苯乙烯/丙烯酸正丁酯/丙烯酸共聚微球的制备及其性能表征
Preparation and Characterization of Poly (styrene/n-butyl acrylate/acrylic acid) Microspheres
查看参考文献19篇
|
文摘
|
通过乳液聚合法和无皂乳液聚合法制备了苯乙烯/丙烯酸正丁酯/丙烯酸共聚微球.讨论了乳化剂用量、引发剂用量、功能单体、软硬单体用量比等对微球粒径和形态的影响.利用扫描电子显微镜(SEM)、傅立叶变换红外光谱仪(FTIR)对微球的粒径、形貌和表面基团进行分析.红外光谱表明,实验室所制备的苯乙烯/丙烯酸正丁酯/丙烯酸共聚微球表面存在丰富的羧基.利用竖片生长法得到自组装的多层胶体微球薄膜.通过对薄膜的反射光谱测量,发现随着湿度的增加,峰位会产生3nm左右的红移. |
|
其他语种文摘
|
In the paper,poly(styrene/n-butyl acrylate/acrylic acid) microspheres were prepared by the emulsion polymerization and the soap-free emulsion polymerization.The influence of emulsifier content、initiator content、functional monomer and the content ratio of soft and hard monomers on the microspheres radius and conformation were discussed.The radius、morphology and surface groups of the microspheres were analyzed by means of SEM and FTIR.The microspheres were assembled into compact colloidal crystal films by vertical growth method.The reflectance spectra of the film(280nm) under 30% and 90% humidity were measured respectively,and it was found that there were about 3nm red-shift of the wavelength of the peak with the increase of the humidity. |
|
来源
|
化学通报
,2008,71(5):368-372 【核心库】
|
|
关键词
|
高分子微球
;
乳液聚合
;
表面改性
;
红外光谱
|
|
地址
|
中国科学院力学研究所, 国家微重力实验室, 北京, 100080
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0441-3776 |
|
学科
|
化学 |
|
基金
|
中国科学院知识创新工程重要方向项目
|
|
文献收藏号
|
CSCD:3269150
|
参考文献 共
19
共1页
|
|
1.
A Reza.
Biomaterials,1993,14(1):5-15
|
CSCD被引
1
次
|
|
|
|
|
2.
K Han.
J. Controlled Release,2001,75(3):259-269
|
CSCD被引
5
次
|
|
|
|
|
3.
Y M Zhao.
Appl. Polym. Sci,2005,97(1):195-200
|
CSCD被引
32
次
|
|
|
|
|
4.
N H Park.
Colloid Polym. Sci,2001,279(11):1082-1089
|
CSCD被引
1
次
|
|
|
|
|
5.
马光辉.
高分子微球材料,2005
|
CSCD被引
31
次
|
|
|
|
|
6.
M Okubo.
Colloid Polym. Sci,1992,270(9):853-858
|
CSCD被引
10
次
|
|
|
|
|
7.
C F Lee.
Polym. Int,1993,30(4):475-481
|
CSCD被引
1
次
|
|
|
|
|
8.
M Tanka.
J. Mater. Sci,1990,25(1):987-991
|
CSCD被引
1
次
|
|
|
|
|
9.
K P Lok.
Can. J. Chem,1985,63:209-216
|
CSCD被引
13
次
|
|
|
|
|
10.
F L Yap.
Biomaterials,2007,28(14):2328-2338
|
CSCD被引
5
次
|
|
|
|
|
11.
H T Zhang.
J. Appl. Polym. Sci,2006,99(6):3586-3591
|
CSCD被引
2
次
|
|
|
|
|
12.
H T Zhang.
Chem. J. Chin. Univ. Chinese,2004,25(2):366-371
|
CSCD被引
1
次
|
|
|
|
|
13.
Q B Wang.
J. Chem. Eng. Jpn,2003,36(10):1227-1230
|
CSCD被引
3
次
|
|
|
|
|
14.
J X Huang.
Polym. Int,2003,52(5):819-826
|
CSCD被引
5
次
|
|
|
|
|
15.
S Slomkowski.
Polym. Adv. Tech,2002,13(10/12):906-918
|
CSCD被引
7
次
|
|
|
|
|
16.
S Omi.
J. Microencapsulation,2001,18(6):749-765
|
CSCD被引
8
次
|
|
|
|
|
17.
曹同玉.
聚合物乳液合成原理性能及应用,2002
|
CSCD被引
9
次
|
|
|
|
|
18.
L K Teh.
Appl. Phys. A,2004,81(7):1399-1404
|
CSCD被引
1
次
|
|
|
|
|
19.
G M Jia.
Acta Photonica Sinica,2005,34(10):1473-1475
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问