激光熔覆Ta-W合金涂层工艺方法研究
Research on Processing of Laser Cladding Ta-W Alloy Coatings
查看参考文献15篇
|
文摘
|
采用预置涂层和同轴送粉激光熔覆方法,分别以Ta/W混合粉末和纯W粉末为熔覆材料,纯Ta为基底,在Ta板上制备Ta-W合金涂层,对难熔金属材料的激光熔覆工艺方法进行了对比研究。利用扫描电镜(SEM)、能谱仪(EDS)及显微硬度计对两种方法所制备熔覆层的微观组织和显微硬度进行了分析。结果表明,预置粉末法激光熔覆层厚度均匀,稀释率低,涂层内部为粗大的Ta-W合金固溶体组织,熔覆层平均硬度为1500HV,高于基底10倍。同轴送粉法激光熔覆层与基底呈良好的冶金结合,熔深较大,涂层内部为致密细小的树枝状Ta-W合金固溶体,均匀分布于Ta中。涂层平均硬度为800HV,为基材的5倍。 |
|
其他语种文摘
|
Ta-W alloy coatings were deposited on pure Ta plate by laser cladding with pre-coating and coaxial powder injection respectively in order to find the effects with two technique.The microstructure of the coatings was analyzed using scanning electron microscopy(SEM)and energy dispersive spectroscopy(EDS).The microhardness was examined by hardness tester.The clad layer which formed with pre-coating had a microstructure of coarse columnar grain and low dilution rate with the substrate.The average microhardness of the clad layer was 1500 HV,it was 10 times greater than the Ta substrate.The clad layer deposited with coaxial power injection had a microstructure consisting of dendrite Ta-W solid solution uniformly dispersed in the Ta matrix.The average microhardness of the clad layer was approximately 800 HV and it was 5 times greater than that of the substrate |
|
来源
|
中国激光
,2011,38(8):0803008-1-080300-6 【核心库】
|
|
关键词
|
激光技术
;
激光熔覆
;
预置粉末
;
同轴送粉
;
Ta-W合金
;
显微组织
|
|
地址
|
中国科学院力学研究所, 中国科学院先进制造工艺力学实验室, 北京, 100190
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0258-7025 |
|
学科
|
金属学与金属工艺;电子技术、通信技术 |
|
基金
|
国家自然科学基金资助课题
|
|
文献收藏号
|
CSCD:4282631
|
参考文献 共
15
共1页
|
|
1.
G A Etemad. Oxidation and mechanical performance of tungsten at high temperatures and high pressures.
AIAA J,1966,4(9):1543-1548
|
CSCD被引
3
次
|
|
|
|
|
2.
J E White. Development of oxidation resistant tungsten-base alloys.
AIAA J,1966,4(2):307-312
|
CSCD被引
3
次
|
|
|
|
|
3.
B W Marshall. Oxidation and ablation characteristics of tantalum in a hyperthermal environment.
AIAA J,1966,4(11):1899-1905
|
CSCD被引
2
次
|
|
|
|
|
4.
Zhou Jianqiu. Comparative study on constitutive modeling of tantalum and tantalum tungsten alloy.
J.Iron &Steel Research,2006,13(4):68-74
|
CSCD被引
1
次
|
|
|
|
|
5.
T S Byun. Dose dependence of mechanical properties in tantalum and tantalum alloys after low temperature irradiation.
J.Nuclear Materials,2008,377(1):72-79
|
CSCD被引
3
次
|
|
|
|
|
6.
张廷杰. 高钨含量钽基合金力学性能的研究.
稀有金属材料与工程,1996,25(4):5-10
|
CSCD被引
11
次
|
|
|
|
|
7.
吴孟海. Ta-10W合金的高温力学性能.
稀有金属材料与工程,2006,35(2):64-67
|
CSCD被引
6
次
|
|
|
|
|
8.
J Mazumder. Closed loop direct metal deposition:art to part.
Optics &Lasers in Engineering,2000,34(4/6):397-414
|
CSCD被引
66
次
|
|
|
|
|
9.
I Manna. Laser surface cladding of Fe-B-C,Fe-B-Si and Fe-BC-Si-Al-C on plain carbon steel.
Surface &Coatings Technology,2006,201(1/2):434-440
|
CSCD被引
28
次
|
|
|
|
|
10.
翟玉峰. 激光熔覆TiC-Mo_2C颗粒增强Fe基涂层的组织与性能.
中国激光,2009,36(12):3287-3292
|
CSCD被引
10
次
|
|
|
|
|
11.
L Shepeleva. Laser cladding of turbine blades.
Surface &Coatings Technology,2000,125(1/3):45-48
|
CSCD被引
43
次
|
|
|
|
|
12.
A J Pinkerton. Rapid prototyping using direct laser deposition———the effect of powder atomization type and flowrate.
J.Engineering Manufacture,2003,217(6):741-752
|
CSCD被引
1
次
|
|
|
|
|
13.
钟如涛. 连续/脉冲CO_2激光熔覆高温合金K403.
中国激光,2010,37(3):852-857
|
CSCD被引
14
次
|
|
|
|
|
14.
王宏宇. 纳米CeO_(2p)对镍基高温合金表面NiCoCrAlY激光熔覆涂层氧化行为的影响.
金属学报,2009,45(8):971-977
|
CSCD被引
15
次
|
|
|
|
|
15.
王文丽. 原位生成TaC颗粒增强镍基激光熔覆层.
中国激光,2007,34(2):277-282
|
CSCD被引
19
次
|
|
|
|
|
了解气象卫星更多信息，请访问