2A97铝锂合金时效行为研究
The Aging Behavior of Aluminum-Lithium Alloy 2A97
查看参考文献17篇
|
文摘
|
通过DSC、XRD、TEM、硬度测试和拉伸测试等手段，研究了2A97铝锂合金时效组织和性能变化。结果表明：2A97合金淬火后在165℃时效18h的显微组织以θ″／θ′和δ′相为主，出现了大量分布不均匀乃相。在165℃时效，随时间延长，T1数量密度增加，平均长度减小，δ′数量密度增加，θ′数量密度和长度增加。在165℃时效18h得到较高的强度和塑性。淬火变形后于135℃时效的组织以细小θ″／θ′、T1和δ′为主，T1和θ″／θ′数量明显高于未变形时效组织。淬火变形后于135℃时效36h的强度明显提高，σ0.2,σb和65分别为441MPa，519MPa和7．4％。 |
|
其他语种文摘
|
The evolution of microstructures and properties of aged 2A97 alloy at 165 ℃ after quenching, and at 135 ℃ after quenching and 4% plastic deformation for various times were investigated. The results show that θ″/θ′ and δ′ phases are the main strengthening phases of aged alloy at 165 ℃ for 18 h after quenching, which shows high tensile strength and ductility resulting from increasing amount of T1 phase distributed heterogeneously in matrix. With increasing aging time at 165 ℃, the number density of θ″/θ′, T1, and δ′ increase, and the length of T1 decreases, while the length of θ″/θ′ increases. Stretch before aging fines the size of θ″/θ′ and T1, and stimulates the precipitation and uniform distribution of them, so it yields higher strength for the alloy aged at 135 ℃ for 36 h after quenching and stretch, which is 441 MPa, 519 MPa, and 7.4% for σ0.2,σb, and δ5, respectively, than the alloy aged at 165 ℃ after quenching. |
|
来源
|
稀有金属材料与工程
,2008,37(11):1898-1902 【核心库】
|
|
关键词
|
时效
;
回归
;
2A97
;
铝锂合金
;
DSC
;
XRD
|
|
地址
|
1.
东北大学, 辽宁, 沈阳, 110004
2.
北京航空材料研究院, 北京, 100095
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-185X |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家973计划
|
|
文献收藏号
|
CSCD:3474901
|
参考文献 共
17
共1页
|
|
1.
Noble B.
Metal Science Journal,1972,6:167
|
CSCD被引
26
次
|
|
|
|
|
2.
Rioja R J.
Aluminum-LithiumⅢ, Proceedings of the Third International Aluminum-Lithium Conference,1985:471
|
CSCD被引
1
次
|
|
|
|
|
3.
Honma T.
Acta Materialia,2004,52:1997
|
CSCD被引
5
次
|
|
|
|
|
4.
Cassada W A.
Metallurgical Transactions A,1991,22:287
|
CSCD被引
29
次
|
|
|
|
|
5.
Howe J M.
Metallurgical Transactions A,1988,19:2911
|
CSCD被引
16
次
|
|
|
|
|
6.
蒋晓军.
金属学报,1994,30(8):355
|
CSCD被引
5
次
|
|
|
|
|
7.
Gable B M.
Journal of Light Metals,2001,1:1
|
CSCD被引
72
次
|
|
|
|
|
8.
Huang Baiyun.
Acta Mater,1998,46(12):4381
|
CSCD被引
1
次
|
|
|
|
|
9.
Ghosh K S.
Metallurgical and Materials Transactions A,2004,35:3681
|
CSCD被引
7
次
|
|
|
|
|
10.
Gregson P J.
Acta Metall,1985,33(3):527
|
CSCD被引
27
次
|
|
|
|
|
11.
Gayle F W.
Scripta Metallurgica et Materialia,1990,24:79
|
CSCD被引
21
次
|
|
|
|
|
12.
黄兰萍. 2197铝-锂合金的组织和性能.
中国有色金属学报,2004,4(12):2066
|
CSCD被引
21
次
|
|
|
|
|
13.
Pickens J R.
Scripta Metallurgica et Materialia,1990,24:457
|
CSCD被引
5
次
|
|
|
|
|
14.
Kumar K S.
Scripta Metallurgica et Materialia,1990,24:1245
|
CSCD被引
12
次
|
|
|
|
|
15.
金延.
航空学报,1991,12(5):313
|
CSCD被引
1
次
|
|
|
|
|
16.
Tosten M H.
Metallurgical Transactions A,1988,19:51
|
CSCD被引
11
次
|
|
|
|
|
17.
Blankenship J C P.
Acta Metall Mater,1994,42(3):845
|
CSCD被引
5
次
|
|
|
|
|
了解气象卫星更多信息，请访问