低碳钢在H2S溶液中的腐蚀行为研究
CORROSION BEHAVIOR OF MILD STEEL UNDER CONDITION OF H2S SOLUTION
查看参考文献10篇
|
文摘
|
通过腐蚀形貌分析、腐蚀产物分析和电化学测试多种分析测试手段,研究了干湿交替循环下低碳钢在H2S溶液中的腐蚀行为. 综合分析结果表明腐蚀初期产物较少,腐蚀速率与循环次数成正比;腐蚀后期,腐蚀产物较多,形成一层保护膜,阻碍腐蚀过程的进行,腐蚀速率与循环次数成反比. FeS的生成可能是腐蚀速率出现转折的一个因素 |
|
其他语种文摘
|
Corrosion behavior of mild steel in the condition of H2S in wet/dry cycles was studied by corrosion analysis, corrosion product and morphology analysis and electrochemical measurement. The results show that the initial corrosion products are less, and corrosion rate is proportional to cycle times;with accumulation of more corrosion product, which possibly acts as corrosion barrier, corrosion rate is inversely proportional to cycle times based on comprehensive analysis. The formation of FeS may be a factor responsible for a turning point of corrosion rate |
|
来源
|
中国腐蚀与防护学报
,2010,30(6):465-468 【核心库】
|
|
关键词
|
H2S
;
低碳钢
;
干湿交替循环
;
腐蚀行为
|
|
地址
|
1.
武汉大学资源与环境科学学院环境工程系, 武汉, 430072
2.
武汉大学资源与环境科学学院环境工程系, 金属腐蚀与防护国家重点实验室, 武汉, 430072
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-4537 |
|
学科
|
化学工业 |
|
文献收藏号
|
CSCD:4106249
|
参考文献 共
10
共1页
|
|
1.
黄旭. H_2S对低碳钢在焦炉煤气中腐蚀行为的影响.
钢铁钒钦,1998,19(4):14-20
|
CSCD被引
1
次
|
|
|
|
|
2.
顾宏邦. A3钢输煤气管道腐蚀穿孔机理的探讨.
山西大学学报(自然科学版),1992,15(1):41-47
|
CSCD被引
1
次
|
|
|
|
|
3.
Medvedeva M L. On the corrosion state of plants for purifying natural gas from acid components.
Prot. Met,2002,38(3):284-288
|
CSCD被引
1
次
|
|
|
|
|
4.
Ma H Y. The influence of hydrogen sulfide on corrosion of iron under different conditions.
Corros. Sci,2000,42:1669
|
CSCD被引
62
次
|
|
|
|
|
5.
Polyakov S G. Specific features of the electrochemical behavior of steels under corrosion cracking of pipelines.
Mater. Sci,1999,35(5):650-656
|
CSCD被引
1
次
|
|
|
|
|
6.
Nishimura T. Electrochemical behavior of rust formed on carbon steel in a wet/dry environment condition chloride ions.
Corrosion,2000,56:935-941
|
CSCD被引
64
次
|
|
|
|
|
7.
董杰. 低碳钢带锈电极的腐蚀行为.
腐蚀科学与防护技术,2006,15(6):414-417
|
CSCD被引
29
次
|
|
|
|
|
8.
李明. 在湿H2S环境中金属腐蚀行为和机理研究概述.
腐蚀科学与防护技术,2005,17(2):107-111
|
CSCD被引
22
次
|
|
|
|
|
9.
Li J. Development of an artificial climatic complex accelerated corrosion tester and investigation of complex accelerated corrosion test methods.
Corrosion,1999,55:498
|
CSCD被引
8
次
|
|
|
|
|
10.
刘永辉.
电化学测试技术,1987:357-395
|
CSCD被引
2
次
|
|
|
|
|
了解气象卫星更多信息，请访问