热处理对定向凝固Co基合金微观组织的影响
Effect of Heat-treatment on Microstructure of Directional Solidification Co-base Superalloy
查看参考文献7篇
|
文摘
|
利用XRD和扫描电镜研究了热处理对一种定向凝固Co基合金微观组织的影响。结果表明:Co基合金的铸态组织主要由Co的固溶体基体、M_7C_3、MC和M_(23)C_6碳化物组成,其中M_7C_3和MC为块状,主要分布在枝晶间,M_(23)C_6呈颗粒状,分布在块状M_7C_3和MC周围。合金经1150℃×4h固溶处理后,大部分块状M_7C_3和MC溶入Co的固溶体基体中,在随后的空冷中析出颗粒状M_(23)C_6。在870℃和970℃时效时,随时效温度的升高和时效时间的延长,合金中M23C6的尺寸逐渐增大。 |
|
其他语种文摘
|
The effects of heat-treatment on the microstructure of directional solidification Co-base superalloy were investigated using XRD and SEM.The results show that the microstructure of Co-base superalloy as-cast is composed of Co matrix,M_7C_3,MC and M_(23)C_6.Among them,MC and M_7C_3 distributes in inter dentrite and M_(23)C_6 near the MC and M_7C_3.After solid solution heat-treating at 1150 ℃ for 4 h,most MC and M_7C_3 dissolves into Co-base matrix,M_(23)C_6 is deposited from Co matrix during following air cooling.When aging at 870 ℃and 970 ℃,the size of M_(23)C_6 increases with the increase of temperature and aging time. |
|
来源
|
热加工工艺
,2011,40(12):152-154,159 【核心库】
|
|
关键词
|
定向凝固Co基合金
;
固溶
;
时效
;
碳化物
|
|
地址
|
1.
辽宁工程技术大学材料科学与工程学院, 辽宁, 阜新, 123000
2.
中平能化集团天工机械制造有限公司, 河南, 平顶山, 467000
3.
中国科学院力学研究所, 北京, 100190
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-3814 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:4425540
|
参考文献 共
7
共1页
|
|
1.
Ssims C T. A contemporary view of cobalt-base alloys.
J. Met.,1967,21(1):27-42
|
CSCD被引
1
次
|
|
|
|
|
2.
Davin A. Modified X40 alloy with improved creep-rupture strength.
Cobalt,1974(2):32-33
|
CSCD被引
1
次
|
|
|
|
|
3.
Fukui Y. Effect of titanium, niobium and zirconium on creep rupture strength and ductility of superalloy.
Metall. Trans. A,1981,12:1033-1039
|
CSCD被引
1
次
|
|
|
|
|
4.
Vandermousen R F. Directional solidification of cobalt-base superalloys.
Cobalt,1974(1):6-12
|
CSCD被引
1
次
|
|
|
|
|
5.
姜文辉. DZ40M钴基高温合金950℃长期时效后的组织与性能.
金属学报,1998,34(12):1289-1294
|
CSCD被引
9
次
|
|
|
|
|
6.
Hiroshi. Effect of heat treatment on precipitation behaviour and high temperature strength in a wrought Co-base superalloy.
Journal of Materials Science,1986,21:2803-2811
|
CSCD被引
1
次
|
|
|
|
|
7.
Jiang Wenhui. Secondary carbide precipitation in a directionally solidified cobalt base superalloy.
Metall. Trans. A,1999,30:513-520
|
CSCD被引
6
次
|
|
|
|
|
了解气象卫星更多信息，请访问