稀土铈对热浸镀铝层组织和性能的影响
Effect of Rare Earth Element Cerium on Properties and Microstructure of Hot Dip Aluminum Coating on Q235 Steel
查看参考文献7篇
|
文摘
|
研究了稀土铈对热浸镀铝层组织结构、耐蚀和耐热性能的影响。结果表明：稀土铈质量分数低于0．3％时，热浸镀铝层的耐蚀性能和高温抗氧化性能都得到提高，超过此含量镀层的性能下降。稀土铈使得过渡层由锯齿形结构转变为平滑结构，使镀层中FeAl3析出相在表层中呈网状分布，随其含量增加过渡层厚度减小。稀土含量超过0．3％时，稀土化合物在表层中呈条块状第二相析出并偏聚，并且随著稀土铈含量增加，表面层中稀土化合物呈块状，且偏聚程度加大。 |
|
其他语种文摘
|
The effect of rare earth element Ce on the microstructure of hot dip aluminum（HDA） coating on Q235 steel have been studied by means of SEM and XRD. The anticorrosive property and oxidation resistance of the coating was also studied by immersion test in 3. 5% sodium chloride solution and at 900℃ for 300 h respectively. If the content of Ce in the hot dip aluminum bath was lowere than 0. 3%, with increasing the content of Ce in the bath, the anticorrosive property and oxidation resistance of HDA coating were improved obviously. If the content of Ce in the bath was higher than 0. 3%, the properties of the HDA coating became poor. By adding Ce into the HDA bath, the saw-toothed shape of transition layer of HAD coating became smooth, FeAl3 phase distributed in the surface layer in netted shape, but the thickness of the transition layer varied little with increasing the content of Ce in the bath. If the content of Ce was more than 0. 3% in the bath, the Ce compound separated out in strip-like shape in the surface layer and got together in the boundary of FeAl3 phase, and with increasing the Ce content in the bath, the shape of Ce compound became blocky and the degree of segregation was more serious. |
|
来源
|
机械工程材料
,2006,30(6):77-79 【核心库】
|
|
关键词
|
热浸镀铝
;
稀土
;
耐蚀性能
;
耐热性能
|
|
地址
|
1.
燕山大学, 亚稳材料制备技术与科学国家重点实验室, 河北, 秦皇岛, 066004
2.
中国科学院力学研究所, 北京, 100080
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1000-3738 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金资助项目
|
|
文献收藏号
|
CSCD:2477966
|
参考文献 共
7
共1页
|
|
1.
李华飞. 热浸镀铝钢的性能及用途.
材料保护,2001,34(5):21-23
|
CSCD被引
15
次
|
|
|
|
|
2.
顾文桂. 热浸镀铝钢带镀层与合金层的组织结构.
钢铁研究学报,1995,7(3):45-50
|
CSCD被引
1
次
|
|
|
|
|
3.
李国喜. 钢材热浸镀铝工艺的研究与应用.
材料保护,1993,25(9):13-16
|
CSCD被引
2
次
|
|
|
|
|
4.
陈军. 热浸镀铝件高温抗氧化性能的研究.
金属热处理,1999(2):16-19
|
CSCD被引
2
次
|
|
|
|
|
5.
孙成伟.
稀土在铝合金中的行为,1992
|
CSCD被引
2
次
|
|
|
|
|
6.
吴元康. 含稀土抗氧化剂的热浸镀铝工艺研究.
材料科学与工艺,1994,2(4):96-99
|
CSCD被引
1
次
|
|
|
|
|
7.
付瑞峰. 稀土元素对Al、Al合金线材电弧喷涂层的耐腐蚀性能试验.
表面工程,1997(4):36-40
|
CSCD被引
1
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问