时效温度及微量Zr+Si对Zn-22%Al合金阻尼性能的影响
INFLUENCES OF AGING TEMPERATURE AND MINOR ADDITION OF Zr+Si ON THE DAMPING PROPERTY OF Zn-22%Al ALLOY
查看参考文献26篇
|
文摘
|
采用动态力学分析仪(DMA)结合显微组织观察,研究了淬火后时效温度以及微量Zr+Si对Zn-22%Al合金阻尼性能的影响.结果表明,随着时效温度的升高,过饱和铝固溶体(α'相)分解加速,片层状组织数量增加并粗化,相界面数量减少,合金的阻尼性能降低.向Zn-22%A1合金中添加微量的Zr+Si后,Zr可抑制合金内粗大树枝晶的生成,细化枝晶;Si可降低α'相分解速率,部分α'相在较低温度下分解成粒状组织,增加铸态合金内相界面数量,同时初生Si相与基体形成非共格界面,产生Si相/基体界面弛豫行为,从而显著提高合金的阻尼性能.Si相与基体因热错配引入的位错通过原子的互扩散而逐渐消失,对合金阻尼性能的影响较小. |
|
其他语种文摘
|
The influences of aging temperature and minor addition of Zr+Si on the damping property of Zn-22%Al alloy were investigated by dynamic mechanical analyzer(DMA) and microstructure observation.The results show that with the increase of aging temperature,the decomposition of super-saturated solid solution of Al(α′phase) is accelerated,resulting in increasing and coarsening of the lamellar structure,which will impair damping property.In addition,the damping property of Zn- 22%Al alloy could be significantly improved by the minor addition of Zr+Si elements,which induced microstructure refinement and increase of interface.The dislocations induced by thermal mismatch between Si phase and matrix have little influence on the damping property of alloy,as the inter-diffusion of atoms makes dislocations decrease gradually. |
|
来源
|
金属学报
,2009,45(9):1099-1105 【核心库】
|
|
关键词
|
Zn-22%A1
;
时效温度
;
Zr
;
Si
;
阻尼性能
|
|
地址
|
中国科学院金属研究所, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:3703090
|
参考文献 共
26
共2页
|
|
1.
孙连超.
锌及锌合金物理冶金学,1994:19,21,283
|
CSCD被引
1
次
|
|
|
|
|
2.
Nuttall K.
Journal of the Institute of Metals,1971,99:266
|
CSCD被引
5
次
|
|
|
|
|
3.
Zhu X F.
Journal of Applied Physics,1990,67:7287
|
CSCD被引
4
次
|
|
|
|
|
4.
Ritchie I G.
Metall Tans.A,1991,22:607
|
CSCD被引
1
次
|
|
|
|
|
5.
Ritchie I G.
Metallurgical Transactions.A,1991,22:617
|
CSCD被引
7
次
|
|
|
|
|
6.
Wei J N.
Phys Star Sol.A,2002,191:435
|
CSCD被引
5
次
|
|
|
|
|
7.
Hinai M.
Journal of the Japan Institute of Metals,1991,55:715
|
CSCD被引
2
次
|
|
|
|
|
8.
Smith A E W.
Journal of the Institute of Metals,1973,101:320
|
CSCD被引
1
次
|
|
|
|
|
9.
Luo B H.
Material Science and Engineering A,2004,370:172
|
CSCD被引
9
次
|
|
|
|
|
10.
Savaskan T.
WEAR,1987,116:211
|
CSCD被引
9
次
|
|
|
|
|
11.
张忠明. ZA27-4%Si合金的阻尼性能及阻尼机理~①.
中国有色金属学报,2003,13:1175
|
CSCD被引
7
次
|
|
|
|
|
12.
Jones R]5.
Philosophical Magazine,1970,22:427
|
CSCD被引
1
次
|
|
|
|
|
13.
Kato M.
Journal of the Japan Institute of Metals,1974,38:539
|
CSCD被引
1
次
|
|
|
|
|
14.
田荣痒.
湖南冶金,1990(3):17
|
CSCD被引
1
次
|
|
|
|
|
15.
高光敏.
国外金属材料,1989(1):44
|
CSCD被引
1
次
|
|
|
|
|
16.
Norman A F.
ACTA MATERIALIA,1998,46:5715
|
CSCD被引
90
次
|
|
|
|
|
17.
Knipling K E.
ACTA MATERIALIA,2008,56:114
|
CSCD被引
28
次
|
|
|
|
|
18.
Fuller M L.
Trans AIMME,1935,117:338
|
CSCD被引
1
次
|
|
|
|
|
19.
Gale W F.
Smithells Metals Reference Book(8th ed),2004:6-1
|
CSCD被引
1
次
|
|
|
|
|
20.
Schoeck G.
Phys Star Sol,1969,32:651
|
CSCD被引
3
次
|
|
|
|
|
了解气象卫星更多信息，请访问