文摘
|
研究了强磁场对Al-4％Cu合金时效析出的影响，采用显微硬度测试、X射线衍射以及电子探针等手段研究了材料的组织及性能。结果表明：在其他条件相同情况下，强磁场提高了材料的硬度，缩短了时效析出时间并且增加了晶界析出相的数量。强磁场作用于相变时引起的时效转变扩散系数的增加是以上变化的主要原因之一。同时，结果也表明在强磁场下时效析出时基体晶粒度、脱溶相形状及其排列方式无明显变化。 |
|
其他语种文摘
|
The effects of high magnetic field annealing on precipitate behavior of Al-4%Cu alloy were studied. Using microhardness test, X-Ray Diffraction （XRD） and Electron Probe Micro-analysis （EPMA） analyze the microstructures and mechanical properties of the material. The results show that the presence of high magnetic field increased the hardness of the alloy, and decreased its ageing time. The results also demonstrate that the high magnetic field makes the amount of precipitated phase increase. These changes result from that the coefficient of ageing diffusion increases in high magnetic field. However, the average grain size of matrix grains, the shape of precipitated phases and its arranging mode have not been changed apparently. |
|
来源
|
铸造
,2006,55(4):338-340 【核心库】
|
|
关键词
|
强磁场
;
Al-4％Cu合金
;
时效析出
;
硬度
;
扩散
|
|
地址
|
1.
大连理工大学材料科学与工程学院, 辽宁, 大连, 116024
2.
北京航空材料研究院, 北京, 100095
3.
中国科学院金属研究所, 辽宁, 沈阳, 110015
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4977 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:2359290
|
|
|
1.
王西宁. 磁场对材料固态相变影响的研究进展.
材料导报,2002,16(2):25-27
|
CSCD被引
8
次
|
|
|
|
|
2.
曹效文. 强磁场下的固体物理研究进展.
物理,2002,31(11):696-701
|
CSCD被引
2
次
|
|
|
|
|
3.
冯光宏. 磁场处理对微合金钢相变过程的影响.
北京科技大学学报,2001,23(3):262-264
|
CSCD被引
4
次
|
|
|
|
|
4.
冯光宏. 微合金钢磁场处理后的珠光体形貌.
钢铁研究学报,2003,15(5):28-31
|
CSCD被引
4
次
|
|
|
|
|
5.
胡心彬. 脉冲磁场对Co-25Ni合金马氏体相变温度的影响[J].
湖北工学院学报,2002,17(1):23-24,30
|
CSCD被引
1
次
|
|
|
|
|
6.
刘宗昌. 金属固态相变教程[M].
金属固态相变教程
|
CSCD被引
1
次
|
|
|
|
|
7.
李松瑞. 金属热处理[M].
金属热处理,2003
|
CSCD被引
43
次
|
|
|
了解气象卫星更多信息，请访问