文摘
|
通过对第三代镍基粉末高温合金FGH98进行热模拟压缩实验，得到了不同温度（1050~1110°C)和不同应变速率下（0.01~ 1s~(-1)）的真应力-真应变曲线。根据其特点分析了该合金的流变应力与温度和应变速率以及应变量的关系。由实验结果得出：该曲线呈典型的热激活特征，合金流变应力对变形温度和应变速率敏感。在此基础上选用Arrhenius方程低应力水平下的简化模型作为其本构关系的经验公式，利用线性回归法确定相关系数并对其误差进行分析，从而得到了该合金的本构方程。 |
|
其他语种文摘
|
Based on the data of hot-compressing tests which were carried out at temperature ranged from 1050℃ to 1110℃ and strain rate from 0.01s~(-1) to 1s~(-1), a system of flow curves of the new type 3~(rd) generation nickel-based superalloy FGH98 was obtained. Then they were used to uncover how the flow stress changes by the change of temperature and strain rate as well as strain. It shows that the curve takes on a typical agitation charateristic and the flow stresses are very sensitive to temperature and strain rate. Subsequently, Arrehenius equation was selected as a model of the constitutive relationship, and the relative parameters were figured out by linear regression analysis of the experimental data with simple error analysis. Then the constitutive equation has been established. |
|
来源
|
航空材料学报
,2011,31(6):12-18 【核心库】
|
|
DOI
|
10.3969/j.issn.1005-5053.2011.6.003
|
|
关键词
|
FGH98
;
粉末冶金
;
高温合金
;
真应力-应变曲线
;
线性回归
;
本构方程
|
|
地址
|
钢铁研究总院高温材料研究所, 北京, 100081
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-5053 |
|
学科
|
航空 |
|
基金
|
国家863计划
|
|
文献收藏号
|
CSCD:4377135
|
|
|
1.
胡本芙. 新型高性能粉末高温合金的研究与发展.
材料工程,2007(2):49-57
|
CSCD被引
14
次
|
|
|
|
|
2.
贾建. 第三代粉末冶金高温合金René104的研究进展.
粉末冶金工业,2007,6:36-43
|
CSCD被引
1
次
|
|
|
|
|
3.
李力. 热等静压及其加锻造和热挤压粉末高温合金FGH95的组织和性能.
钢铁研究总院学报,1985,5(4):411-415
|
CSCD被引
3
次
|
|
|
|
|
4.
吴凯. 新型镍基粉末高温合金的高温变形行为.
航空材料学报,2010,30(4):1-7
|
CSCD被引
6
次
|
|
|
|
|
5.
王少林. 金属高温塑性本构方程的研究.
上海交通大学学报,1985,5(4):20-24
|
CSCD被引
1
次
|
|
|
|
|
6.
张仁鹏.
含夹杂粉末高温合金等温预成形设计与过程模拟,2007:24-25
|
CSCD被引
1
次
|
|
|
|
|
7.
Lenard G J G.
Modelling hot deformation of steels,1989:101-115
|
CSCD被引
2
次
|
|
|
|
|
8.
Peter T. A neutral templating route to mesoporous molecular.
Science,1995,267(10):865-867
|
CSCD被引
2
次
|
|
|
了解气象卫星更多信息，请访问