脉冲电流作用下40Cr钢淬火残余应力的消除
Residual stress release in quenched 40Cr steel under electropulsing
查看参考文献15篇
|
文摘
|
研究了脉冲电流作用下40Cr钢淬火残余应力的消除．结果表明，当脉冲电流密度达到一定数值后，材料中的残余应力开始部分弛豫；当电流密度达到6．3kA／mm ~2时，残余应力可在700μs的脉冲电流处理时间内完全消除，而试样的瞬时温升仅约为360℃．在脉冲电流作用下残余应力弛豫的主要原因，可能是电流的电致塑性效应降低了材料的屈服强度，试样在由快速加热产生的瞬时热压应力和残余应力的共同作用下发生了微量的塑性变形． |
|
其他语种文摘
|
High current density electropulsing was used to release quenched residual stress in 40Cr steel. It was found that residual stress began to release when the current density was higher than a certain value. And when the current density was up to 6.3 kA/mm~2, the residual stress could be completely released in 700 μs at a temperature rise of about 360 ℃. The main reason for the stress release was proposed to be that the yield stress of the material decreased due to the electroplastic effect of current, and at the same time, there was a thermal compressive stress induced by the high-rate heating process of electropulsing. The thermal compressive stress and the residual stress might caused plastic deformation of the sample and therefore realized residual stress release. |
|
来源
|
材料研究学报
,2007,21(1):41-44 【核心库】
|
|
关键词
|
金属材料
;
脉冲电流
;
淬火残余应力
;
40Cr钢
|
|
地址
|
中国科学院金属研究所, 沈阳材料科学国家（联合）实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-3093 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
辽宁省自然科学基金
|
|
文献收藏号
|
CSCD:2756593
|
参考文献 共
15
共1页
|
|
1.
K Heindlhofer.
Evaluation of Residual Stress,1948
|
CSCD被引
1
次
|
|
|
|
|
2.
张定铨.
材料中残余应力的X射线分析和作用,1999:167
|
CSCD被引
1
次
|
|
|
|
|
3.
F Tang. Research on residual stress reduction by a low frequency alternating magnetic field.
J Mater Process Technol,1998,74:255
|
CSCD被引
26
次
|
|
|
|
|
4.
A L Lu. Research on residual-stress reduction by strong pulsed magnetic treatment.
J Mater Process Technol,1998,74:259
|
CSCD被引
20
次
|
|
|
|
|
5.
Y I Ragozin. A new express-method of residual stresses relief in metals and ceramics in;Proc.
Proc.4# Int.Conf.on Residual Stresses,1994:926
|
CSCD被引
1
次
|
|
|
|
|
6.
Y I Ragozin.
Proc.6# Int.Conf.on Residual Stresses,2000:991
|
CSCD被引
1
次
|
|
|
|
|
7.
郭晓楠.
高强电脉冲对黄铜性能和碳纤维结构的影响[博士学位论文],1999
|
CSCD被引
1
次
|
|
|
|
|
8.
H Conrad.
Dislocations in Solids,1989:497
|
CSCD被引
6
次
|
|
|
|
|
9.
O.V(O)hringer.
Residual Stress,1986:47
|
CSCD被引
1
次
|
|
|
|
|
10.
H Conrad. Effect of electric current pulses on fatigue characteristics of polycrystalline copper.
Mater Sci and Eng A,1991,145:1
|
CSCD被引
15
次
|
|
|
|
|
11.
S D Antolovich. The effects of electric Currents and fields on deformation in metals ceramics and ionic materials:An interpretive survey.
Mater ＆Manuf Proc,2004,19(4):587
|
CSCD被引
12
次
|
|
|
|
|
12.
L B Zuev. Dislocation mobility in Zn single crystals under current pulses.
Dok Akad Nauk SSSR,1978,84:239
|
CSCD被引
1
次
|
|
|
|
|
13.
S H Xiao. Yao S.
Mater.Sci.Eng.A,2002,332:351
|
CSCD被引
7
次
|
|
|
|
|
14.
O A Troitskii. Anisotropy of the effect of electron-beam and-ir-radiation on the deformation process of zinc single crystals in the brittle state.
Dokl Akad Nauk SSSR,1963,148:332
|
CSCD被引
2
次
|
|
|
|
|
15.
D W Tang. Thermal stress relaxation behavior in thin films under transient laser-pulse heating.
J Appl Phys,1993,73(8):3749
|
CSCD被引
30
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问