拉速对连铸方坯轻压下率的影响
INFLUENCE OF CASTING SPEED ON SOFT REDUCTION GRADIENT IN CONTINUOUS CASTING BLOOM
查看参考文献13篇
|
文摘
|
结合压下率理论模型,考察了连铸方坯在不同拉速下压下率的变化规律.结果表明,方坯压下率在轻压下入口处最大,沿拉坯方向线性减少;与板坯相比,两者的压下率值在轻压下入口处均相差不大,方坯压下率值在轻压下出口处较板坯小;拉速每增加0.1 m/min,方坯平均压下率减少约为0.04 mm/m.方坯压下速率的取值范围不受拉速影响,最大值和最小值分别为0.13和0.04 mm/min.压下速率沿拉坯方向呈线性减少,拉速越大,压下速率减少越慢;方坯的平均压下速率也不随拉速变化,保持定值0.088 mm/min,较板坯的平均压下速率小. |
|
其他语种文摘
|
On the basis of the theoretical model of soft reduction gradient, the soft reduction gradients for continuous casting bloom under different casting speeds were investigated. The results show that the reduction gradient of bloom is the biggest at the inlet of soft reduction zone, and decreases linearly along the strand. The value of bloom reduction gradient is much lower than that of slab at the outlet of soft reduction zone, and little different from that of slab at the inlet of soft reduction zone.As the casting speed increases by 0.1 m/min, the average reduction gradient of bloom decreases by 0.04 mm/m. It seems that the casting speed has no effect on the range of reduction rate which changes linearly from 0.13 to 0.04 mm/min. And the average reduction rate of bloom, which is independent of
casting speed and keeps the value of 0.088 mm/min, is much lower than that of slab. |
|
来源
|
金属学报
,2009,45(2):253-256 【核心库】
|
|
关键词
|
连铸方坯
;
轻压下
;
压下率
;
压下速率
|
|
地址
|
1.
中冶赛迪工程技术股份有限公司自动化事业部, 重庆, 400013
2.
东北大学材料与冶金学院, 辽宁, 沈阳, 110044
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:3538334
|
参考文献 共
13
共1页
|
|
1.
Sivesson P.
Ironmaking Steelmaking,1998,25:239
|
CSCD被引
10
次
|
|
|
|
|
2.
Raja V R.
Steel Times Int,2005,29(4):41
|
CSCD被引
4
次
|
|
|
|
|
3.
Scholes A.
Ironmaking and Steelmaking,2005,32:101
|
CSCD被引
14
次
|
|
|
|
|
4.
Flemings M C.
ISIJ International,2000,40:833
|
CSCD被引
65
次
|
|
|
|
|
5.
Yim C H.
ISIJ International,1996,36(Suppl):231
|
CSCD被引
9
次
|
|
|
|
|
6.
Morwald K.
Steel Times Int,2003,12(1):17
|
CSCD被引
3
次
|
|
|
|
|
7.
Morsut L.
MPT Int,2003,26(2):44
|
CSCD被引
3
次
|
|
|
|
|
8.
H(o)dl H.
MPT Int,2003,26(3):74
|
CSCD被引
1
次
|
|
|
|
|
9.
Shigeaki O.
ISIJ International,1991,31:1400
|
CSCD被引
7
次
|
|
|
|
|
10.
Ralph N.
STEEL RESEARCH,2003,74:700
|
CSCD被引
6
次
|
|
|
|
|
11.
Yamanaka A.
Ironmaking and Steelmaking,1999,26:64
|
CSCD被引
6
次
|
|
|
|
|
12.
林启勇. 连铸板坯轻压下过程压下率理论模型及其分析.
金属学报,2007,43:847
|
CSCD被引
10
次
|
|
|
|
|
13.
林启勇. 连铸板坯轻压下过程中的压下效率分析.
金属学报,2007,43:1301
|
CSCD被引
8
次
|
|
|
|
|
了解气象卫星更多信息，请访问