Preparation of Ordered Mesoporous Carbon/Polyaniline Electrodes and as Electrochemical Sensors for Cu2+
介孔碳/聚苯胺修饰电极的制备及其对Cu2+的响应研究(英文)
查看参考文献34篇
|
文摘
|
A new electrode, obtained by the dispersion of ordered mesoporous carbon(MC) nanoparticles onto polyaniline(PANI) was presented in this paper. Ordered mesoporous carbon was prepared by pyrolysis of sucrose filled in the mesoporous channels of SBA-15 at 1 200 ℃, and followed by dissolution of the silica matrix in hydrofluoric acid. The pore structure of the MC material was evaluated using XRD, nitrogen adsorption,TEM.SEM showed that PANI-MC films presented a wholy modified morphology when compared to PANI film. Electrochemical characterization indicated that the potential shift toward negative direction. This can be attributed to the porous feature of MC, which imposes resistance for ion migration in mesoporous. The deposition potential and time had been optimized for determination of Cu2+ in aqueous solution. ASV analysis revealed that the new electrode presented a linear response to low concentrations of Cu2+. Under optimized conditions, the current showed a linear dependence with concentration in the range 1.00 ×10-81×10-6 mol. L-1.The detection limit was 6×10-9 mol. L-1.The results showed good reproducibility and stability |
|
其他语种文摘
|
制备了一个新的电极-聚苯胺掺杂介孔碳修饰电极(PANI-MC),并且研究了电极的电化学性质.在介孔分子筛SBA-15的孔道中沉积蔗糖,然后在氮气的保护下,1200℃热裂解,生成孔道规则排列的介孔碳(MC);XRD,N2吸附-脱附,TEM等方法表征了介孔碳的结构,用SEM表征了PANI-MC修饰电极的形貌.结果表明:复合电极膜与修饰前的聚苯胺膜形貌不同,与介孔碳形貌相似,介孔碳纳米微粒的大小清洗可辨,长度大约为2040μm.复合电极循环伏安结果显示:峰电位向负电位方向移动,这可能是因为介孔碳的孔道结构阻碍了离子的转移.同时,还研究了复合电极对Cu2+的相应,表明:电极对低浓度的Cu2+有很好的线性相应,可以作为Cu2+的感应器 |
|
来源
|
无机化学学报
,2010,26(11):1927-1933 【核心库】
|
|
关键词
|
mesoporous carbon
;
copper determination
;
electrodes
|
|
地址
|
Shenyang University of Chemical Technology, Education Department of Liaoning Province, Key Laboratory of Applied Technology of Polymer Materials, Shenyang, 110142
|
|
语种
|
英文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4861 |
|
学科
|
化学 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:4064776
|
参考文献 共
34
共2页
|
|
1.
Joo S H.
Mesopor. Mater,2001,44/45(1):153-158
|
CSCD被引
11
次
|
|
|
|
|
2.
Ryoo R.
Adv. Mater,2001,13(9):677-681
|
CSCD被引
96
次
|
|
|
|
|
3.
Jun S.
J.Am. Chem. Soc,2000,122(43):10712-10713
|
CSCD被引
169
次
|
|
|
|
|
4.
Shin H J.
Chem. Commun,2001,4:349-350
|
CSCD被引
9
次
|
|
|
|
|
5.
Ryoo R.
Stud. Surf. Sci. Catal,2001,135:150-157
|
CSCD被引
9
次
|
|
|
|
|
6.
Yahya A I.
Sens. Actuators B,2008,129(2):834-840
|
CSCD被引
2
次
|
|
|
|
|
7.
Rasa P.
Electrochimica Acta,2004,50(1):159-167
|
CSCD被引
1
次
|
|
|
|
|
8.
Zoran M.
Electrochim. Acta,2009,54(10):2941-2950
|
CSCD被引
4
次
|
|
|
|
|
9.
Xu G C.
Eur. Polym. J,2009,45(9):2701-2707
|
CSCD被引
5
次
|
|
|
|
|
10.
Li X X.
Electrochim. Acta,2009,54(24):5634-5639
|
CSCD被引
2
次
|
|
|
|
|
11.
Wang F.
Talanta,2009,79(2):376-382
|
CSCD被引
4
次
|
|
|
|
|
12.
Zeng X D.
Sens. Actuators B,2008,133(2):381-386
|
CSCD被引
4
次
|
|
|
|
|
13.
Tan J.
Talanta,2008,76(1):9-14
|
CSCD被引
8
次
|
|
|
|
|
14.
Lok P S.
Talanta,2004,64(2):13-319
|
CSCD被引
1
次
|
|
|
|
|
15.
Senthilkumar S.
Sens. Actuators B,2009,141(1):65-75
|
CSCD被引
1
次
|
|
|
|
|
16.
Rihab N.
Electrochem. Commun,2010,12(1):98-100
|
CSCD被引
1
次
|
|
|
|
|
17.
Pandey P C.
Sens. Actuators B,1999,54(3):210-214
|
CSCD被引
1
次
|
|
|
|
|
18.
Xin Y L.
Biosens. Bioelectron,2008,24(3):369-375
|
CSCD被引
1
次
|
|
|
|
|
19.
FAN Li-Fang.
Fenxi Ceshi Xuebao,2010,2:180-184
|
CSCD被引
1
次
|
|
|
|
|
20.
Zen J M.
Electroanalysis,2003,15:1073-1087
|
CSCD被引
6
次
|
|
|
|
|
了解气象卫星更多信息，请访问