空心微珠表面化学沉积Co-P合金研究
Electroless plating Co-P alloy on the surface of fly ash cenospheres

刘家琴 ¹ 叶敏 ¹ 吴玉程 ¹ 张立德 ²

文摘	利用化学镀工艺在粉煤灰空心微珠表面均匀、完整地包覆磁性Co-P合金层,成功制备出新型轻质的复合导电粉体。使用XRD、EDS、SEM和镶嵌金相的方法对样品进行形貌观察和分析表征,并讨论了镀液温度、pH值和稳定剂浓度对沉积效率的影响。结果表明,空心微珠经过敏化-活化的表面预处理后,利用化学镀方法可以得到均匀、包覆完整的Co-P合金层,并且出现了新的晶化相-αCo单质。T=90℃、pH=10.2和加入适量的硫脲是使反应良好进行的最佳工艺参数。
其他语种文摘	A new kind of composite electric powder can be prepared by electroless plating Co-P alloy on fly ash cenospheres.XRD,EDS,SEM and Metallic microgragh analytical methods are utilized to show the properties and microstructure of the cenospheres coated with Co-P films.The influence of plating temperature,pH value and stabilize agent content on deposition rate are respectively discussed.The results indicate that uniform and high quality Co-P film can be obtained by electroless plating after sensitization and activation.A new crystalline phase of α-Co is appeared on the plating films.Adjusting the plating temperature at 90℃,pH value at 10.2 and adding proper thiourea could enable the reaction well.
来源	功能材料 ,2008,39(11):1850-1852 【核心库】
关键词	空心微珠 ; 化学沉积 ; Co-P ; 预处理
地址	1. 合肥工业大学材料学院, 安徽, 合肥, 230009 2. 中国科学院固体物理研究所, 安徽, 合肥, 230031
语种	中文
文献类型	研究性论文
ISSN	1001-9731
学科	化学工业
基金	合肥工业大学科研发展基金
文献收藏号	CSCD:3459165