater than that of the Ta substrate. The ablative property is also obviously improved. |
|
来源
|
稀有金属材料与工程
,2012,41(7):1211-1215 【核心库】
|
|
关键词
|
激光熔覆
;
同轴送粉
;
Ta-W合金
;
显微组织
;
烧蚀性能
|
|
地址
|
中国科学院力学研究所, 北京, 100190
|
|
语种
|
中文 |
|
ISSN
|
1002-185X |
|
学科
|
金属学与金属工艺;电子技术、通信技术 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:4603557
|
参考文献 共
11
共1页
|
|
1.
Etemad G A.
AIAA Journal,1966,4(9):1543
|
CSCD被引
3
次
|
|
|
|
|
2.
White J E.
AIAA Journal,1966,4(2):307
|
CSCD被引
3
次
|
|
|
|
|
3.
Marshall B W.
AIAA Journal,1966,4(11):1899
|
CSCD被引
2
次
|
|
|
|
|
4.
Zhou Jianqiu.
Journal of Iron and Steel Research,2006,13(4):68
|
CSCD被引
2
次
|
|
|
|
|
5.
Byun T S.
Journal of Nuclear Materials,2008,377:72
|
CSCD被引
3
次
|
|
|
|
|
6.
张廷杰. 高钨含量钽基合金力学性能的研究.
稀有金属材料与工程,1996,25(4):5
|
CSCD被引
11
次
|
|
|
|
|
7.
吴孟海.
稀有金属材料与工程,2006,35(S2):64
|
CSCD被引
6
次
|
|
|
|
|
8.
Mazumder J.
Optics and Laser Engineering,2000,34(4):397
|
CSCD被引
67
次
|
|
|
|
|
9.
钟如涛. 连续/脉冲CO_2激光熔覆高温合金K403.
中国激光,2010,37(3):852
|
CSCD被引
14
次
|
|
|
|
|
10.
王晶. γ-TiAl金属间化合物合金表面激光熔覆TiC-Ti-Al涂层研究.
稀有金属材料与工程,2008,37(12):2191
|
CSCD被引
6
次
|
|
|
|
|
11.
王宏宇. 纳米CeO_(2p)对镍基高温合金表面NiCoCrAlY激光熔覆涂层氧化行为的影响.
金属学报,2009,45(8):971
|
CSCD被引
15
次
|
|
|
|
|
了解气象卫星更多信息，请访问