文摘
|
针对激光相变强化搭接带存在的回火软化等问题,对激光强化的球墨铸铁材料QT700-2搭接区的显微硬度、表面粗糙度、物相变化等进行了测试,并分析了强化机理。结果表明:选用合理的搭接率等工艺参数,球墨铸铁激光搭接强化后的硬度可达到50HRC以上,调节搭接宽度可以避免搭接区的回火软化问题。多道搭接强化后表层的马氏体组织呈区域性交错分布,材料表面形成非均匀、多尺度强化结构,强化后的表面具有良好的耐磨性和耐疲劳性。通过上述结果,对材料激光搭接强化的工艺参数进行了合理的优化。 |
|
其他语种文摘
|
Microhardness,surface roughness and phase transformation of overlapping zone in multi-track laser hardening on a ductile cast iron QT700-2 were tested.The experimental results show that with proper processing parameters,the microhardness of treated layer can be higher than 50HRC.The temper softening in overlapping zone can be prevented by changing the overlapping ratio.The interlaced distribution of martensite and non-uniform,multi-scale structure in hardened zone after multi-track laser hardening led to a good wear and fatigue resistance of surface.Processing parameters of laser hardening on ductile cast iron were optimized. |
|
来源
|
材料热处理学报
,2008,29(6):168-172 【核心库】
|
|
关键词
|
脉冲激光相变强化
;
搭接工艺
;
球墨铸铁QT700-2
;
强化带
|
|
地址
|
中国科学院力学研究所, 先进制造工艺力学中科院重点实验室, 北京, 100190
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1009-6264 |
|
学科
|
金属学与金属工艺;电子技术、通信技术 |
|
文献收藏号
|
CSCD:3467064
|
|
|
1.
Miokovic T. Influence of cyclic temperature changes on the microstructure of AISI 4140 after laser surface hardening.
Acta Materialia,2007,55:589-599
|
CSCD被引
6
次
|
|
|
|
|
2.
Pantelis I D. Wear and corrosion resistance of laser surface hardened structural steel.
Surface and Coatings Technology,2002,298:125-134
|
CSCD被引
2
次
|
|
|
|
|
3.
庄其仁. 模具表面的激光热处理研究.
中国激光,2002,29(3):271-276
|
CSCD被引
4
次
|
|
|
|
|
4.
温宗胤. 大型汽车覆盖件拉深模具的激光表面强化处理.
应用激光,2006,26(4):230-232
|
CSCD被引
7
次
|
|
|
|
|
5.
虞 钢.
集成化激光智能加工工程,2001:109-112
|
CSCD被引
1
次
|
|
|
|
|
6.
崔春阳. 球墨铸铁变换激光束淬火性能的研究.
金属热处理,2006,31(10):31-33
|
CSCD被引
5
次
|
|
|
了解气象卫星更多信息，请访问