熔盐电解法制备CaB_6及其表征
PREPARATION AND CHARACTERIZATION OF CaB_6 BY MOLTEN SALT ELECTROLYSIS
查看参考文献16篇
|
文摘
|
研究了熔盐电解法制备CaB_6的合成工艺，确定了制备CaB_6粉末的合成温度、电解电压和电解时间．同时，对电解所生成的阴极产物的相组成、颗粒尺寸与形貌进行了表征。结果表明，CaCl_2熔盐体系制备CaB_6粉末的基本工艺条件是：Ar气环境保护，电解电压3．0V，900℃电解30h。所合成的CaB_6晶体粉末粒径范围为2—8μm，颗粒形态规整，为规则的长方体，对电解过程中阴极进行循环伏安扫描分析，确定硼酸盐向阴极的扩散速率为控制电解过程的重要环节。 |
|
其他语种文摘
|
CaB_6 powder was synthesized by molten salt electrolysis method, and the effects of synthesis temperature, electrolysis voltage and time on the phase composition, particle size and shape of cathode products were analyzed by XRD and SEM. The experimental results show that the best synthesis conditions of CaB_6 powder in CaCl_2 molten salt system are： environment of argon, voltage of 3.0 V, temperature of 900℃ for 30 h, under which the range of CaB_6 crystal size is 2--8 μm and the morphology of particles is cuboid massive shape. Using cyclic voltammetry in cathode process, it is Droved that the electrolysis Process is controlled by the diffusion rate of borate to the cathode. |
|
来源
|
金属学报
,2008,44(10):1243-1246 【核心库】
|
|
关键词
|
熔盐电解
;
熔盐体系
;
CaB_6
;
扩散速率
;
循环伏安法
|
|
地址
|
东北大学材料与冶金学院, 辽宁, 沈阳, 110004
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
化学工业 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:3420311
|
参考文献 共
16
共1页
|
|
1.
Alexander D T L.
Acta Mater,2006,54:2933
|
CSCD被引
18
次
|
|
|
|
|
2.
Bossuyt S.
Mater Sci Eng,2004,375:240
|
CSCD被引
1
次
|
|
|
|
|
3.
Chen Z.
Nature,2000,407:361
|
CSCD被引
249
次
|
|
|
|
|
4.
Li G M.
Electrochem Commun,2007,9:1951
|
CSCD被引
11
次
|
|
|
|
|
5.
Ma M.
J Alloys Compd,2006,420:37
|
CSCD被引
21
次
|
|
|
|
|
6.
Qiu G H.
Electrochim Acta,2006,51:5785
|
CSCD被引
28
次
|
|
|
|
|
7.
Schwandt C.
Electrochim Acta,2005,51:66
|
CSCD被引
38
次
|
|
|
|
|
8.
Shigek O.
J Cryst Growth,1998,192:346
|
CSCD被引
1
次
|
|
|
|
|
9.
Yu L P.
Electrochem Commun,2007,9:1374
|
CSCD被引
5
次
|
|
|
|
|
10.
Zhang M L.
J Alloys Compd,2007,440:362
|
CSCD被引
19
次
|
|
|
|
|
11.
Zheng S Q.
J Am Ceram Soc,2001,84:2725
|
CSCD被引
8
次
|
|
|
|
|
12.
胡小锋. CaCl2-NaCl熔盐电脱氧法制备金属Ta.
金属学报,2006,42:285
|
CSCD被引
16
次
|
|
|
|
|
13.
杨丽霞. CaB_6陶瓷研究的进展.
硅酸盐学报,2003,31:687
|
CSCD被引
5
次
|
|
|
|
|
14.
郑树起. 硼热还原法制备LaB_6粉末.
硅酸盐学报,2001,29:128
|
CSCD被引
12
次
|
|
|
|
|
15.
邵元华.
电化学方法原理和应用,2005:160
|
CSCD被引
1
次
|
|
|
|
|
16.
豆志河. 自蔓延高温合成CaB6的基础研究.
中国有色金属学报,2004,14:322
|
CSCD被引
13
次
|
|
|
|
|
了解气象卫星更多信息，请访问